夹片螺母装配失效分析
Failure Analysis of Speed Nuts during Assembly
摘 要
对汽车总装线上装配螺栓的过程中被撕裂的夹片螺母进行了理化检验和失效原因分析。结果表明：夹片螺母是由于受到了较大的外力而发生一次性过载撕裂；还原并分析装配现场发现，夹片螺母及与其相连的两个钣金件之间的相对位置出现了错配，从而导致装配时因未对正而发生夹片螺母过载撕裂失效。
现场装配
过载撕裂
位置匹配
speed nut
site assembly
overload tearing
relative position matching
Abstract
The physical and chemical inspection and failure cause analysis of the torn speed nuts during the assembly of the bolts on the automobile assembly line were carried out. The results show that the failure of the speed nut was a one-time overload tearing due to the large external force. Recovering and analyzing of the assembly site, it was found that the relative position between the speed nut and the two sheet metal parts connected thereto was mismatched. As a result, the speed nut overload tearing failure occured due to misalignment during assembly.
中图分类号 TH131.3 U463.334 DOI 10.11973/lhjy-wl201810014
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/8/10
修改稿日期
网络出版日期
作者单位点击查看
备注董玉军(1987-),男,硕士,主要从事汽车金属材料的检测和研究工作,dongyujun@csvw.com
引用该论文: DONG Yujun,LI Dan,LONG Teng,XIAO Jiong,CAO Pengfei. Failure Analysis of Speed Nuts during Assembly[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(10): 772～774
董玉军,李丹,龙腾,肖炯,曹鹏飞. 夹片螺母装配失效分析[J]. 理化检验－物理分册, 2018, 54(10): 772～774
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李文丽. 基于CATIA的汽车内外饰典型紧固件库开发及应用[J]. 汽车工程师,2010(11):47-50.
【2】丁惠麟,金荣芳. 机械零件缺陷、失效分析与实例[M]. 北京:化学工业出版社,2013.
【3】张先鸣. 汽车高强紧固件热处理工艺[J]. 现代零部件,2012(8):42-44.
【4】鲁修宇,夏艳花,周勇,等. 我国汽车紧固件的现状及发展[J]. 热处理技术与装备,2015,36(6):76-80.
【5】孟文华,曾伟传,顾静青,等. 10.9级螺栓早期疲劳断裂失效分析[J]. 理化检验(物理分册),2017,53(5):365-367.
【6】吴佳峻. 18CrNiMo7-6钢齿轮轴开裂失效分析[J]. 理化检验(物理分册),2017,53(9):671-674.
【2】丁惠麟,金荣芳. 机械零件缺陷、失效分析与实例[M]. 北京:化学工业出版社,2013.
【3】张先鸣. 汽车高强紧固件热处理工艺[J]. 现代零部件,2012(8):42-44.
【4】鲁修宇,夏艳花,周勇,等. 我国汽车紧固件的现状及发展[J]. 热处理技术与装备,2015,36(6):76-80.
【5】孟文华,曾伟传,顾静青,等. 10.9级螺栓早期疲劳断裂失效分析[J]. 理化检验(物理分册),2017,53(5):365-367.
【6】吴佳峻. 18CrNiMo7-6钢齿轮轴开裂失效分析[J]. 理化检验(物理分册),2017,53(9):671-674.
相关信息