不锈钢焊缝的涡流正交探头检测试验
Detecting test of orthogonal eddy current probe for stainless steel welds
摘 要
涡流检测方法可以在不去除涂层或者防腐层的情况下对焊缝实施检测，然而关于特种设备焊缝的涡流检测技术的应用较少。以304不锈钢焊缝为研究对象，通过自制正交焊缝检测探头开展检测试验，并对其特性进行研究，以供同行交流。
探头
涡流检测
不锈钢
weld
probe
eddy current testing
stainless steel
Abstract
For the common workpiece morphology of welds,eddy current test method can be carried out without removing the coating or the corrosion-resistant layer. However, the technical application of the weld eddy current test is less, especially in the detection of special equipment. The paper takes 304 stainless steel welds as an object and conducts experiments by using self-made orthogonal detection probes for weld to study its characteristics for peer communication.
中图分类号 TG115.28 DOI 10.11973/wsjc202005014
所属栏目 试验研究
基金项目 广东省质量技术监督局科技项目（2018CT22）
收稿日期 2019/11/6
修改稿日期
网络出版日期
作者单位点击查看
备注马冰洋(1989-),硕士,主要从事特种设备检验与无损检测技术应用研究工作
引用该论文: MA Bingyang,HUANG Guilin,YANG Zerong. Detecting test of orthogonal eddy current probe for stainless steel welds[J]. Nondestructive Testing, 2020, 42(5): 63～66
马冰洋,黄桂林,杨泽榕. 不锈钢焊缝的涡流正交探头检测试验[J]. 无损检测, 2020, 42(5): 63～66
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】任吉林. 电磁检测[M].北京:国防工业出版社,2001.
【2】吕香慧, 张宇,楼淼,等.带涂层焊缝的电磁涡流检测[J].无损检测,2010,32(6):441-443.
【3】汤祺, 冯搏,杨芸,等.表面粗糙度对涡流检测的影响[J].无损检测,2016,38(3):47-51.
【4】林俊明, 张开良,林发炳,等.焊缝表面裂纹涡流检测技术[J].中国特种设备安全,2004, 20(6):33-36.
【2】吕香慧, 张宇,楼淼,等.带涂层焊缝的电磁涡流检测[J].无损检测,2010,32(6):441-443.
【3】汤祺, 冯搏,杨芸,等.表面粗糙度对涡流检测的影响[J].无损检测,2016,38(3):47-51.
【4】林俊明, 张开良,林发炳,等.焊缝表面裂纹涡流检测技术[J].中国特种设备安全,2004, 20(6):33-36.
相关信息