Corrosion Law of Wellbore in Wenchang Oil Field
摘 要
通过井下多臂井径仪(MIT)检测了解文昌油田井筒的腐蚀概况,利用高温高压反应釜进行了模拟试验,研究了井筒的腐蚀规律。结果表明:井筒在上部位置和中下部位置腐蚀较为严重;随着温度的升高,1Cr试样的腐蚀速率先增大后减小,在75 ℃时腐蚀最严重;腐蚀介质流速越大试样的腐蚀速率越大;随着二氧化碳分压的增加,试样的腐蚀速率增大,腐蚀由全面腐蚀转变为局部腐蚀,腐蚀坑也变大变深,并且有黑色腐蚀产物附着;1Cr试样和13Cr试样发生电偶腐蚀时,1Cr试样表面发生明显的局部腐蚀,腐蚀速率高于13Cr试样的。
Abstract
Through underground MIT test, the corrosion profile of the wellbore in Wenchang oilfield was studied. A simulation experiment was carried out using a high temperature and high pressure autoclave to study the corrosion law of the wellbore. The results show that the corrosion of the wellbore in the upper position and lower part was more serious. With the increase of temperature, the corrosion rate of the 1Cr sample increased first and then decreased, and the corrosion was the most serious at 75 ℃. The greater the flow rate of the corrosive medium, the greater the corrosion rate of the sample. As the partial pressure of carbon dioxide increased, the corrosion rate of the sample increased, the corrosion changed from general corrosion to localized corrosion, the corrosion pit became larger and deeper, and black corrosion products adhered. When galvanic corrosion occurred in the 1Cr and 13Cr samples, significant localized corrosion occurred on the surface of the 1Cr sample, and the corrosion rate was higher than that of the 13Cr sample.
中图分类号 TG172 DOI 10.11973/fsyfh-201905016
所属栏目 应用技术
基金项目
收稿日期 2017/10/20
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHENG Huaan,WANG Jiawei,WEN Ninghua,WANG Xiuyun,ZHOU Yuxia,WANG Chenglong,LI Dapeng. Corrosion Law of Wellbore in Wenchang Oil Field[J]. Corrosion & Protection, 2019, 40(5): 387
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘绘新,苏东平. 川东气田油管腐蚀现象的基本特征[J]. 天然气工业,2000,20(5):77-79.
【2】李建忠,王海成,李宁. 油气田开发中二氧化碳腐蚀的危害与研究现状[J]. 广州化工,2011,39(21):21-23,56.
【3】张学元,王凤平,陈卓元,等. 油气开发中二氧化碳腐蚀的研究现状和趋势[J]. 油田化学,1997,14(2):190-196.
【4】MURATA T,SATO E,MATSUHASHI R. Factors controlling corrosion of steels in CO2-saturated environments[J]. Advances in CO2 Corrosion,1984(1):64-71.
【2】李建忠,王海成,李宁. 油气田开发中二氧化碳腐蚀的危害与研究现状[J]. 广州化工,2011,39(21):21-23,56.
【3】张学元,王凤平,陈卓元,等. 油气开发中二氧化碳腐蚀的研究现状和趋势[J]. 油田化学,1997,14(2):190-196.
【4】MURATA T,SATO E,MATSUHASHI R. Factors controlling corrosion of steels in CO2-saturated environments[J]. Advances in CO2 Corrosion,1984(1):64-71.
相关信息