Forging Cracking Cause of 4Cr5MoSiV1 Steel Module
摘 要
某公司一批4Cr5MoSiV1钢模块在进行锻造加工时发生开裂。通过化学成分分析、金相检验、硬度测试和能谱分析等方法对模块锻造开裂的原因进行了分析。结果表明:4Cr5MoSiV1钢模块显微组织中存在的偏析以及沿晶分布的网络状低熔点富铜相是造成锻造开裂的直接原因。
Abstract
A batch of 4Cr5MoSiV1 steel modules in a company cracked during forging. The causes of forging cracking were analyzed by chemical composition anslysis, metallographic examination, hardness test, energy spectrum analysis and so on. The results show that the proximate causes of forging cracking were segregation and network like low melting point copper rich phase distributed along the crystal in microstructure of 4Cr5MoSiV1 steel module.
中图分类号 TG142.45 DOI 10.11973/lhjy-wl202007015
所属栏目 质量控制与失效分析
基金项目
收稿日期 2019/8/20
修改稿日期
网络出版日期
作者单位点击查看
备注张全新(1976-),男,高级工程师,主要从事金属材料研发及分析工作,35803684@qq.com
引用该论文: ZHANG Quanxin,JIANG Haijun,WANG Chunyi. Forging Cracking Cause of 4Cr5MoSiV1 Steel Module[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2020, 56(7): 66~68
张全新,江海军,王春奕. 4Cr5MoSiV1钢模块锻造开裂原因[J]. 理化检验-物理分册, 2020, 56(7): 66~68
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】姜祖赓.模具钢[M].北京:冶金工业出版社,1988.
【2】陈再枝,蓝德年.模具钢手册[M].北京:冶金工业出版社,2002.
【3】程里.模锻钢件锻造生产中的铜脆龟裂分析及预防[J].热加工工艺,2006,35(2):58.
【4】江学强,吉卫.铜脆产生原因及防止措施[J].四川兵工学报,2006(5):48-50.
【5】曾辉藩,彭澎,廖丕博,等.压铸模具钢4Cr5MoSiV1的热处理工艺及组织[J].模具制造,2005(12):68-70.
【2】陈再枝,蓝德年.模具钢手册[M].北京:冶金工业出版社,2002.
【3】程里.模锻钢件锻造生产中的铜脆龟裂分析及预防[J].热加工工艺,2006,35(2):58.
【4】江学强,吉卫.铜脆产生原因及防止措施[J].四川兵工学报,2006(5):48-50.
【5】曾辉藩,彭澎,廖丕博,等.压铸模具钢4Cr5MoSiV1的热处理工艺及组织[J].模具制造,2005(12):68-70.
相关信息