5252H32铝合金维氏硬度试验的测量不确定度评定
Uncertainty Evaluation on Measurement of Vickers Hardness Test of 5252H32 Aluminum Alloy
摘 要
依据GB/T 4340.1-2009对5252H32铝合金进行了维氏硬度试验，并对试验结果进行了测量不确定度评定。结果表明：5252H32铝合金维氏硬度试验的测量不确定度主要来源于压痕对角线的不确定度、载荷的不确定度及数值修约引入的不确定度；控制影响不确定度的主要因素，可以减小测量不确定度，保证试验结果的准确性。
维氏硬度试验
不确定度评定
aluminum alloy
Vickers hardness test
uncertainty evaluation
Abstract
The Vickers hardness of 5252H32 aluminum alloy was tested according to GB/T 4340.1-2009, and the uncertainty of the test results was evaluated. The results show that the uncertainty of Vickers hardness measurement of 5252H32 aluminum alloy mainly comes from the uncertainty of diagonal indentation, the uncertainty of load and the uncertainty introduced by digital revision. Controlling the main factors affecting the uncertainty can reduce the uncertainty of measurement and ensure the accuracy of the test results.
中图分类号 TH823 DOI 10.11973/lhjy-wl201901008
所属栏目 试验技术与方法
基金项目
收稿日期 2018/3/15
修改稿日期
网络出版日期
作者单位点击查看
备注潘飚(1970-),男,高级工程师,主要从事材料分析测试研究工作,1847902925@qq.com
引用该论文: PAN Biao. Uncertainty Evaluation on Measurement of Vickers Hardness Test of 5252H32 Aluminum Alloy[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(1): 33～34
潘飚. 5252H32铝合金维氏硬度试验的测量不确定度评定[J]. 理化检验－物理分册, 2019, 55(1): 33～34
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡水江,李生初,杨航飞,等. 金属材料维氏硬度测量不确定度的评定[J]. 金属制品,2009,35(1):59-60.
【2】尹立新,王萍. 显微维氏硬度测量不确定度评定[J]. 首钢科技,2007(1):49-52.
【3】张红菊,吴磊,李璞,等. 维氏硬度试验在进行NADCAP实验室认证时应注意的要点[J]. 理化检验(物理分册),2016,52(12):875-877.
【4】张宪,穆丹宁. 金属材料维氏硬度试验测量不确定度的评定[J]. 理化检验(物理分册),2017,53(6):410-412.
【5】杜凯,张忠和. FV520B钢和Q235A钢焊接接头的维氏硬度试验[J]. 理化检验(物理分册),2017,53(1):24-28.
【2】尹立新,王萍. 显微维氏硬度测量不确定度评定[J]. 首钢科技,2007(1):49-52.
【3】张红菊,吴磊,李璞,等. 维氏硬度试验在进行NADCAP实验室认证时应注意的要点[J]. 理化检验(物理分册),2016,52(12):875-877.
【4】张宪,穆丹宁. 金属材料维氏硬度试验测量不确定度的评定[J]. 理化检验(物理分册),2017,53(6):410-412.
【5】杜凯,张忠和. FV520B钢和Q235A钢焊接接头的维氏硬度试验[J]. 理化检验(物理分册),2017,53(1):24-28.
相关信息