活塞杆用纳米WC-10Co4Cr涂层的微观结构及性能
Microstructure and Performance of Nano-WC-10Co4Cr Coating for Piston Rod
摘 要
采用大功率超声速喷涂火焰（HVOF）技术在活塞杆表面制备了纳米WC-10Co4Cr陶瓷涂层。通过扫描电镜（SEM）、金相分析仪、结合力试验机、显微硬度计、电化学工作站等手段分析研究了纳米WC-10Co4Cr陶瓷活塞杆的表面性能。结果表明：纳米WC-10Co4Cr陶瓷涂层具有远高于活塞杆基材的硬度及耐蚀性，在500 g载荷下与氮化硅球对磨180 min，涂层的磨损量少于基材的1/150，并且涂层与基材之间的结合强度超过80 MPa。制备的纳米WC-10Co4Cr陶瓷涂层完全满足活塞杆的实际使用需求，并且可以大幅提高其使用寿命。
启闭机活塞杆
超声速火焰喷涂
耐磨损
耐腐蚀
nano-WC-10Co4Cr ceramic coating
hoist piston rod
high veloaty oxygen fuel (HVOF)
wear resistance
corrosion resistance
Abstract
Nano-WC-10Co4Cr ceramic coatings were prepared on the surface of piston rod by high-power high veloaty oxygen fuel (HVOF) thermal spraying technology. The surface properties of nano-WC-10Co4Cr ceramic piston rod were studied and analyzed by means of scanning electron microscope (SEM), metallographic analyzer, binding force tester, micro-hardness tester, and electrochemical workstation. The results showed that the nano-WC-10Co4Cr ceramic coating had much higher hardness and corrosion resistance than those of the piston rod substrate. After abrasion with silicon nitride balls at 500 g load for 180 min, the wear of the coating was less than 1/150 of the substrate, and the bonding strength between the coating and the substrate exceeded 80 MPa. The prepared nano-WC-10Co4Cr ceramic coatings completely meet the actual use requirements of the piston rod, and could greatly improve its service life.
中图分类号 TG147.442 DOI 10.11973/fsyfh-202005001
所属栏目 试验研究
基金项目 国家“948计划”项目（201218）；浙江省科技计划（2017C37048）；浙江省科技计划（2016C37091）；杭州市科技发展计划（20162231E10）；杭州市社会发展科研攻关项目（161323Z006）
收稿日期 2018/6/19
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHAO Jian,CHEN Xiaoming,FU Li,LIU Wei,MAO Pengzhan,ZHANG Lei. Microstructure and Performance of Nano-WC-10Co4Cr Coating for Piston Rod[J]. Corrosion & Protection, 2020, 41(5): 1
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱丽红. 几种表面强化方法在2Cr13活塞杆上的应用比较[J]. 创新沈阳文集,2009(A):16-22.
【2】李玉臣. 液压启闭机在水利工程中的应用及运行维护管理[J]. 北京水务,2010(3):49-51.
【3】孙万昌,张磊,张晗,等. 金属表面复合层研究进展[J]. 热加工工艺,2011,40(16):75-77.
【4】陈光,李霄琳,李跃年. 国产陶瓷活塞杆液压缸在白沙滩泵站输水总干渠扩建工程的应用[J]. 水利水电技术,2008,39(7):58-60.
【5】蔡剑锋,沈翔,谭大基. 陶瓷活塞杆液压启闭机在多布水电站的应用[J]. 西北水电,2017(2):71-73.
【6】何晓,刘昌耀,张士永. 陶瓷涂层活塞杆在往复式压缩机中的应用研究[J]. 机械设计与制造,2012(9):235-237.
【7】刘晓燕,王爱兵,贾丽娜. 工程车活塞杆用45#钢电沉积Ni-WC纳米复合镀层的研究[J]. 电镀与环保,2017,37(6):5-7.
【8】查柏林,王汉功,徐可为. 液压活塞杆耐磨陶瓷涂层研究[J]. 机床与液压,2006,34(1):86-88.
【9】QIAO Y F,FISCHER T E,DENT A. The effects of fuel chemistry and feedstock powder structure on the mechanical and tribological properties of HVOF thermal-sprayed WC-Co coatings with very fine structures[J]. Surface and Coatings Technology,2003,172(1):24-41.
【10】刘娟,余江成,潘罗平,等. HVAF喷涂WC-12Co涂层的空蚀、磨损及磨蚀性能研究[J]. 水力发电学报,2012,31(3):230-233.
【11】MUTASIM L,BANKAR V,RIM L C. High velocity oxy-fuel thermal sprayed coatings as alternatives to WC-12Co coatings and chromium plating[M].[S.l.]:Materials Park,1997:901-908.
【12】吴燕明,赵坚,陈小明,等. 超声速喷涂纳米WC复合涂层与电镀铬层的组织及性能[J]. 材料热处理学报,2015,36(S1):171-176.
【13】梁存光,李新梅. 曲面响应法在等离子喷涂WC-12Co涂层工艺优化中的应用[J]. 材料科学与工艺,2018,26(2):90-96.
【2】李玉臣. 液压启闭机在水利工程中的应用及运行维护管理[J]. 北京水务,2010(3):49-51.
【3】孙万昌,张磊,张晗,等. 金属表面复合层研究进展[J]. 热加工工艺,2011,40(16):75-77.
【4】陈光,李霄琳,李跃年. 国产陶瓷活塞杆液压缸在白沙滩泵站输水总干渠扩建工程的应用[J]. 水利水电技术,2008,39(7):58-60.
【5】蔡剑锋,沈翔,谭大基. 陶瓷活塞杆液压启闭机在多布水电站的应用[J]. 西北水电,2017(2):71-73.
【6】何晓,刘昌耀,张士永. 陶瓷涂层活塞杆在往复式压缩机中的应用研究[J]. 机械设计与制造,2012(9):235-237.
【7】刘晓燕,王爱兵,贾丽娜. 工程车活塞杆用45#钢电沉积Ni-WC纳米复合镀层的研究[J]. 电镀与环保,2017,37(6):5-7.
【8】查柏林,王汉功,徐可为. 液压活塞杆耐磨陶瓷涂层研究[J]. 机床与液压,2006,34(1):86-88.
【9】QIAO Y F,FISCHER T E,DENT A. The effects of fuel chemistry and feedstock powder structure on the mechanical and tribological properties of HVOF thermal-sprayed WC-Co coatings with very fine structures[J]. Surface and Coatings Technology,2003,172(1):24-41.
【10】刘娟,余江成,潘罗平,等. HVAF喷涂WC-12Co涂层的空蚀、磨损及磨蚀性能研究[J]. 水力发电学报,2012,31(3):230-233.
【11】MUTASIM L,BANKAR V,RIM L C. High velocity oxy-fuel thermal sprayed coatings as alternatives to WC-12Co coatings and chromium plating[M].[S.l.]:Materials Park,1997:901-908.
【12】吴燕明,赵坚,陈小明,等. 超声速喷涂纳米WC复合涂层与电镀铬层的组织及性能[J]. 材料热处理学报,2015,36(S1):171-176.
【13】梁存光,李新梅. 曲面响应法在等离子喷涂WC-12Co涂层工艺优化中的应用[J]. 材料科学与工艺,2018,26(2):90-96.
相关信息