Optimum Method for Grain Display of High Strength Steel A-100
摘 要
采用不同的化学浸蚀液,研究了A-100高强钢晶界的显示效果;使用恒温水浴锅,测定了在不同温度的浸蚀液下晶界的显示时间;利用金相显微镜观察该钢晶界显示是否清晰。结果表明:A-100高强钢晶粒显示的推荐化学浸蚀液为过饱和苦味酸+雕牌洗涤剂溶液(结晶状)以及过饱和苦味酸+白猫洗涤剂溶液(结晶状);浸蚀液温度为40℃或45℃时,清晰显示晶界所用的时间最短。
Abstract
The display effects of grain boundary of high strength steel A-100 were analyzed by different chemical etchant. The display time of grain boundary in etching solution at different temperatures was measured by thermostat water bath, and the morphology of grain boundary was observed by metallographic microscope. The results show that the optimum etching solution for grain of high strength steel A-100 is supersaturated picric acid+eagle brand detergent solution (crystalline shape) or supersaturated picric acid+white cat brand detergent solution (crystalline shape). When the temperature of etching solution is 40℃ or 45℃, the clear display of grain boundaries takes the shortest time.
中图分类号 TG113 DOI 10.11973/lhjy-wl201908005
所属栏目 专题报道(金属晶粒度测定方法)
基金项目
收稿日期 2019/4/16
修改稿日期
网络出版日期
作者单位点击查看
备注刘玉芬(1982-),女,工程师,学士,主要从事金相检验技术分析工作,13504138958@163.com
引用该论文: LIU Yufen. Optimum Method for Grain Display of High Strength Steel A-100[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(8): 538~541
刘玉芬. A-100高强钢晶粒显示优选方法[J]. 理化检验-物理分册, 2019, 55(8): 538~541
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】叶文冰. A100二次硬化型超高强度合金研制[J]. 特钢技术,2014,20(1):14-16.
【2】孙朝明,孟玉堂,杨桂珠. 金相晶粒度定量评定技术进展[J]. 理化检验(物理分册),2012,48(12):814-817.
【3】王长健,王钢. 300M钢晶粒度腐蚀方法研究[J]. 大型铸锻件,2004(3):13-16.
【4】黄振东. 钢铁金相图谱[M]. 北京:中国科技文化出版社,2005.
【2】孙朝明,孟玉堂,杨桂珠. 金相晶粒度定量评定技术进展[J]. 理化检验(物理分册),2012,48(12):814-817.
【3】王长健,王钢. 300M钢晶粒度腐蚀方法研究[J]. 大型铸锻件,2004(3):13-16.
【4】黄振东. 钢铁金相图谱[M]. 北京:中国科技文化出版社,2005.
相关信息