Applicability of Anti-corrosion Coatings for New Type Ground Gathering Pipelines
摘 要
采用高温高压反应釜模拟塔河油田高矿化度,高H2S和CO2的腐蚀环境,通过检测高温高压腐蚀试验后涂层的外观、铅笔硬度、附着力、漏点、耐冲击等物理性能,研究了JG-01耐酸涂层和EP-98环氧无溶剂涂层的防护性能。结果表明:经30 d试验后,EP-98环氧无溶剂涂层表面起泡,发生失效;JG-01耐酸涂层的各项物理性能均为未发生改变。经过高温高压腐蚀试验后,JG-01耐酸涂层的极化曲线出现明显钝化现象,腐蚀电流密度基本不变,且仍具有极高的极化电阻,即JG-01耐酸涂层在该环境中具有较好的抗腐蚀性能。
Abstract
A high-temperature and high-pressure reactor was used to simulate on-site corrosion environment of Tahe oilfield with high salinity and high H2S and CO2. The protective properties of JG-01 acid-resistant coating and EP-98 epoxy solvent-free coating were studied by testing the physical properties of coating, pencil hardness, adhesion, leak point and impact resistance after high temperature and high pressure corrosion test. The results showed that after 30 days of testing, the surface of EP-98 epoxy solvent-free coating foamed and failed; the physical properties of JG-01 acid-resistant coating were unchanged. After the high temperature and high pressure corrosion test, the polarization curve of the JG-01 acid-resistant coating showed obvious passivation, the corrosion current density was basically unchanged, and still had a very high polarization resistance. JG-01 acid-resistant coating has good corrosion resistance in this environment.
中图分类号 TG174 DOI 10.11973/fsyfh-201907010
所属栏目 应用技术
基金项目
收稿日期 2019/1/15
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: YAO Bin,XIAO Wenwen,WU Xiaoxian,XU Yanyan,GE Pengli,GAO Duolong. Applicability of Anti-corrosion Coatings for New Type Ground Gathering Pipelines[J]. Corrosion & Protection, 2019, 40(7): 519
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王丹, 袁世娇, 吴小卫, 等. 油气管道CO2/H2S腐蚀及防护技术研究进展. 表面技术, 2016,45(3):31-37.
【2】舒勇. 防腐防垢综合配套技术在开发中后期油田集输系统中的应用. 石油工程建设, 2003,29(2):26-29.
【3】张显程, 巩建鸣, 涂善东, 等. 涂层缺陷对涂层失效与基体腐蚀行为的影响研究. 材料科学与工程学报, 2003,21(6):922-926.
【4】臧国军, 崔斌. 油气集输管道内涂层金属腐蚀失效机理研究. 石油化工设计, 2005,22(4):54-56.
【5】GONZÁLEZ S, CÁCERES F, FOX V, et al. Resistance of metallic substrates protected by an organic coating containing aluminum powder. Progress in Organic Coatings, 2003,46(4):317-323.
【6】吴跃焕.钢铁腐蚀与涂料湿附着力的关系. 合成材料老化与应用, 2002,31(1):28-31.
【7】周斌葛, 何毅, 王雅诗, 等. 管道用酚醛环氧树脂内涂层失效分析. 广东化工, 2012,39(7):7-8.
【8】元辛.涂层/金属体系腐蚀失效行为的理论及实验研究. 西安:西北工业大学, 2016, 52-60.
【2】舒勇. 防腐防垢综合配套技术在开发中后期油田集输系统中的应用. 石油工程建设, 2003,29(2):26-29.
【3】张显程, 巩建鸣, 涂善东, 等. 涂层缺陷对涂层失效与基体腐蚀行为的影响研究. 材料科学与工程学报, 2003,21(6):922-926.
【4】臧国军, 崔斌. 油气集输管道内涂层金属腐蚀失效机理研究. 石油化工设计, 2005,22(4):54-56.
【5】GONZÁLEZ S, CÁCERES F, FOX V, et al. Resistance of metallic substrates protected by an organic coating containing aluminum powder. Progress in Organic Coatings, 2003,46(4):317-323.
【6】吴跃焕.钢铁腐蚀与涂料湿附着力的关系. 合成材料老化与应用, 2002,31(1):28-31.
【7】周斌葛, 何毅, 王雅诗, 等. 管道用酚醛环氧树脂内涂层失效分析. 广东化工, 2012,39(7):7-8.
【8】元辛.涂层/金属体系腐蚀失效行为的理论及实验研究. 西安:西北工业大学, 2016, 52-60.
相关信息