Cause Analysis on Leakage of T91 Steel Supporting Tube of Primary Superheater in a Ultra Supercritical Boiler
摘 要
某电厂超超临界锅炉一级过热器T91钢吊挂管在运行1 400 h后发生泄漏。通过宏观检查、化学成分分析、力学性能试验、硬度测试和金相检验等方法对吊挂管泄漏原因进行了分析。结果表明:吊挂管发生短时过热,其耐压强度急剧下降,在内部介质压力作用下,管段发生胀粗和壁厚减薄,当壁厚不足以抵抗内压作用时管段发生爆裂,导致该吊挂管的泄漏。
Abstract
The T91 steel supporting tube of primary superheater of ultra supercritical boiler in a power plant leaked after operating for 1 400 h. By means of macroscopic examination, chemical composition analysis, mechanical property test, hardness test and metallographic examination, the causes of leakage of supporting tube were analyzed. The results show that the pressure strength of the supporting tube decreased sharply due to its short-time overheating. Under the internal medium pressure, the tube section expanded and the wall thickness decreased. When the wall thickness was not enough to resist the internal pressure, the tube section bursted, resulted in the leakage of the supporting tube.
中图分类号 TG142.1 DOI 10.11973/lhjy-wl202001015
所属栏目 质量控制与失效分析
基金项目 华能国际电力股份有限公司资助项目(NBKJ15-H03)
收稿日期 2019/1/16
修改稿日期
网络出版日期
作者单位点击查看
备注田晓(1985-),女,工程师,主要从事电站新型耐热钢性能研究、寿命评估及失效分析工作,tianxiao@tpri.com.cn
引用该论文: TIAN Xiao,QIN Chengpeng,XU Hui,SHANG Xuewei. Cause Analysis on Leakage of T91 Steel Supporting Tube of Primary Superheater in a Ultra Supercritical Boiler[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(1): 56~60
田晓,秦承鹏,徐慧,商雪威. 某超超临界锅炉一级过热器T91钢吊挂管泄漏原因分析[J]. 理化检验-物理分册, 2020, 56(1): 56~60
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵彦芬,张路,王正品,等. 高温过热器T91、T22管爆管分析[J]. 热力发电,2004,33(11):61-64.
【2】张作贵,万海波,王延峰. 长期服役再热器管T91钢的微观组织老化行为研究[J]. 动力工程学报,2019,36(6):499-503.
【3】柯浩,杜艾洁,张才稳,等. 某超临界锅炉高温过热器出口弯头爆管原因分析[J]. 发电与空调,2015,36(6):48-50.
【4】史志刚,侯安柱,李益民. T91钢长期运行过程中微观组织老化研究[J]. 热力发电,2006,35(4):54-58.
【5】刘爽,赵永宁,刘天佐,等. 超临界670 MW机组高温过热器爆管原因分析[J]. 热力发电,2010,39(9):103-105.
【6】赵彦芬,张璐,刘艳,等. 超超临界机组T92钢高温受热面管爆管原因分析[J].理化检验(物理分册),2012,48(3):180-184.
【7】蒙新明,张路,赖云亭,等. 某超临界机组锅炉过热器管爆管原因分析[J]. 理化检验(物理分册),2015,51(5):353-357.
【2】张作贵,万海波,王延峰. 长期服役再热器管T91钢的微观组织老化行为研究[J]. 动力工程学报,2019,36(6):499-503.
【3】柯浩,杜艾洁,张才稳,等. 某超临界锅炉高温过热器出口弯头爆管原因分析[J]. 发电与空调,2015,36(6):48-50.
【4】史志刚,侯安柱,李益民. T91钢长期运行过程中微观组织老化研究[J]. 热力发电,2006,35(4):54-58.
【5】刘爽,赵永宁,刘天佐,等. 超临界670 MW机组高温过热器爆管原因分析[J]. 热力发电,2010,39(9):103-105.
【6】赵彦芬,张璐,刘艳,等. 超超临界机组T92钢高温受热面管爆管原因分析[J].理化检验(物理分册),2012,48(3):180-184.
【7】蒙新明,张路,赖云亭,等. 某超临界机组锅炉过热器管爆管原因分析[J]. 理化检验(物理分册),2015,51(5):353-357.
相关信息