X70钢输气管道凹陷失效分析
Failure Analysis on Dent of X70 Steel Gas Pipeline
摘 要
某X70钢天然气输气管道发生凹陷泄漏事故，通过宏观分析、力学性能试验、金相检验、微观分析、残余应力测试、有限元模拟等方法，对管道凹陷泄漏的原因进行了分析。结果表明：管道在铺设时受到岩石的挤压而产生凹陷，在管道服役过程中，凹陷处壁厚严重减薄，应力水平大幅升高而产生了微裂纹，裂纹逐渐扩展穿透管壁，最终导致管道泄漏。
凹陷
泄漏
有限元模拟
gas pipeline
dent
leakage
finite element simulation
Abstract
A dent leakage accident occurred in an X70 steel natural gas pipeline. By means of macro analysis, mechanical properties test, metallographic examination, micro analysis, residual stress testing and finite element simulation, the causes of pipeline dent leakage were analyzed. The results show that the pipeline was compacted by rock during laying pipelines, which resulted in pipeline dent. During the service of the pipeline, micro cracks formed in the dent due to the wall thickness of the depression was seriously thinned and the stress level rised sharply. The crack propagated gradually and penetrated the pipeline wall, eventually led to pipeline leakage.
中图分类号 TE973 DOI 10.11973/lhjy-wl201907011
所属栏目 质量控制与失效分析
基金项目 "十三五"国家重点研发计划（2017YFC0805804）；中国石油天然气股份有限公司重大科技专项（2016E-0610）
收稿日期 2019/3/26
修改稿日期
网络出版日期
作者单位点击查看
备注武刚(1985-),男,工程师,主要从事油气管道及储存设施完整性的研究,wugang010@cnpc.com.cn
引用该论文: WU Gang,ZHU Lixia,LUO Jinheng,LIU Chang,LI Lifeng,SUN Mingnan. Failure Analysis on Dent of X70 Steel Gas Pipeline[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(7): 478～482
武刚,朱丽霞,罗金恒,刘畅,李丽锋,孙明楠. X70钢输气管道凹陷失效分析[J]. 理化检验－物理分册, 2019, 55(7): 478～482
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄维和, 郑洪龙,王婷. 我国油气管道建设运行管理技术及发展展望[J]. 油气储运,2014,33(12):1259-1262.
【2】李鹤林,吉玲康,田伟. 西气东输一、二线管道工程的几项重大技术进步[J]. 天然气工业,2010,30(4):1-9.
【3】杨祖佩,郑洪龙,冯庆善,等. 管道完整性管理技术[M]. 北京:石油工业出版社,2011.
【4】杨琼,帅健,左尚志. 管道凹陷研究现状[J]. 油气储运,2009,28(6):10-15.
【5】COSHAM A, HOPKINS P. The effect of dents in pipelines-guidance in the pipeline defect assessment manual[J]. International Journal of Pressure Vessels & Piping,2004,81(2):127-139.
【6】DAWSON S J, RUSSELL A, PATTERSON A. Emerging techniques for enhanced assessment and analysis of dents[J]. Journal of Pipeline Engineering,2008,7(3):189-204.
【7】巴发海,李凯. 金属材料残余应力的测定方法[J]. 理化检验(物理分册),2017,53(11):771-777.
【8】王晓宇,任丽萍,徐星泓,等. X射线衍射法测定圆棒表面残余应力的影响因素[J]. 理化检验(物理分册),2017,53(7):471-473.
【9】孙明楠,高健,林冬,等. 含凹陷油气管道安全评估方法[C]//2015年全国失效分析学术会议论文集. 北京:中国机械工程学会,2015:432-435.
【10】刘啸奔,张宏,唐凯,等. 基于有限元的含凹陷X60管道极限压力研究[C]//2013年中国国际管道会议暨第一届中国管道与储罐腐蚀与防护学术交流会论文集. 北京:中国腐蚀与防护学会,2013:224-228.
【11】苏成功,刘燕,王威强,等. 压痕对不锈钢材料表面残余应力的影响[J]. 山东大学学报(工学版),2016,47(1):90-96.
【2】李鹤林,吉玲康,田伟. 西气东输一、二线管道工程的几项重大技术进步[J]. 天然气工业,2010,30(4):1-9.
【3】杨祖佩,郑洪龙,冯庆善,等. 管道完整性管理技术[M]. 北京:石油工业出版社,2011.
【4】杨琼,帅健,左尚志. 管道凹陷研究现状[J]. 油气储运,2009,28(6):10-15.
【5】COSHAM A, HOPKINS P. The effect of dents in pipelines-guidance in the pipeline defect assessment manual[J]. International Journal of Pressure Vessels & Piping,2004,81(2):127-139.
【6】DAWSON S J, RUSSELL A, PATTERSON A. Emerging techniques for enhanced assessment and analysis of dents[J]. Journal of Pipeline Engineering,2008,7(3):189-204.
【7】巴发海,李凯. 金属材料残余应力的测定方法[J]. 理化检验(物理分册),2017,53(11):771-777.
【8】王晓宇,任丽萍,徐星泓,等. X射线衍射法测定圆棒表面残余应力的影响因素[J]. 理化检验(物理分册),2017,53(7):471-473.
【9】孙明楠,高健,林冬,等. 含凹陷油气管道安全评估方法[C]//2015年全国失效分析学术会议论文集. 北京:中国机械工程学会,2015:432-435.
【10】刘啸奔,张宏,唐凯,等. 基于有限元的含凹陷X60管道极限压力研究[C]//2013年中国国际管道会议暨第一届中国管道与储罐腐蚀与防护学术交流会论文集. 北京:中国腐蚀与防护学会,2013:224-228.
【11】苏成功,刘燕,王威强,等. 压痕对不锈钢材料表面残余应力的影响[J]. 山东大学学报(工学版),2016,47(1):90-96.
相关信息