选区激光熔化成型GH3536合金的显微组织与拉伸性能
Microstructure and Tensile Properties of GH3536 Alloy Formed by SLM
摘 要
采用选区激光熔化（SLM）成型技术制备了GH3536合金试样，并对其显微组织与拉伸性能进行了分析。结果表明：SLM成型GH3536合金试样的基体显微组织为奥氏体，试样内部存在明显的微裂纹，纵向和横向的显微组织形貌存在明显不同；该试样纵向的拉伸性能优于横向的，相对于热轧Hastelloy X（GH3536）合金，SLM成型GH3536合金试样的强度较好，但塑性较差。
GH3536合金
显微组织
拉伸性能
selective laser melting
GH3536 alloy
microstructure
tensile property
Abstract
GH3536 alloy samples were prepared by selective laser melting (SLM) and their microstructure and tensile properties were analyzed. The results show that the matrix microstructure of GH3536 alloy formed by SLM was austenite, and there were obvious micro cracks inside the samples. The longitudinal and transversal microstructure of the sample was obviously different. The longitudinal tensile properties of the samples were better than that of the transversal ones. Compared with hot rolled Hastelloy X (GH3536) alloy, the strength of GH3536 alloy samples formed by SLM was better, but the plasticity was poorer.
中图分类号 TG131 DOI 10.11973/lhjy-wl201901004
所属栏目 试验与研究
基金项目 上海市应用技术开发专项资金项目（2015-101）
收稿日期 2018/1/23
修改稿日期
网络出版日期
作者单位点击查看
备注刘凯(1992-),男,硕士研究生,主要从事3D打印金属性能的研究,13651623104@163.com
引用该论文: LIU Kai,WANG Rong,QI Hai,YANG Qiyun,LI Yali. Microstructure and Tensile Properties of GH3536 Alloy Formed by SLM[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(1): 15～18
刘凯,王荣,祁海,杨启云,李雅莉. 选区激光熔化成型GH3536合金的显微组织与拉伸性能[J]. 理化检验－物理分册, 2019, 55(1): 15～18
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】范立坤. 增材制造用金属粉末材料的关键影响因素分析[J]. 理化检验(物理分册),2015,51(7):480-482.
【2】张学军,唐思熠,肇恒跃,等. 3D打印技术研究现状和关键技术[J]. 材料工程,2016,44(2):122-128.
【3】WANG D, SONG C, YANG Y, et al. Investigation of crystal growth mechanism during selective laser melting and mechanical property characterization of 316L stainless steel parts[J]. Materials and Design,2016,100:291-299.
【4】刘业胜,韩品连,胡寿丰,等. 金属材料激光增材制造技术及在航空发动机上的应用[J]. 航空制造技术,2014,454(10):62-67.
【5】巩水利,锁红波,李怀学. 金属增材制造技术在航空领域的发展与应用[J]. 航空制造技术,2013,433(13):66-71.
【6】周隐玉,王飞,薛春. 3D打印18Ni300模具钢的显微组织和力学性能[J]. 理化检验(物理分册),2016,52(4):243-246.
【7】杨启云,吴玉道,沙菲. 选区激光熔化成型Inconel625合金的显微组织及力学性能[J]. 机械工程材料,2016,40(6):83-87.
【8】黄文普,喻寒琛,殷杰,等. 激光选区熔化成型K4202镍基铸造高温合金的组织和性能[J]. 金属学报,2016,52(9):1089-1095.
【2】张学军,唐思熠,肇恒跃,等. 3D打印技术研究现状和关键技术[J]. 材料工程,2016,44(2):122-128.
【3】WANG D, SONG C, YANG Y, et al. Investigation of crystal growth mechanism during selective laser melting and mechanical property characterization of 316L stainless steel parts[J]. Materials and Design,2016,100:291-299.
【4】刘业胜,韩品连,胡寿丰,等. 金属材料激光增材制造技术及在航空发动机上的应用[J]. 航空制造技术,2014,454(10):62-67.
【5】巩水利,锁红波,李怀学. 金属增材制造技术在航空领域的发展与应用[J]. 航空制造技术,2013,433(13):66-71.
【6】周隐玉,王飞,薛春. 3D打印18Ni300模具钢的显微组织和力学性能[J]. 理化检验(物理分册),2016,52(4):243-246.
【7】杨启云,吴玉道,沙菲. 选区激光熔化成型Inconel625合金的显微组织及力学性能[J]. 机械工程材料,2016,40(6):83-87.
【8】黄文普,喻寒琛,殷杰,等. 激光选区熔化成型K4202镍基铸造高温合金的组织和性能[J]. 金属学报,2016,52(9):1089-1095.
相关信息