CT80钢级连续油管焊接接头在不同质量分数NaCl溶液中的电化学腐蚀行为
Electrochemical Corrosion Behavior of Welded Joint of CT80 Grade Coiled Tubing in NaCl Solutions with Different Mass Fractions
摘 要
采用动电位极化技术和电化学阻抗谱测试方法研究了CT80钢级连续油管焊接接头的母材和焊缝在不同质量分数（3.5%，5.0%，7.0%）NaCl溶液中的电化学腐蚀行为。结果表明：在不同质量分数NaCl溶液中，母材和焊缝的极化曲线均呈典型的阳极溶解特征，没有钝化现象；随着NaCl质量分数（即Cl-1浓度）的增加，母材和焊缝的开路电位和自腐蚀电位负移，极化电阻减小，自腐蚀电流密度增大，耐腐蚀性能减小；母材的热力学稳定性和耐腐蚀性能优于焊缝的。
连续油管
焊接接头
电化学阻抗谱
NaCl溶液
耐腐蚀性能
CT80 tubing steel
coiled tubing
welded joint
electrochemical impendence spectroscopy
NaCl solution
corrosion resistance
Abstract
Electrochemical corrosion behavior of base metal and weld from welded joint of CT80 grade coiled tubing in NaCl solutions with different mass fractions (3.5%, 5.0%, 7.0%) was investigated by potentiodynamic polarization technique and electrochemical impendence spectroscopy testing method. The results show that the polarization curves of the base metal and weld presented a typical anodic dissolution characteristic in NaCl solutions with different mass fractions. No passivation phenomenon was observed. With the increase of NaCl mass fraction (i.e., Cl-1 concentration), the open circuit potential and the free corrosion potential of the base metal and weld showed negative shifts, the polarization resistance decreased and the free corrosion current density increased; the corrosion resistance decreased. The thermodynamic stability and corrosion resistance of the base metal were better than those of the weld.
中图分类号 TG174 DOI 10.11973/jxgccl201812014
所属栏目 材料性能及应用
基金项目 国家质检公益性行业科研专项经费资助项目（201510205-03）；西安石油大学青年科技创新基金资助项目（2015QN014）；西安石油大学材料科学与工程省级优势学科资助项目
收稿日期 2017/11/3
修改稿日期 2018/11/11
网络出版日期
作者单位点击查看
备注雒设计(1979-),男,陕西礼泉人,副教授,博士
引用该论文: LUO Sheji,ZHANG Hui,HAN Lihong. Electrochemical Corrosion Behavior of Welded Joint of CT80 Grade Coiled Tubing in NaCl Solutions with Different Mass Fractions[J]. Materials for mechancial engineering, 2018, 42(12): 68～72
雒设计,张辉,韩礼红. CT80钢级连续油管焊接接头在不同质量分数NaCl溶液中的电化学腐蚀行为[J]. 机械工程材料, 2018, 42(12): 68～72
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】LUO S J, WANG R. Identification of the selective corrosion existing at the seam weld of electric resistance-welded pipes[J]. Corrosion Science, 2014, 87:517-520.
【2】CRABTREE A R, GAVIN W. Coiled tubing in sour environment:Theory and practice[J]. SPE Drilling & Completion, 2005, 20(1):71-80.
【3】苏新亮, 李根生, 沈忠厚,等. 连续油管钻井技术研究与应用进展[J]. 天然气工业, 2008, 28(8):55-57.
【4】鲜宁, 姜放, 荣明, 等. 连续油管在酸性环境下的腐蚀与防护及其研究进展[J]. 天然气工业, 2011, 31(4):113-116.
【5】董晓强, 李钊. 304连续油管在油井条件下的失效分析[J]. 热加工工艺, 2015(10):239-240.
【6】STANLEY R K. An analysis of failure in coiled tubing[C]//IADC/SPE Drilling Conference. Dallas, Texas:Texas Society of Petroleum Engineers, 1998.
【7】毕宗岳,张鹏,井晓天,等.连续油管在川东气田的腐蚀行为研究[J].焊管,2011,34(4):26-40.
【8】李洪斌,毕宗岳,鲜林云,等.φ38.1 mm连续油管穿孔失效分析[J].焊管,2017,40(7):55-59.
【9】舒勇华,王福会,周龙江,等.NaCl膜和水蒸气对纯Cr腐蚀行为的影响[J].中国腐蚀与防护学报,2000,20(1):88-95.
【10】GRIGORIS E K, STEFANO M S. Pitting corrosion of artificially aged T6AA2024/SiCp composites in 3.5wt.% NaCl aqueous solution[J]. Corrosion Science,2007,49(6):2711-2720.
【11】AZZERRI N, MANCIA F, TAMBA A. Electrochemical prediction of corrosion behaviour of stainless steels in chloride-containing water[J]. Corrosion Science, 1982, 22(7):675-687.
【12】李继红,赵鹏康,余晗,等.连续油管电阻焊热影响区不完全正火区的组织与性能[J]. 金属热处理,2012,34(7):33-37.
【13】许庆,张英,许蓉娜. 冷却速度对连续油管焊接接头热影响区组织及性能的影响[J].热处理技术及装备,2016,37(1):65-66.
【14】张敏,赵鹏康,王文武,等. 高频电阻焊连续油管焊接HAZ组织性能热模拟分析[J]. 焊接技术, 2011, 40(2):12-15.
【15】BI Z Y, WANG R, JING X T. Grooving corrosion of oil coiled tubes manufactured by electrical resistance welding[J]. Corrosion Science, 2012, 57(2):67-73.
【16】毕宗岳,井晓天,鲜林云,等.热处理对连续油管焊缝沟槽腐蚀行为的影响[J].材料热处理技术,2011,40(8):150-153.
【17】祝成龙,赵国仙,薛艳,等.温度对连续油管QT-900在CO2环境中腐蚀行为的影响[J].腐蚀与防护,2013,34(3):232-235.
【18】薛玉娜,雒设计,刘明,等.CT80连续油管钢的电化学腐蚀行为[J].腐蚀科学与防护技术,2013,25(1):23-29.
【19】宋诗哲.腐蚀电化学研究方法[M].北京:化学工业出版社,1988:120.
【20】张文钺.焊接冶金学基本原理[M].北京:机械工业出版社,1996.
【2】CRABTREE A R, GAVIN W. Coiled tubing in sour environment:Theory and practice[J]. SPE Drilling & Completion, 2005, 20(1):71-80.
【3】苏新亮, 李根生, 沈忠厚,等. 连续油管钻井技术研究与应用进展[J]. 天然气工业, 2008, 28(8):55-57.
【4】鲜宁, 姜放, 荣明, 等. 连续油管在酸性环境下的腐蚀与防护及其研究进展[J]. 天然气工业, 2011, 31(4):113-116.
【5】董晓强, 李钊. 304连续油管在油井条件下的失效分析[J]. 热加工工艺, 2015(10):239-240.
【6】STANLEY R K. An analysis of failure in coiled tubing[C]//IADC/SPE Drilling Conference. Dallas, Texas:Texas Society of Petroleum Engineers, 1998.
【7】毕宗岳,张鹏,井晓天,等.连续油管在川东气田的腐蚀行为研究[J].焊管,2011,34(4):26-40.
【8】李洪斌,毕宗岳,鲜林云,等.φ38.1 mm连续油管穿孔失效分析[J].焊管,2017,40(7):55-59.
【9】舒勇华,王福会,周龙江,等.NaCl膜和水蒸气对纯Cr腐蚀行为的影响[J].中国腐蚀与防护学报,2000,20(1):88-95.
【10】GRIGORIS E K, STEFANO M S. Pitting corrosion of artificially aged T6AA2024/SiCp composites in 3.5wt.% NaCl aqueous solution[J]. Corrosion Science,2007,49(6):2711-2720.
【11】AZZERRI N, MANCIA F, TAMBA A. Electrochemical prediction of corrosion behaviour of stainless steels in chloride-containing water[J]. Corrosion Science, 1982, 22(7):675-687.
【12】李继红,赵鹏康,余晗,等.连续油管电阻焊热影响区不完全正火区的组织与性能[J]. 金属热处理,2012,34(7):33-37.
【13】许庆,张英,许蓉娜. 冷却速度对连续油管焊接接头热影响区组织及性能的影响[J].热处理技术及装备,2016,37(1):65-66.
【14】张敏,赵鹏康,王文武,等. 高频电阻焊连续油管焊接HAZ组织性能热模拟分析[J]. 焊接技术, 2011, 40(2):12-15.
【15】BI Z Y, WANG R, JING X T. Grooving corrosion of oil coiled tubes manufactured by electrical resistance welding[J]. Corrosion Science, 2012, 57(2):67-73.
【16】毕宗岳,井晓天,鲜林云,等.热处理对连续油管焊缝沟槽腐蚀行为的影响[J].材料热处理技术,2011,40(8):150-153.
【17】祝成龙,赵国仙,薛艳,等.温度对连续油管QT-900在CO2环境中腐蚀行为的影响[J].腐蚀与防护,2013,34(3):232-235.
【18】薛玉娜,雒设计,刘明,等.CT80连续油管钢的电化学腐蚀行为[J].腐蚀科学与防护技术,2013,25(1):23-29.
【19】宋诗哲.腐蚀电化学研究方法[M].北京:化学工业出版社,1988:120.
【20】张文钺.焊接冶金学基本原理[M].北京:机械工业出版社,1996.
相关信息