Discussion on Upper Temperature Limit of 12Cr2MoWVTiB Steel Tube in Superheater for Power Plant
摘 要
以某电厂在当量温度585 ℃运行约14万h的过热器受热面12Cr2MoWVTiB钢管作为研究对象,研究了其宏观形貌、化学成分、显微组织及室温和高温力学性能,对其使用温度上限进行了探讨。结果表明:该钢管未出现明显的胀粗和减薄现象,组织中未见蠕变孔洞,组织老化级别为3级,室温力学性能比未服役的略有下降,仍满足标准要求;该钢管在运行约14万h后仍具有良好的抗高温蠕变性能,其持久强度仅比标准指标低12.1 MPa;结合该电厂过热器受热面管的运行情况认为,12Cr2MoWVTiB钢受热面管可以在585 ℃下安全运行,这与DL/T 715-2015规定的575 ℃使用温度上限有所冲突。
Abstract
A superheater in power plant was operated at equivalent temperature of 585 ℃ for 140 000 h; Macromorphology, chemical composition, microstructure and mechanical properties at room temperature and elevated temperature of the heat surface tube of 12Cr2MoWVTiB steel from the superheater were studied, and upper temperature limit of the steel tube was discussed. The results show that no obvious swelling and thinning were observed in the steel tube. No creep holes were found in the microstructure and the aging grade of microstructure was grade 3. The mechanical properties at room temperature were slightly lower than those of unoperated steel tube, and still met the standard requirements. After service for about 140 000 h, the steel tube still had good high-temperature creep resistance; the stress-rupture strength was only 12.1 MPa lower than the standard requirement. Considering the running situation of heat surface tube in superheator of the power plant, it was suggested that 12Cr2MoWVTiB steel heat surface tube can be reliably operated at temperatures no higher than 585 ℃; this conflicts with the 575 ℃ upper temperature limit specified in DL/T 715-2015.
中图分类号 TK228 DOI 10.11973/jxgccl201903005
所属栏目 试验研究
基金项目
收稿日期 2018/1/13
修改稿日期 2019/1/14
网络出版日期
作者单位点击查看
备注句光宇(1990-),男,山西朔州人,工程师,硕士
引用该论文: JU Guangyu,WANG Ti,SONG Li,YUAN Hongyu,LIU Wensheng,XIE Zhaozeng,WANG Zhiwu. Discussion on Upper Temperature Limit of 12Cr2MoWVTiB Steel Tube in Superheater for Power Plant[J]. Materials for mechancial engineering, 2019, 43(3): 24~28
句光宇,王体,宋利,袁红玉,刘文生,谢照增,王志武. 电厂过热器用12Cr2MoWVTiB钢管使用温度上限的探讨[J]. 机械工程材料, 2019, 43(3): 24~28
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】雷文娟, 焦瑞华. 12Cr2MoWVTiB钢焊后热处理工艺的探讨[J]. 金属加工:热加工, 2009(4):36-38.
【2】张磊, 廉根宽. 电站锅炉四管泄漏分析与治理[M]. 北京:中国水利水电出版社, 2009:5-6.
【3】柯浩,冯砚厅,徐雪霞,等. 某电站锅炉12Cr2MoWVTiB钢过热器爆管原因分析[C]//中国计量协会冶金分会2014年会暨能源计量与绿色冶金论坛论文集.北京:中国计量协会冶金分会, 2014:582-585.
【4】曹文浩,犹公,赵世英,等.300 MW、600 MW锅炉用12Cr2MoWVTiB钢管运行可靠性试验研究[J].锅炉制造,1999(2):39-46.
【2】张磊, 廉根宽. 电站锅炉四管泄漏分析与治理[M]. 北京:中国水利水电出版社, 2009:5-6.
【3】柯浩,冯砚厅,徐雪霞,等. 某电站锅炉12Cr2MoWVTiB钢过热器爆管原因分析[C]//中国计量协会冶金分会2014年会暨能源计量与绿色冶金论坛论文集.北京:中国计量协会冶金分会, 2014:582-585.
【4】曹文浩,犹公,赵世英,等.300 MW、600 MW锅炉用12Cr2MoWVTiB钢管运行可靠性试验研究[J].锅炉制造,1999(2):39-46.
相关信息