X光管用联轴轴承滚道处麻点成因分析
Cause Analysis on Pockmarks in Raceway of Coupling Bearing for X-Ray Tube
摘 要
某X光管用联轴轴承在装配检验过程中发现滚道处存在麻点，采用宏观分析、化学成分分析、硬度测试、金相检验等方法对麻点产生的原因进行了分析。结果表明：该轴承的原材料在铸造过程中冷却速度较慢产生了尺寸过大的大块角状碳化物，在滚道磨削和超精研磨过程中大块角状碳化物剥落，从而在轴承滚道处产生麻点。
麻点
原材料
碳化物
coupling bearing
pockmark
raw material
carbide
Abstract
The pockmarks in the raceway of coupling bearing for X-Ray tube were found during the process of assembly inspection, the formation causes of pockmarks were analyzed by means of macro analysis, chemical composition analysis, hardness test, metallographic examination and so on. The results show that the cooling rate of the raw material was slower in casting process, and large bulk angular carbides were produced. In the process of raceway grinding and ultra fine grinding, large bulk angular carbides were peeled off, which resulted in pockmarks on the bearing raceway.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201811016
所属栏目 质量控制与失效分析
基金项目
收稿日期 2017/12/1
修改稿日期
网络出版日期
作者单位点击查看
备注陈鹏飞(1989-),男,助理工程师,主要从事金属材料热处理及金属构件的失效分析工作,xcswcpf@163.com
引用该论文: CHEN Pengfei. Cause Analysis on Pockmarks in Raceway of Coupling Bearing for X-Ray Tube[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2018, 54(11): 850～852
陈鹏飞. X光管用联轴轴承滚道处麻点成因分析[J]. 理化检验－物理分册, 2018, 54(11): 850～852
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】石功奇,丁培道,周守则. 合金元素对高速钢共晶碳化物的影响[J]. 理化检验(物理分册),1990(4):28-30.
【2】俞峰,许达,罗迪. 高速钢中的碳化物缺陷[J]. 钢铁研究学报,2008,20(6):1-6.
【3】杨伟旗. 高速钢原材料检验方法探讨[J]. 理化检验(物理分册),2002,38(7):300-302.
【4】罗迪,邢国华,刘宇,等. M42高速钢中的碳化物[J]. 钢铁,1991(10):35-38.
【5】FISCHER A,KOHLHAAS E,唐元祈. 对高速钢显微组织的观察[J]. 理化检验(物理分册),1980(3):47-50.
【2】俞峰,许达,罗迪. 高速钢中的碳化物缺陷[J]. 钢铁研究学报,2008,20(6):1-6.
【3】杨伟旗. 高速钢原材料检验方法探讨[J]. 理化检验(物理分册),2002,38(7):300-302.
【4】罗迪,邢国华,刘宇,等. M42高速钢中的碳化物[J]. 钢铁,1991(10):35-38.
【5】FISCHER A,KOHLHAAS E,唐元祈. 对高速钢显微组织的观察[J]. 理化检验(物理分册),1980(3):47-50.
相关信息