某钢结构螺栓断裂失效分析
Failure Analysis on Frature of a Bolt for Steel Construction
摘 要
某公司一户外钢结构楼梯螺栓发生断裂失效，采用宏观分析、化学成分分析、金相分析、硬度测试、断口分析等方法对螺栓断裂原因进行了分析。结果表明：螺栓断裂主要是因为螺栓部分新鲜表面暴露在空气中，在腐蚀性环境和应力的共同作用下，应力集中的螺栓根部开始萌生裂纹，裂纹由外向内扩展，最终造成一次性断裂。
螺栓
断裂
腐蚀
应力集中
steel construction
bolt
fracture
corrosion
stress concentration
Abstract
The bolt used in a company's outdoor steel construction stair fractured, and means such as macro analysis, chemical composition analysis, metallographic analysis, hardness test and fracture analysis were used to analyze the fracture causes of the bolt. The results show that the fracture of the bolt was mainly due to the fresh surface of the bolt being exposed to the air. Under the combined action of the corrosive environment and stress, cracks initiated at the root of the bolt where the stress was concentrated. The cracks propagated from the outside to the inside and eventually caused a one-time fracture.
中图分类号 TG115 TU391 DOI 10.11973/lhjy-wl201810012
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/6/5
修改稿日期
网络出版日期
作者单位点击查看
备注邱康勇(1987-),男,工程师,学士,主要从事金属材料的理化检验及机械零部件失效分析工作,295717869@qq.com
引用该论文: QIU Kangyong,ZHANG Jie,WU Jiquan. Failure Analysis on Frature of a Bolt for Steel Construction[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(10): 765～768
邱康勇,张杰,吴继权. 某钢结构螺栓断裂失效分析[J]. 理化检验－物理分册, 2018, 54(10): 765～768
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张奎志, 刘刚,曲政. 电厂钢结构腐蚀防护应用[J]. 全面腐蚀控制,2004,18(5):42-44.
【2】张栋. 失效分析[M]. 北京:国防工业出版社,2004.
【3】张建国. 20MnTiB高强螺栓断裂原因分析[J]. 热处理技术与装备,2011,32(5):44-46.
【4】张彦文,吴立新,王志奋,等. 储气球罐连接阀螺栓断裂分析[J]. 理化检验(物理分册),2013,49(9):628-631.
【2】张栋. 失效分析[M]. 北京:国防工业出版社,2004.
【3】张建国. 20MnTiB高强螺栓断裂原因分析[J]. 热处理技术与装备,2011,32(5):44-46.
【4】张彦文,吴立新,王志奋,等. 储气球罐连接阀螺栓断裂分析[J]. 理化检验(物理分册),2013,49(9):628-631.
相关信息