镍钛丝断裂原因分析
Cause Analysis on Fracture of Nickel Titanium Wires
摘 要
某镍钛合金植入类医疗器械产品里的镍钛丝在生产过程中发生断裂，采用化学成分分析、力学性能试验、洁净度测试、断口宏微观分析以及能谱分析等方法对其断裂原因进行了分析。结果表明：镍钛丝的加工应力未得到很好的消除，加之编织模棒和热缩管引入了腐蚀介质，二者共同作用导致该镍钛丝发生了应力腐蚀断裂。
镍钛丝
断裂
应力腐蚀
implantable medical device
nickel titanium wire
fracture
stress corrosion
Abstract
The nickel titanium wires in a nickel titanium alloy implantable medical device product fractured during production. The fracture reasons were analyzed by chemical composition analysis, mechanical property test, cleanliness test, macro and micro fracture analysis, energy spectrum analysis and so on. The results show that the machining stress of the nickel titanium wires had not been eliminated well, and the corrosive medium introduced by the braiding rod and the heat shrinkable tube. These two factors together caused the stress corrosion fracture of the nickel titanium wires.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201811011
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/12/13
修改稿日期
网络出版日期
作者单位点击查看
备注施小立(1985-),女,高级工程师,博士,主要从事医疗器械产品材料研究、注册与检测工作,lxl863@126.com
引用该论文: SHI Xiaoli,QI Fengjun,MU Ying,LIAO Jingyou,LIU Yanwen,LI Xiaoling. Cause Analysis on Fracture of Nickel Titanium Wires[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(11): 829～832
施小立,祁凤君,穆盈,廖经友,刘艳文,李晓玲. 镍钛丝断裂原因分析[J]. 理化检验－物理分册, 2018, 54(11): 829～832
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】廖景娱. 金属构件失效分析[M]. 北京:化学工业出版社,2003.
【2】费勤勇,李晓玲,江俊灵,等. 注水阀弹簧断裂原因分析[J]. 理化检验(物理分册),2007,43(12):48-50.
【3】李晓玲,董毅,董霞,等. 高压釜密封环断裂分析[J]. 理化检验(物理分册),1994,30(5):50-52.
【4】钟群鹏,赵子华. 断口学[M]. 北京:高等教育出版社,2006.
【2】费勤勇,李晓玲,江俊灵,等. 注水阀弹簧断裂原因分析[J]. 理化检验(物理分册),2007,43(12):48-50.
【3】李晓玲,董毅,董霞,等. 高压釜密封环断裂分析[J]. 理化检验(物理分册),1994,30(5):50-52.
【4】钟群鹏,赵子华. 断口学[M]. 北京:高等教育出版社,2006.
相关信息