TA2钛接骨板断裂失效分析
Failure Analysis on Fracture of TA2 Titanium Bone Plate
摘 要
某患者体内植入的TA2钛接骨板发生断裂，采用宏观观察、化学成分分析、硬度测试、金相检验、扫描电镜分析等方法对接骨板断裂原因进行了分析。结果表明：TA2钛接骨板材料经冷变形处理后组织中存在较大的残余应力是接骨板发生断裂的重要原因，接骨板断裂形式为裂纹由接骨板外侧向内侧扩展的解理脆断。
接骨板
残余应力
解理脆断
TA2 titanium
bone plate
residual stress
cleavage brittle fracture
Abstract
The TA2 titanium bone plate implanted in a patient broke. The fracture causes of bone plate were analyzed by means of macroscopic observation, chemical composition analysis, hardness test, metallographic examination and scanning electron microscope analysis. The results show that the large residual stress in the structure of TA2 titanium plate after cold deformation was an important reason for the fracture of the bone plate, and the fracture form of the plate was cleavage brittle fracture with cracks extending from the outside to the inside of the bone plate.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202003017
所属栏目 质量控制与失效分析
基金项目
收稿日期 2019/3/27
修改稿日期
网络出版日期
作者单位点击查看
备注邱康勇(1987-),男,工程师,主要从事金属材料的理化检验及机械零件失效分析工作,295717869@qq.com
引用该论文: QIU Kangyong,HE Yan,WU Jiquan. Failure Analysis on Fracture of TA2 Titanium Bone Plate[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(3): 65～67
邱康勇,贺艳,吴继权. TA2钛接骨板断裂失效分析[J]. 理化检验－物理分册, 2020, 56(3): 65～67
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】关薇,翟伟,刘斌,等. 接骨板固有风险浅析[J]. 中国药物警戒,2013, 10(12):752-754.
【2】李荣,魏东,许陆,等. 外科植入用TA3钛合金接骨板断裂失效分析[J]. 理化检验(物理分册),2016,52(12):897-898.
【3】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京:国防工业出版社,2004.
【4】龚桂仙,吴立新,张友登. 不锈钢接骨板和骨钉断裂失效分析[J]. 武汉工程职业技术学院学报,2010,22(3):33-35.
【2】李荣,魏东,许陆,等. 外科植入用TA3钛合金接骨板断裂失效分析[J]. 理化检验(物理分册),2016,52(12):897-898.
【3】张栋,钟培道,陶春虎,等. 失效分析[M]. 北京:国防工业出版社,2004.
【4】龚桂仙,吴立新,张友登. 不锈钢接骨板和骨钉断裂失效分析[J]. 武汉工程职业技术学院学报,2010,22(3):33-35.
相关信息