铝合金板材的超声C扫描检测
Ultrasonic C-scan Testing of Aluminum Alloy Plate
摘 要
针对8 mm厚的铝合金板材开展了8通道超声C扫描检测技术研究，参照GJB 1580A-2004 标准中的AAA级质量验收要求设计并制作了对比试块，结合对比试块对影响检测结果的关键工艺参数进行了分析和试验验证。结果表明，所确定的检测工艺能够满足0.4 mm平底孔的检测灵敏度要求，可以应用于类似金属板材的高效、自动化超声检测。
超声C扫描
检测参数
aluminum alloy plate
ultrasonic C-scan
testing parameter
Abstract
Eight-channel ultrasonic C-scan testing was carried out on 8mm aluminum alloy sheets. The key testing parameters affecting the test results were analyzed and validated by the comparative test block which was designed and manufactured according to GJB1580A-2004 AAA grade acceptance requirements. The results show that the detection process identified in this paper can achieve the detection sensitivity of φ0.4 mm, which can be applied to the highly efficient and automated ultrasonic testing of similar sheet metal.
中图分类号 TG115.28 DOI 10.11973/wsjc201806005
所属栏目 试验研究
基金项目
收稿日期 2018/1/22
修改稿日期
网络出版日期
作者单位点击查看
联系人作者王飞(wf0420@163.com)
备注王飞(1986-),男,高级工程师,主要从事无损检测技术研究与应用工作
引用该论文: WANG Fei,TU Jun,CHEN Jie,WU Zhencheng. Ultrasonic C-scan Testing of Aluminum Alloy Plate[J]. Nondestructive Testing, 2018, 40(6): 18～20
王飞,涂俊,陈杰,吴振成. 铝合金板材的超声C扫描检测[J]. 无损检测, 2018, 40(6): 18～20
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】冯苏乐,赵毕艳,罗益民,等.液力成形在运载火箭增压输送系统中的应用[J].航天制造技术,2014(5):38-42.
【2】彭赫力,冯苏乐,李中权,等.大深宽比整流罩拉深成形数值模拟[J]. 航天制造技术,2014(4):19-22.
【3】吴时红,何双起,陈颖,等.金属薄板超声无损检测[J].宇航材料工艺,2007(6):124-126.
【4】周正干,冯占英, 高翌飞,等.超声导波在大型薄铝板缺陷检测中的应用[J].航空学报,2007,29(4):1044-1048.
【2】彭赫力,冯苏乐,李中权,等.大深宽比整流罩拉深成形数值模拟[J]. 航天制造技术,2014(4):19-22.
【3】吴时红,何双起,陈颖,等.金属薄板超声无损检测[J].宇航材料工艺,2007(6):124-126.
【4】周正干,冯占英, 高翌飞,等.超声导波在大型薄铝板缺陷检测中的应用[J].航空学报,2007,29(4):1044-1048.
相关信息