Metallographic Preparation Technology of Porous Nickel-Graphite Thermal Spraying Coating
摘 要
由于镍-石墨热喷涂涂层中金属骨架、润滑相及孔隙各相的硬度和韧性差异较大,使得金相试样表面容易出现孔隙扩大、拔出、划痕、水污等制样缺陷,导致无法反映涂层的真实微观形貌。通过改进和优化切割取样、镶嵌、试样磨抛等金相制备参数,制备了镍-石墨热喷涂涂层金相试样。结果表明:试样切割取样过程中在夹具与试样之间加装塑料薄片,切割后试样浸没于无水酒精溶液清洗,特殊的3次真空浸渗方式镶嵌试样,选择最佳抛光时间和低回复性抛光布,能真实呈现镍-石墨热喷涂涂层各相的形貌、数量和分布。
Abstract
Because the hardness and toughness of metal skeleton, lubricating phase and pore in the nickel-graphite thermal spraying coating differ greatly, the surface defects of the metallographic sample such as pore enlargement, pulling out, scratch and water pollution were easy to appear, which led to the true micromorphology of the coating could not be reflect eventually. By means of improving and optimizing metallographic preparation parameters such as cutting sampling, inlaying and sample grinding, metallographic specimens of nickel-graphite thermal spraying coating were prepared. The results show that during the process of sample cutting added plastic sheet between the clamp and the sample, the sample were soaked in the anhydrous alcohol solution after cutting, special three times vacuum infiltration method inlaid sample, selecting the best polishing time and low recovery polishing cloth could truly show the pore morphology, quantity and distribution of each phase of the nickel-graphite thermal spraying coating.
中图分类号 TG115.21+1 DOI 10.11973/lhjy-wl201807008
所属栏目 试验技术与方法
基金项目
收稿日期 2017/11/16
修改稿日期
网络出版日期
作者单位点击查看
备注谢善(1979-),男,工程师,主要从事热喷涂涂层的理化检验和失效分析工作,huitzhe@163.com
引用该论文: XIE Shan,QUAN Qiongrui,LI Xin. Metallographic Preparation Technology of Porous Nickel-Graphite Thermal Spraying Coating[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(7): 499~503
谢善,全琼蕊,李欣. 多孔镍-石墨热喷涂涂层的金相制备技术[J]. 理化检验-物理分册, 2018, 54(7): 499~503
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】CHUPP R E, GHASRIPOOR F,TURNQUIST N A,et al. Advanced seals for industrial turbine applications:dynamic seal development[J]. Journal of Propulsion and Power,2002,18(6):1260-1266.
【2】张俊红,鲁鑫,何振鹏,等. 航空发动机可磨耗封严涂层技术研究及性能评价[J]. 材料工程,2016,44(4):94-109.
【3】尹春雷,陈美英,占佳,等. 可磨耗封严涂层研究进展[J]. 航空制造技术,2008(20):92-94.
【4】田晔,张淑婷,马江虹,等. 可磨耗封严涂层发展及应用[J]. 有色金属(冶炼部分),2006(z1):96-99.
【5】FARAOUN H I,GROSDIDIER T,SEICHEPINE J L,et al. Improvement of thermally sprayed abradable coating by microstructure control[J]. Surface and Coatings Technology,2006,201(6):2303-2312.
【6】王荣. 机械装备的失效分析(续前)第4讲:金相分析技术(下)[J]. 理化检验(物理分册),2017,53(4):225-234.
【7】刘昌奎. 物理冶金检测技术[M]. 北京:化学工业出版社,2015.
【8】黄志锋,褚胜林,张灵芝,等. 真空浸渍树脂法制备烧结金属材料金相样品[J]. 理化检验(物理分册),2007,43(10):509-511.
【2】张俊红,鲁鑫,何振鹏,等. 航空发动机可磨耗封严涂层技术研究及性能评价[J]. 材料工程,2016,44(4):94-109.
【3】尹春雷,陈美英,占佳,等. 可磨耗封严涂层研究进展[J]. 航空制造技术,2008(20):92-94.
【4】田晔,张淑婷,马江虹,等. 可磨耗封严涂层发展及应用[J]. 有色金属(冶炼部分),2006(z1):96-99.
【5】FARAOUN H I,GROSDIDIER T,SEICHEPINE J L,et al. Improvement of thermally sprayed abradable coating by microstructure control[J]. Surface and Coatings Technology,2006,201(6):2303-2312.
【6】王荣. 机械装备的失效分析(续前)第4讲:金相分析技术(下)[J]. 理化检验(物理分册),2017,53(4):225-234.
【7】刘昌奎. 物理冶金检测技术[M]. 北京:化学工业出版社,2015.
【8】黄志锋,褚胜林,张灵芝,等. 真空浸渍树脂法制备烧结金属材料金相样品[J]. 理化检验(物理分册),2007,43(10):509-511.
相关信息