Reason for Corrosion of Al-Mg-Cu Alloy Drainage Plate for Disconnector
摘 要
研究了腐蚀后Al-Mg-Cu合金引流板的显微组织、微区成分、电化学腐蚀性能以及腐蚀产物成分等,并与新引流板的进行了对比,分析了其腐蚀失效的原因。结果表明:Al-Mg-Cu合金引流板的腐蚀是由含硫的酸雨引起的,电流热效应导致引流板的组织老化,θ相的析出和粗化使引流板的耐腐蚀性能进一步降低。
Abstract
The microstructure, micro area composition, electrochemical corrosion property and corrosion product composition of the corroded Al-Mg-Cu alloy drainage plate were investigated and compared with those of the new drainage plate. The reason for corrosion failure was analyzed. The results show that the corrosion of the Al-Mg-Cu alloy drainage plate was caused by acid rain containing sulphur element; the thermal effect of electric current led to the aged structure of the drainage plate, and the precipitation and coarsening of θ phase decreased the corrosion resistance of the drainage plate further.
中图分类号 TG172.3 DOI 10.11973/jxgccl201805016
所属栏目 失效分析
基金项目
收稿日期 2017/2/15
修改稿日期 2018/1/3
网络出版日期
作者单位点击查看
备注缪春辉(1986-),男,安徽合肥人,高级工程师,博士
引用该论文: MIAO Chunhui,ZHANG Tao,CHEN Guohong,WANG Ruomin,LI Jianlin,TANG Quan. Reason for Corrosion of Al-Mg-Cu Alloy Drainage Plate for Disconnector[J]. Materials for mechancial engineering, 2018, 42(5): 78~81
缪春辉,张涛,陈国宏,王若民,李坚林,汤泉. 隔离开关用Al-Mg-Cu合金引流板的腐蚀原因[J]. 机械工程材料, 2018, 42(5): 78~81
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】丁俭,杜喜望,靳子惠,等. 加入Al-5Ti-B细化剂和Al-2Zr-Sc中间合金后铝锌镁合金的组织和拉伸性能[J]. 机械工程材料, 2017, 41(1):38-42.
【2】王少华,马志锋, 刘惠, 等. 铝锌镁铜锆钪合金型材的组织和性能[J]. 机械工程材料, 2014, 38(6):60-65.
【3】DESCHAMPS A, TEXIERB G, RINGEVAL S,et al. Influence of cooling rate on the precipitation microstructure in a medium strength Al-Zn-Mg alloy[J]. Materials Science and Engineering A, 2009, 501(1/2):133-139.
【4】刘春燕,邱义伦,王斌. 2A12铝合金热处理工艺研究[J]. 热处理, 2008, 23(5):59-61.
【5】王芝秀,李海,顾建华,等. Cu含量对Al-Mg-Si-Cu合金微观组织和性能的影响[J]. 中国有色金属学报, 2012, 22(12):3348-3355.
【6】雷阿利,冯拉俊, 马小菊. 几种不同材料在含硫介质中的腐蚀性[J]. 中国腐蚀与防护学报, 2007, 27(2):65-69.
【7】李旭东,刘元海,刘治国,等. 预腐蚀7A09铝合金腐蚀坑处萌生疲劳裂纹扩展深度的估算[J]. 机械工程材料, 2017, 41(1):25-29.
【8】聂辉文,曾小玲,聂俊红,等. 不同时效状态下Al-Zn-Mg-Zr-Sc合金的应力腐蚀行为[J]. 机械工程材料, 2016, 40(11):98-102.
【9】KIMBERLI J A, SACHIN R S, PAUL N C, et al. Effect of prior corrosion on short crack behavior in 2024-T3 aluminum alloy[J]. Corrosion Science, 2008, 50(9):2588-2595.
【2】王少华,马志锋, 刘惠, 等. 铝锌镁铜锆钪合金型材的组织和性能[J]. 机械工程材料, 2014, 38(6):60-65.
【3】DESCHAMPS A, TEXIERB G, RINGEVAL S,et al. Influence of cooling rate on the precipitation microstructure in a medium strength Al-Zn-Mg alloy[J]. Materials Science and Engineering A, 2009, 501(1/2):133-139.
【4】刘春燕,邱义伦,王斌. 2A12铝合金热处理工艺研究[J]. 热处理, 2008, 23(5):59-61.
【5】王芝秀,李海,顾建华,等. Cu含量对Al-Mg-Si-Cu合金微观组织和性能的影响[J]. 中国有色金属学报, 2012, 22(12):3348-3355.
【6】雷阿利,冯拉俊, 马小菊. 几种不同材料在含硫介质中的腐蚀性[J]. 中国腐蚀与防护学报, 2007, 27(2):65-69.
【7】李旭东,刘元海,刘治国,等. 预腐蚀7A09铝合金腐蚀坑处萌生疲劳裂纹扩展深度的估算[J]. 机械工程材料, 2017, 41(1):25-29.
【8】聂辉文,曾小玲,聂俊红,等. 不同时效状态下Al-Zn-Mg-Zr-Sc合金的应力腐蚀行为[J]. 机械工程材料, 2016, 40(11):98-102.
【9】KIMBERLI J A, SACHIN R S, PAUL N C, et al. Effect of prior corrosion on short crack behavior in 2024-T3 aluminum alloy[J]. Corrosion Science, 2008, 50(9):2588-2595.
相关信息