Techonology of Environment Friendly Cyanide-Free Electro-Brush Silver Plating and Its Practical Application
摘 要
为满足电力系统检修工作中对供电设备修复技术的新要求,以焦磷酸钾为络合剂成功地制备出了性能优异的无氰电刷镀液,并采用电刷镀技术在铜基体材料表面制备得银镀层;通过镀层附着力试验、扫描电镜(SEM)、能谱(EDS)等方法对银镀层的结构和性能进行表征。结果表明:镀液性能稳定,经过两周的密封保存,镀液没有沉淀析出且电导率无明显变化;银镀层在铜基体上附着力良好,镀层厚度能超过20 μm,达到了相关应用的要求;该电刷镀工艺能够有效修复隔离开关、导流接头、接线柱、设备线夹、刀闸触头以及三相连接板的缺陷,使修复后设备性能达到使用要求。
Abstract
In order to meet the new requirements for repairing technology of power supply equipment in power system maintenance work. A cyanide-free brush plating solution with excellent performance was successfully prepared with potassium pyrophosphate as a complexing agent. And silver plating was prepared on the surface of copper as a substrate by electro-brush plating. The structure and properties of the silver plating were characterized by adhesion testing, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS). The results show that the performance of the plating solution was stable. After two weeks of sealing and preservation, the plating solution did not precipitate and the conductivity did not change significantly. The silver plating had good adhesion on the copper substrate, and the thickness of the silver plating was over 20 μm, meeting the requirements of related applications. The electro-brush plating process can effectively repair defects on isolating switches, diversion joints, binding posts, equipment clamps, knife gate contacts and three-phase connection boards, making the repaired device performance meet the usage requirements.
中图分类号 TG174.44 DOI 10.11973/fsyfh-201908007
所属栏目 试验研究
基金项目 湖北省技术创新专项重大项目(2018ACA152);国网湖北省电力有限公司孝感供电公司项目(2017421408000083);国网湖北省电力有限公司孝感供电公司项目(2017421408000037)
收稿日期 2018/11/28
修改稿日期
网络出版日期
作者单位点击查看
联系人作者李伟(840368992@qq.com)
引用该论文: HUANG Chaofan,ZHENG Kewang,WANG Wei,QIN Caiqin,ZHANG Jianbing,YANG Fan,LI Wei. Techonology of Environment Friendly Cyanide-Free Electro-Brush Silver Plating and Its Practical Application[J]. Corrosion & Protection, 2019, 40(8): 584
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴青龙. 无氰电镀银工艺及机理的研究. 哈尔滨:哈尔滨工业大学, 2007.
【2】秦峰, 张荣红, 赵以娟, 等. 传统银饰的制作及其工艺特点. 宝石和宝石学杂志, 2007, 9(1):31-33.
【3】刘仁志. 无氰镀银的工艺与技术现状. 电镀与精饰, 2006, 28(1):21-24.
【4】张庆, 成旦红, 郭国才,等. 无氰镀银技术发展及研究现状. 电镀与精饰, 2007, 29(5):12-16.
【5】梁旭东. 刷镀银工艺及其在电机产品上的应用. 东方电气评论, 2017, 31(1):85-88.
【6】杨勇彪, 张正富, 陈庆华,等. 铜基无氰镀银的研究. 云南冶金, 2004, 33(4):20-22.
【7】王宗雄, 储荣邦, 鲍新华, 等. 实用氰化镀银工艺. 电镀与涂饰, 2015, 34(24):1424-1438.
【8】CHEN J S, FANG Y M, QIU Q Y, et al. Electrodeposition of bright gold-a green path using hypoxanthine as a complexing agent. Green Chemistry, 2011, 13(9):2339-2343.
【9】曾勇. 电刷镀Ni/石墨复合镀层的工艺及性能研究.煤矿机械, 2017,38(7):69-71.
【10】王宗雄.鲍新华,任吉华.电刷镀的设备、镀液配方及应用.电镀与涂饰,2017,36(12):632-642.
【11】车丽媛, 吴昊, 夏阳, 等. 无氰碱性低锡铜-锡合金电镀工艺. 电镀与环保, 2017, 37(3):9-12.
【12】张杰, 俞培祥, 周海飞,等. 氰化电镀与无氰刷镀下触头镀银层性能比较. 腐蚀与防护, 2014, 35(11):1131-1134.
【13】吕晓东. 高压电力设备试验方法及安全措施的深入研究. 工程技术研究, 2017(12):96-97.
【2】秦峰, 张荣红, 赵以娟, 等. 传统银饰的制作及其工艺特点. 宝石和宝石学杂志, 2007, 9(1):31-33.
【3】刘仁志. 无氰镀银的工艺与技术现状. 电镀与精饰, 2006, 28(1):21-24.
【4】张庆, 成旦红, 郭国才,等. 无氰镀银技术发展及研究现状. 电镀与精饰, 2007, 29(5):12-16.
【5】梁旭东. 刷镀银工艺及其在电机产品上的应用. 东方电气评论, 2017, 31(1):85-88.
【6】杨勇彪, 张正富, 陈庆华,等. 铜基无氰镀银的研究. 云南冶金, 2004, 33(4):20-22.
【7】王宗雄, 储荣邦, 鲍新华, 等. 实用氰化镀银工艺. 电镀与涂饰, 2015, 34(24):1424-1438.
【8】CHEN J S, FANG Y M, QIU Q Y, et al. Electrodeposition of bright gold-a green path using hypoxanthine as a complexing agent. Green Chemistry, 2011, 13(9):2339-2343.
【9】曾勇. 电刷镀Ni/石墨复合镀层的工艺及性能研究.煤矿机械, 2017,38(7):69-71.
【10】王宗雄.鲍新华,任吉华.电刷镀的设备、镀液配方及应用.电镀与涂饰,2017,36(12):632-642.
【11】车丽媛, 吴昊, 夏阳, 等. 无氰碱性低锡铜-锡合金电镀工艺. 电镀与环保, 2017, 37(3):9-12.
【12】张杰, 俞培祥, 周海飞,等. 氰化电镀与无氰刷镀下触头镀银层性能比较. 腐蚀与防护, 2014, 35(11):1131-1134.
【13】吕晓东. 高压电力设备试验方法及安全措施的深入研究. 工程技术研究, 2017(12):96-97.
相关信息