Effect of Thermal Tensile Deformation and Solution Aging Treatment on Microstructure of TC4-DT Titanium Alloy
摘 要
分别在α+β两相区(925℃)、近β两相区(960℃)、准β单相区(995℃)对TC4-DT钛合金进行等温恒应变速率热拉伸变形,再进行920,940,960,980℃固溶和550,720℃时效热处理,研究了其流变应力的变化趋势和不同工艺处理后的显微组织。结果表明:在拉伸变形初期,流变应力迅速增大至峰值后缓慢减小,同时流变应力降幅随变形温度的升高而减小;拉伸变形温度越高或变形量越大,组织中初生α相量越少,针状α相越多,形成的片层组织越多;经960,995℃拉伸变形和不同温度固溶处理后,固溶温度越高,析出的针状α相越多,越易形成片层组织;经拉伸变形、固溶和时效处理后的显微组织和时效处理前的差别不大,但在针状α相间的β相上析出了次生α相,且时效温度越高,针状α相越粗大,片层组织越明显。
Abstract
The isothermal constant strain rate hot tensile deformation was conducted on TC4-DT titanium alloy in α+β two-phase region (925℃), near-β two-phase region (960℃) and quasi-β single-phase region (995℃), respectively. And then solution at 950, 940, 960, 980℃ and aging at 550, 720℃ were carried out. The change trend of flow stress and microstructure after different treatment processes were studied. The results show that in the initial stage of tensile deformation, the flow stress increased rapidly to the peak value and then decreased slowly. The reduction extent of flow stress decreased with the increase of deformation temperature. The higher the tensile deformation temperature or the larger the deformation amount, the less the amount of primary α phase in the microstructure, and the more the needle-like α phase and the lamellar structure. The higher the solution temperature was, the more the needle-like α phase precipitated, and the easier the lamellar structure formed after tensile deformation of at 960, 995℃ and solution treatment at different temperatures. The microstructure after hot tensile deformation, solution and aging treatment had little difference from that before aging treatment, but the secondary α phase precipitated on β phases between needle-like α phases; the higher the aging temperature, the coarser the needle-like α phase, and the more obvious the lamellar structure.
中图分类号 TG146.23 DOI 10.11973/jxgccl201911006
所属栏目 材料性能及应用
基金项目 浙江省教育厅科研项目(Y201840231)
收稿日期 2019/4/26
修改稿日期 2019/10/14
网络出版日期
作者单位点击查看
备注潘巧玉(1982-),女,浙江东阳人,工程师,学士
引用该论文: PAN Qiaoyu,YU Xinping,QI Yongjie,HUANG Qinghua,PAN Guangyong. Effect of Thermal Tensile Deformation and Solution Aging Treatment on Microstructure of TC4-DT Titanium Alloy[J]. Materials for mechancial engineering, 2019, 43(11): 21~26
潘巧玉,余新平,齐永杰,黄庆华,潘光永. 热拉伸变形及固溶时效处理对TC4-DT钛合金显微组织的影响[J]. 机械工程材料, 2019, 43(11): 21~26
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】房卫萍,陈沦,史耀武,等.损伤容限钛合金的研究进展及应用现状[J].材料工程, 2010(9):95-98.
【2】VENKATESH B D, CHEN D L, BHOLE S D. Effect of heat treatment on mechanical properties of Ti-6Al-4V ELI alloy[J]. Materials Science & Engineering:A, 2009, 506(1/2):117-124.
【3】雷文光,韩栋,张永强,等.不同热处理工艺对TC4-DT钛合金棒材组织和性能的影响[J].材料导报, 2015, 29(7):120-123.
【4】朱知寿.航空结构用新型高性能钛合金材料技术研究与发展[J].航空科学技术, 2012(1):5-9.
【5】朱知寿,王庆如,郑永灵,等.损伤容限型钛合金新型β锻造工艺[J].中国有色金属学报,204,14(增刊3):13-16.
【6】张智,巨建辉,戚运莲,等.钛合金锻造工艺及其锻件的应用[J].热加工工艺,2010, 39(23):34-37.
【7】田伟,伏宇,钟燕,等.锻造工艺对TC17钛合金的显微组织和力学性能的影响[J].材料热处理学报,2016, 37(9):57-61.
【8】杨海瑛,陈军,赵永庆.热处理对TC4-DT钛合金组织性能的影响[J].材料开发与应用,2009,24(2):13-16.
【9】郭萍,赵永庆,曾卫东,等.两相区热处理对TC4-DT钛合金断裂韧性的影响[J].稀有金属材料与工程,2018,47(4):1221-1225.
【10】刘诚,董洪波,张贵华,等.热处理对TC4-DT钛合金拉伸变形后组织的影响[J].材料热处理学报,2015,36(2):21-26.
【11】张贵华,董洪波,朱深亮,等.三重热处理对热变形后TC4-DT合金微观组织的影响[J].材料热处理学报,2015,36(8):84-89.
【12】康少酺,李壮,于欢欢,等.水冷温度对TC4钛合金组织演变的影响[J].航空制造技术,2017(1):103-105.
【13】LI H M, LI M Q, LUO J, et al. Microstructure and mechanical properties of heat-treated Ti-5Al-2Sn-2Zr-4Mo-4Cr[J].Transactions of Nonferrous Metals Society of China,2015,25(9):2893-2900.
【14】孙朋朋,姚泽坤,郭鸿镇,等.等温锻造温度对TC6钛合金组织和性能的影响[J].热加工工艺,2011,40(3):30-32.
【15】邵鉴彪,张显程,王颖,等.双相钛合金拉伸时微观应力和应变的有限元模拟[J].机械工程材料,2016,40(2):102-106.
【16】韩栋,张鹏省,毛小南,等.两种典型热处理工艺对TC18钛合金组织性能的影响[J].钛工业进展,2009,26(6):23-26.
【17】王哲,王新南,祝力伟,等.TB17钛合金等温时效析出行为[J].航空材料学报,2016,36(5):1-6.
【2】VENKATESH B D, CHEN D L, BHOLE S D. Effect of heat treatment on mechanical properties of Ti-6Al-4V ELI alloy[J]. Materials Science & Engineering:A, 2009, 506(1/2):117-124.
【3】雷文光,韩栋,张永强,等.不同热处理工艺对TC4-DT钛合金棒材组织和性能的影响[J].材料导报, 2015, 29(7):120-123.
【4】朱知寿.航空结构用新型高性能钛合金材料技术研究与发展[J].航空科学技术, 2012(1):5-9.
【5】朱知寿,王庆如,郑永灵,等.损伤容限型钛合金新型β锻造工艺[J].中国有色金属学报,204,14(增刊3):13-16.
【6】张智,巨建辉,戚运莲,等.钛合金锻造工艺及其锻件的应用[J].热加工工艺,2010, 39(23):34-37.
【7】田伟,伏宇,钟燕,等.锻造工艺对TC17钛合金的显微组织和力学性能的影响[J].材料热处理学报,2016, 37(9):57-61.
【8】杨海瑛,陈军,赵永庆.热处理对TC4-DT钛合金组织性能的影响[J].材料开发与应用,2009,24(2):13-16.
【9】郭萍,赵永庆,曾卫东,等.两相区热处理对TC4-DT钛合金断裂韧性的影响[J].稀有金属材料与工程,2018,47(4):1221-1225.
【10】刘诚,董洪波,张贵华,等.热处理对TC4-DT钛合金拉伸变形后组织的影响[J].材料热处理学报,2015,36(2):21-26.
【11】张贵华,董洪波,朱深亮,等.三重热处理对热变形后TC4-DT合金微观组织的影响[J].材料热处理学报,2015,36(8):84-89.
【12】康少酺,李壮,于欢欢,等.水冷温度对TC4钛合金组织演变的影响[J].航空制造技术,2017(1):103-105.
【13】LI H M, LI M Q, LUO J, et al. Microstructure and mechanical properties of heat-treated Ti-5Al-2Sn-2Zr-4Mo-4Cr[J].Transactions of Nonferrous Metals Society of China,2015,25(9):2893-2900.
【14】孙朋朋,姚泽坤,郭鸿镇,等.等温锻造温度对TC6钛合金组织和性能的影响[J].热加工工艺,2011,40(3):30-32.
【15】邵鉴彪,张显程,王颖,等.双相钛合金拉伸时微观应力和应变的有限元模拟[J].机械工程材料,2016,40(2):102-106.
【16】韩栋,张鹏省,毛小南,等.两种典型热处理工艺对TC18钛合金组织性能的影响[J].钛工业进展,2009,26(6):23-26.
【17】王哲,王新南,祝力伟,等.TB17钛合金等温时效析出行为[J].航空材料学报,2016,36(5):1-6.
相关信息