Effect of AlN Content on Microstructure and Properties ofTi(C,N)-Based Cermet
摘 要
研究了AlN添加量(0,1%,2%,3%,质量分数)对Ti(C,N)基金属陶瓷硬度、抗弯强度以及抗氧化性能的影响。结果表明:不同AlN添加量下的金属陶瓷主要由Ti(C,N)、Ni3Al和镍相组成;随着AlN添加量增加,金属陶瓷的硬度增大,抗弯强度先增大后减小,AlN添加量为2%时达到峰值;与未添加AlN相比,添加2%AlN金属陶瓷的氧化质量增加较慢,氧化膜结构更致密,抗氧化性能更好。
Abstract
The effect of AlN addition amount (0,1%,2%,3%, mass fraction) on the hardness, bending strength and oxidation resistance of Ti(C,N)-based cermets was studied. The results show that the cermets with different addition amount of AlN were all mainly composed of Ti(C,N), Ni3Al and nickel phases. With increasing the addition amount of AlN, the hardness of the cermet increased, and the bending strength increased first and then decreased, reaching the peak value with 2%AlN. The oxidation mass gain of the cermet with 2%AlN increased slowly compared with the without AlN, and the oxide film structure was relatively dense, indicating the better oxidation resistance.
中图分类号 TG711 DOI 10.11973/jxgccl202103002
所属栏目 试验研究
基金项目
收稿日期 2019/12/5
修改稿日期 2020/11/9
网络出版日期
作者单位点击查看
备注王超锋(1994-),男,河南郑州人,硕士研究生
引用该论文: WANG Chaofeng,CHEN Yikun,LIU Huachen,DU Xueming,YAO Zhenhua. Effect of AlN Content on Microstructure and Properties ofTi(C,N)-Based Cermet[J]. Materials for mechancial engineering, 2021, 45(3): 6~10
王超锋,陈义坤,刘华臣,杜学铭,姚振华. AlN含量对Ti(C,N)基金属陶瓷组织和性能的影响[J]. 机械工程材料, 2021, 45(3): 6~10
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈玮,邹莉.高速切削中的刀具材料[J]. 现代制造工程,2006(12):138-141. CHEN W, ZOU L. Cutting tool materials in high speed machining[J]. Modern Manufacturing Engineering,2006(12):138-141.
【2】LIU N, XU Y D, LI Z H, et al. Effects of addition of TiN nanoparticles on microstructure and mechanical properties of TiC based cermets[J]. Meterials Science & Technology, 2002, 18(5):586-590.
【3】鲍贤勇,曾美琴,鲁忠臣,等.烧结温度对Ti(C,N)基金属陶瓷组织及力学性能的影响[J].材料热处理学报,2017,38(5):61-66. BAO X Y, ZENG M Q, LU Z C,et al. Influence of sintering temperature on microstructure and mechanical properties of Ti(C, N)-based cermets[J].Transactions of Materials and Heat Treatment,2017,38(5):61-66.
【4】YI C H,FAN H Y,XIONG J,et al.Effect of WC content on the microstructures and corrosion behavior of Ti(C,N)-based cermets[J].Ceramics International, 2013,39(1):503-509.
【5】朱刚,谢明,陈家林,等.黏结相组成对Ti(C,N)基金属陶瓷高温氧化行为的影响[J].机械工程材料,2016,40(11):75-80. ZHU G, XIE M, CHEN J L, et al. Effects of binder components on high-temperature oxidation behavior of Ti(C,N)-based cermets[J].Materials for Mechanical Engineering, 2016,40(11):75-80.
【6】CHICARDI E,CÓRDOBA J M,GOTOR F J.High temperature oxidation resistance of (Ti,Ta)(C,N)-based cermets[J].Corrosion Science,2016,102:125-136.
【7】LIU N,CHAO S,HUANG X M.Effects of TiC/TiN addition on the microstructure and mechanical properties of ultra-fine grade Ti (C,N)-Ni cermets[J].Journal of the European Ceramic Society, 2006,26(16):3861-3870.
【8】LIU A J,LIU N.Effect of WC-Co granules on mechanical properties and microstructure of Ti(C,N)-based cermets[J].Ceramics International, 2016,42(14):15274-15284.
【9】WU P,ZHENG Y,ZHAO Y L,et al.Effect of TaC addition on the microstructures and mechanical properties of Ti(C,N)-based cermets[J].Materials & Design, 2010,31(7):3537-3541.
【10】KIM S,ZUO J M,KANG S.Effect of WC or NbC addition on lattice parameter of surrounding structure in Ti(C0.7N0.3)-Ni cermets investigated by TEM/CBED[J].Journal of the European Ceramic Society,2010,30(10):2131-2138.
【11】LIU C,LIN N,HE Y H.Influence of Mo2C and TaC additions on the microstructure and mechanical properties of Ti(C,N)-based cermets[J].Ceramics International,2016,42(2):3569-3574.
【12】赵永乐,赵能伟,刘林艳,等.Cr3C2对Ti(C,N)基金属陶瓷性能的影响[J].硬质合金,2008,25(1):1-5. ZHAO Y L, ZHAO N W, LIU L Y, et al. Effect of Cr3C2 on the properties of Ti(C,N)-based cermets[J].Cemented Carbide,2008,25(1):1-5.
【13】WANG J,LIU Y,FENG Y,et al.Effect of NbC on the microstructure and sinterability of Ti(C0.7,N0.3)-based cermets[J].International Journal of Refractory Metals and Hard Materials,2009,27(3):549-551.
【14】刘宁,崔昆,胡镇华.添加AlN对Ti(C,N)基金属陶瓷力学性能和显微组织的影响[J].理化检验(物理分册),1997,33(1):15-17. LIU N, CUI K, HU Z H. Effect of addition of AIN on the mechanical properties and microstructure of Ti(C,N) based cermets[J].Physical Testing and Chemical Analysis(Part A:Physical Testing),1997,33(1):15-17.
【15】ZHAN B,LIU N,JIN Z B,et al.Effect of VC/Cr3C2 on microstructure and mechanical properties of Ti(C,N)-based cermets[J].Transactions of Nonferrous Metals Society of China,2012,22(5):1096-1105.
【2】LIU N, XU Y D, LI Z H, et al. Effects of addition of TiN nanoparticles on microstructure and mechanical properties of TiC based cermets[J]. Meterials Science & Technology, 2002, 18(5):586-590.
【3】鲍贤勇,曾美琴,鲁忠臣,等.烧结温度对Ti(C,N)基金属陶瓷组织及力学性能的影响[J].材料热处理学报,2017,38(5):61-66. BAO X Y, ZENG M Q, LU Z C,et al. Influence of sintering temperature on microstructure and mechanical properties of Ti(C, N)-based cermets[J].Transactions of Materials and Heat Treatment,2017,38(5):61-66.
【4】YI C H,FAN H Y,XIONG J,et al.Effect of WC content on the microstructures and corrosion behavior of Ti(C,N)-based cermets[J].Ceramics International, 2013,39(1):503-509.
【5】朱刚,谢明,陈家林,等.黏结相组成对Ti(C,N)基金属陶瓷高温氧化行为的影响[J].机械工程材料,2016,40(11):75-80. ZHU G, XIE M, CHEN J L, et al. Effects of binder components on high-temperature oxidation behavior of Ti(C,N)-based cermets[J].Materials for Mechanical Engineering, 2016,40(11):75-80.
【6】CHICARDI E,CÓRDOBA J M,GOTOR F J.High temperature oxidation resistance of (Ti,Ta)(C,N)-based cermets[J].Corrosion Science,2016,102:125-136.
【7】LIU N,CHAO S,HUANG X M.Effects of TiC/TiN addition on the microstructure and mechanical properties of ultra-fine grade Ti (C,N)-Ni cermets[J].Journal of the European Ceramic Society, 2006,26(16):3861-3870.
【8】LIU A J,LIU N.Effect of WC-Co granules on mechanical properties and microstructure of Ti(C,N)-based cermets[J].Ceramics International, 2016,42(14):15274-15284.
【9】WU P,ZHENG Y,ZHAO Y L,et al.Effect of TaC addition on the microstructures and mechanical properties of Ti(C,N)-based cermets[J].Materials & Design, 2010,31(7):3537-3541.
【10】KIM S,ZUO J M,KANG S.Effect of WC or NbC addition on lattice parameter of surrounding structure in Ti(C0.7N0.3)-Ni cermets investigated by TEM/CBED[J].Journal of the European Ceramic Society,2010,30(10):2131-2138.
【11】LIU C,LIN N,HE Y H.Influence of Mo2C and TaC additions on the microstructure and mechanical properties of Ti(C,N)-based cermets[J].Ceramics International,2016,42(2):3569-3574.
【12】赵永乐,赵能伟,刘林艳,等.Cr3C2对Ti(C,N)基金属陶瓷性能的影响[J].硬质合金,2008,25(1):1-5. ZHAO Y L, ZHAO N W, LIU L Y, et al. Effect of Cr3C2 on the properties of Ti(C,N)-based cermets[J].Cemented Carbide,2008,25(1):1-5.
【13】WANG J,LIU Y,FENG Y,et al.Effect of NbC on the microstructure and sinterability of Ti(C0.7,N0.3)-based cermets[J].International Journal of Refractory Metals and Hard Materials,2009,27(3):549-551.
【14】刘宁,崔昆,胡镇华.添加AlN对Ti(C,N)基金属陶瓷力学性能和显微组织的影响[J].理化检验(物理分册),1997,33(1):15-17. LIU N, CUI K, HU Z H. Effect of addition of AIN on the mechanical properties and microstructure of Ti(C,N) based cermets[J].Physical Testing and Chemical Analysis(Part A:Physical Testing),1997,33(1):15-17.
【15】ZHAN B,LIU N,JIN Z B,et al.Effect of VC/Cr3C2 on microstructure and mechanical properties of Ti(C,N)-based cermets[J].Transactions of Nonferrous Metals Society of China,2012,22(5):1096-1105.
相关信息