BZ102井S13Cr110钢油管裂纹成因分析
Cause Analysis on Cracks of an S13Cr110 Steel Tubing in Well BZ102
摘 要
BZ102井S13Cr110钢油管出现裂纹，通过磁粉探伤、金相分析、点蚀坑分析、化学成分分析、力学性能试验等方法对裂纹产生的原因进行了分析。结果表明：油管纵向裂纹为应力腐蚀裂纹，裂纹产生与A环空腐蚀环境、油管材料特性及油管受力条件有关。
裂纹
磁粉探伤
应力腐蚀
tubing
crack
magnetic particle testing
stress corrosion
Abstract
Cracks appeared on an S13Cr110 steel tubing in well BZ102. The causes of cracks were analyzed by means of magnetic particle testing, metallographic analysis, pit analysis, chemical composition analysis and mechanical property test. The results show that the longitudinal cracks of the tubing was stress corrosion cracks. The formation of the cracks was related to the corrosive environment in annulus A, the material characteristics and the stress condition of the tubing.
中图分类号 TG946 TG115.2 DOI 10.11973/lhjy-wl201909017
所属栏目 质量控制与失效分析
基金项目
收稿日期 2018/9/3
修改稿日期
网络出版日期
作者单位点击查看
备注杨向同(1972-),男,高级工程师,主要从事测井及试油技术研究和管理工作,lvshuanlu@163.com
引用该论文: YANG Xiangtong,XIE Junfeng,SONG Yang,MA Lei,Lü Shuanlu,ZHAO Mifeng,LI Danping,WANG Hua,XUE Jijun,ZHU Lianggen. Cause Analysis on Cracks of an S13Cr110 Steel Tubing in Well BZ102[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2019, 55(9): 663～666
杨向同,谢俊峰,宋洋,马磊,吕拴录,赵密锋,李丹平,王华,薛继军,朱良根. BZ102井S13Cr110钢油管裂纹成因分析[J]. 理化检验－物理分册, 2019, 55(9): 663～666
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨向同,吕拴录,付安庆,等. 某天然气井改良型13Cr特殊螺纹接头油管腐蚀原因分[J]. 石油矿场机械,2016,45(10):78-81.
【2】杨向同,吕拴录,宋文文,等. 某井超级13Cr油管接箍开裂原因分析[J]. 石油管材与仪器2016,2(1):40-45.
【3】吕拴录,赵国仙,王新虎,等. 特殊螺纹接头油管腐蚀原因分析[J]. 腐蚀与防护,2005,26(4):179-181.
【4】LV S L, LUO F Q, XIANG J M, et al. Cause analysis on corrosion for API tubing[J]. Corrosion Science &Protect Technology,2008,20(5):388-390.
【5】吕拴录,相建民,常泽亮,等. 牙哈301井油管腐蚀原因分析[J]. 腐蚀与防护,2008,29(11):706-709.
【6】LV S L, XIANG J M, CHANG Z L, et al. Analysis of premium connection downhole tubing corrosion[J]. Material Performance,2008,47(5):66-69.
【7】YUAN P B, GUO S W, LV S L. Failure analysis of high-alloy oil well tubing coupling[J]. Material Performance,2010,49(8):68-71.
【8】张福祥,吕拴录,王振彪,等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全,2010,26(5):65-68.
【9】吕拴录,李元斌,王振彪,等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J]. 腐蚀与防护,2010,31(11):902-904.
【10】谢俊峰,宋文文,常泽亮,等. 某天然气井13Cr油管腐蚀原因分析[J]. 腐蚀与防护,2014,35(7):754-757.
【11】吕拴录,宋文文,杨向同,等. 某井S13Cr特殊螺纹接头油管柱腐蚀原因分析[J]. 腐蚀与防护,2015,36(1):76-83.
【12】吕拴录,李鹤林,韩勇,等. IEU G105钻杆腐蚀疲劳刺穿断裂原因分析[J]. 腐蚀与防护,2009,30(5):355-357.
【13】杨向同,吕拴录,邝献任,等. ZG105H井油管断裂原因分析及预防措施[J]. 理化检验(物理分册),2018,54(1):78-80.
【14】吕拴录,杨向同,宋文文,等. 某井超级13Cr特殊螺纹接头油管接箍横向开裂原因分析[J]. 理化检验(物理分册),2015,51(4):297-301.
【2】杨向同,吕拴录,宋文文,等. 某井超级13Cr油管接箍开裂原因分析[J]. 石油管材与仪器2016,2(1):40-45.
【3】吕拴录,赵国仙,王新虎,等. 特殊螺纹接头油管腐蚀原因分析[J]. 腐蚀与防护,2005,26(4):179-181.
【4】LV S L, LUO F Q, XIANG J M, et al. Cause analysis on corrosion for API tubing[J]. Corrosion Science &Protect Technology,2008,20(5):388-390.
【5】吕拴录,相建民,常泽亮,等. 牙哈301井油管腐蚀原因分析[J]. 腐蚀与防护,2008,29(11):706-709.
【6】LV S L, XIANG J M, CHANG Z L, et al. Analysis of premium connection downhole tubing corrosion[J]. Material Performance,2008,47(5):66-69.
【7】YUAN P B, GUO S W, LV S L. Failure analysis of high-alloy oil well tubing coupling[J]. Material Performance,2010,49(8):68-71.
【8】张福祥,吕拴录,王振彪,等. 某高压气井套压升高及特殊螺纹接头不锈钢油管腐蚀原因分析[J]. 中国特种设备安全,2010,26(5):65-68.
【9】吕拴录,李元斌,王振彪,等. 某高压气井13Cr油管柱泄漏和腐蚀原因分析[J]. 腐蚀与防护,2010,31(11):902-904.
【10】谢俊峰,宋文文,常泽亮,等. 某天然气井13Cr油管腐蚀原因分析[J]. 腐蚀与防护,2014,35(7):754-757.
【11】吕拴录,宋文文,杨向同,等. 某井S13Cr特殊螺纹接头油管柱腐蚀原因分析[J]. 腐蚀与防护,2015,36(1):76-83.
【12】吕拴录,李鹤林,韩勇,等. IEU G105钻杆腐蚀疲劳刺穿断裂原因分析[J]. 腐蚀与防护,2009,30(5):355-357.
【13】杨向同,吕拴录,邝献任,等. ZG105H井油管断裂原因分析及预防措施[J]. 理化检验(物理分册),2018,54(1):78-80.
【14】吕拴录,杨向同,宋文文,等. 某井超级13Cr特殊螺纹接头油管接箍横向开裂原因分析[J]. 理化检验(物理分册),2015,51(4):297-301.
相关信息