Reason Analysis on Fracture of Cr12 Steel Water Swelling Mold Bases
摘 要
Cr12钢水胀型模具底座在使用过程中发生批量断裂,采用宏观检验、化学成分分析、金相检验、断口分析、硬度测试等方法对该批模具底座断裂的原因进行了分析。结果表明:该批模具底座断裂为沿晶脆性断裂;断裂的主要原因为模具材料碳含量超标,且锻造不充分导致共晶碳化物粗大且呈严重网状聚集分布,造成应力集中,在内应力和外力的共同作用下模具底座产生裂纹并迅速扩展而断裂。
Abstract
The Cr12 steel water swelling mold bases fractured in bulk during use, and the fracture reasons of the mold bases were analyzed by macroscopic inspection, chemical composition analysis, metallographic examination, fracture analysis and hardness test. The results show that the fracture of the mold bases was brittle fracture. The main reasons for the fracture were that the carbon content of the mold material was excessive and the forging was not enough, which resulted in coarse eutectic carbides and serious reticular aggregation distribution, and eventually led to stress concentration of the material. Under the co-action of internal stress and external force, cracks generated in the mold bases, and then spread rapidly and led to fracture.
中图分类号 TG172 DOI 10.11973/lhjy-wl201810015
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/8/29
修改稿日期
网络出版日期
作者单位点击查看
备注魏亮新(1984-),男,工程师,主要从事金属材料及制品质量检验及失效分析工作,weilx-ike@163.com
引用该论文: WEI Liangxin,HUANG Zidong,HONG Zehao,CHEN Liling. Reason Analysis on Fracture of Cr12 Steel Water Swelling Mold Bases[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(10): 775~777
魏亮新,黄子东,洪泽浩,陈丽玲. Cr12钢水胀模具底座断裂原因分析[J]. 理化检验-物理分册, 2018, 54(10): 775~777
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】林慧国. 袖珍世界钢号手册[M]. 北京:机械工业出版社,2003.
【2】任颂赞. 钢铁金相图谱[M]. 上海:上海科学技术文献出版社,2003.
【3】胡世炎. 机械失效分析手册[M]. 成都:四川科学技术出版社,1999.
【4】杨晓,陈政龙,潘恒沛,等. 40Cr钢紧固螺栓断裂原因分析[J]. 理化检验(物理分册),2016,52(12):903-905.
【5】金静静,李玲. 某油田钻杆旋塞阀断裂原因分析[J]. 理化检验(物理分册),2016,52(5):355-359.
【2】任颂赞. 钢铁金相图谱[M]. 上海:上海科学技术文献出版社,2003.
【3】胡世炎. 机械失效分析手册[M]. 成都:四川科学技术出版社,1999.
【4】杨晓,陈政龙,潘恒沛,等. 40Cr钢紧固螺栓断裂原因分析[J]. 理化检验(物理分册),2016,52(12):903-905.
【5】金静静,李玲. 某油田钻杆旋塞阀断裂原因分析[J]. 理化检验(物理分册),2016,52(5):355-359.
相关信息