4340钢零件热处理后磁粉检测试验
Experiment of Magnetic Particle Inspection of Heat Treated 4340 Steel Parts
摘 要
对4340钢零件热处理后进行磁粉检测时，发现零件表面存有磁痕显示。通过对不同试件进行对比试验和分析可知，该磁痕显示并非热处理裂纹，而是合金偏析，并对此提出了改进建议。
磁痕
偏析
工艺试验
magnetic powder inspection
magnetic trace
segregation
process test
Abstract
When the 4340 steel parts were performed by magnetic powder inspection after heat treatment, magnetic traces appeared. Through comparison test and analysis, it is found that the magnetic trace is not a heat treatment crack, but an alloy segregation and suggestions for improvement are put forward.
中图分类号 TG157 TG115.28 DOI 10.11973/wsjc201905010
所属栏目 试验研究
基金项目
收稿日期 2018/10/5
修改稿日期
网络出版日期
作者单位点击查看
联系人作者胡久(hujiu108@163.com)
备注胡久(1987-),男,硕士,工程师,主要从事飞机金属材料的选用及应用工作
引用该论文: HU Jiu,MA Lu,CHEN Yan,WANG Yukui,WANG Chong,HUANG Zhiyong. Experiment of Magnetic Particle Inspection of Heat Treated 4340 Steel Parts[J]. Nondestructive Testing, 2019, 41(5): 44～46
胡久,马路,陈彦,王宇魁,王翀,黄智勇. 4340钢零件热处理后磁粉检测试验[J]. 无损检测, 2019, 41(5): 44～46
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】龙晓华.磁粉探伤中磁痕显示的分类、判定及处理[J].中国新技术新产品,2011(10):148.
相关信息