Study on Residual Strength of High-grade X100 Gas Pipeline with Double Point Corrosion Defects
摘 要
国内外学者目前的研究主要针对管道的单点腐蚀缺陷,鲜少有关于双点腐蚀的,尤其是缺少对高钢级管道双点腐蚀缺陷的研究。以X100高钢级单蚀、双蚀管道为研究对象,采用ABAQUS软件建立有限元模型,研究了腐蚀深度、腐蚀宽度、腐蚀长度、双点蚀间距等不同腐蚀缺陷几何参数对轴向双点腐蚀失效压力的影响情况。结果表明:相对于其他参数,轴向双点蚀深度对失效压力的影响最大,同时,随着轴向双点蚀缺陷深度、缺陷长度的增大,失效压力减小,并且减少的速率呈现递减趋势。
Abstract
The current researches of domestic and foreign scholars mainly focus on single-point corrosion defects of pipelines. There are few studies on double-point corrosion, especially the lack of research on double-point corrosion defects of high-grade steel pipelines. Taking X100 high-steel-grade single-corrosion and double-corrosion pipelines as the research object, ABAQUS software was used to establish a finite element model to study the influence of different corrosion defect geometric parameters such as corrosion depth, corrosion width, corrosion length, and double pitting spacing on the failure pressure at axial double pitting corrosion condition. The results show that compared with other parameters, axial double pitting depth had the greatest influence on the failure pressure. At the same time, as the depth and length of the axial double pitting defect increased, the failure pressure decreased, and the rate of decrease showed a decreasing trend.
中图分类号 TB115 DOI 10.11973/fsyfh-202104009
所属栏目 试验研究
基金项目 中国石油科技创新基金项目(2017D-5007-0606)
收稿日期 2020/6/28
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: YANG Yanhua,GU Xiaoting,ZHANG Xu,CAO Ping,ZANG Xuerui,LI Hao. Study on Residual Strength of High-grade X100 Gas Pipeline with Double Point Corrosion Defects[J]. Corrosion & Protection, 2021, 42(4): 48
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】臧雪瑞,顾晓婷,王秋妍,等. 含腐蚀缺陷高钢级输气管道的失效压力模型[J]. 油气储运,2019,38(3):285-290,296.
【2】马彬,帅健,刘德绪,等. 基于有限元法对爆破试验预测埋地管道极限载荷的准确性分析[J]. 天然气工业,2013,33(6):108-112.
【3】曹学文,赵联祁,崔铭伟,等. 相互影响双腐蚀缺陷管道的剩余强度[J]. 油气储运,2015,34(4):354-361.
【4】王战辉,马向荣,高勇,等. 双点腐蚀缺陷油气管道剩余强度[J]. 化工科技,2019,27(1):9-13.
【5】洪来凤,孙铁,赵志海. 基于ANSYS的双点腐蚀缺陷管道剩余强度评价[J]. 油气储运,2010,29(12):916-917,924.
【6】马树锋,吴洋. 双点腐蚀缺陷对管道剩余寿命的影响[J]. 管道技术与设备,2015(1):46-48.
【7】李琪. 基于破裂极限状态的X80腐蚀管道可靠性分析[D]. 成都:西南石油大学,2016.
【8】崔铖. 含内腐蚀缺陷高强钢输气管道剩余强度的评估方法研究[D]. 北京:北京交通大学,2015.
【9】帅健,张春娥,陈福来. 非线性有限元法用于腐蚀管道失效压力预测[J]. 石油学报,2008,29(6):933-937.
【10】罗金恒,赵新伟,张华,等. 腐蚀管道剩余寿命预测方法[J]. 管道技术与设备,2006(5):37-39.
【11】MA B,SHUAI J,LIU D X,et al. Assessment on failure pressure of high strength pipeline with corrosion defects[J]. Engineering Failure Analysis,2013,32:209-219.
【12】臧雪瑞,顾晓婷,王秋妍. 含腐蚀缺陷X100输气管道的剩余强度研究[J]. 材料保护,2019,52(9):125-131.
【13】LIU J,MORTIMER L,WOOD A. Project #153H Corrosion Assessment Guidance for High Strength Steels (Phase 2)[R]. [S.l.]:[s.n.],2009.
【14】CHAUHAN V,BRISTER J,DAFEA M. A review of methods for assessing the remaining strength of corroded pipelines[R]. [S.l.]:[s.n.],2009.
【15】帅健,张春娥,陈福来. 线性有限元法用于腐蚀管道失效压力预测[J]. 石油学报,2008,29(6):933-937.
【16】张斌,钱成文,王玉梅,等. 国内外高钢级管线钢的发展及应用[J]. 石油工程建设,2008(1):13-16,7,76.
【17】王国丽, 管伟, 韩景宽,等. X100、X90管线钢管在高压输气管道中应用的方案研究[J]. 石油规划设计,2015(2):5-10,54.9
【2】马彬,帅健,刘德绪,等. 基于有限元法对爆破试验预测埋地管道极限载荷的准确性分析[J]. 天然气工业,2013,33(6):108-112.
【3】曹学文,赵联祁,崔铭伟,等. 相互影响双腐蚀缺陷管道的剩余强度[J]. 油气储运,2015,34(4):354-361.
【4】王战辉,马向荣,高勇,等. 双点腐蚀缺陷油气管道剩余强度[J]. 化工科技,2019,27(1):9-13.
【5】洪来凤,孙铁,赵志海. 基于ANSYS的双点腐蚀缺陷管道剩余强度评价[J]. 油气储运,2010,29(12):916-917,924.
【6】马树锋,吴洋. 双点腐蚀缺陷对管道剩余寿命的影响[J]. 管道技术与设备,2015(1):46-48.
【7】李琪. 基于破裂极限状态的X80腐蚀管道可靠性分析[D]. 成都:西南石油大学,2016.
【8】崔铖. 含内腐蚀缺陷高强钢输气管道剩余强度的评估方法研究[D]. 北京:北京交通大学,2015.
【9】帅健,张春娥,陈福来. 非线性有限元法用于腐蚀管道失效压力预测[J]. 石油学报,2008,29(6):933-937.
【10】罗金恒,赵新伟,张华,等. 腐蚀管道剩余寿命预测方法[J]. 管道技术与设备,2006(5):37-39.
【11】MA B,SHUAI J,LIU D X,et al. Assessment on failure pressure of high strength pipeline with corrosion defects[J]. Engineering Failure Analysis,2013,32:209-219.
【12】臧雪瑞,顾晓婷,王秋妍. 含腐蚀缺陷X100输气管道的剩余强度研究[J]. 材料保护,2019,52(9):125-131.
【13】LIU J,MORTIMER L,WOOD A. Project #153H Corrosion Assessment Guidance for High Strength Steels (Phase 2)[R]. [S.l.]:[s.n.],2009.
【14】CHAUHAN V,BRISTER J,DAFEA M. A review of methods for assessing the remaining strength of corroded pipelines[R]. [S.l.]:[s.n.],2009.
【15】帅健,张春娥,陈福来. 线性有限元法用于腐蚀管道失效压力预测[J]. 石油学报,2008,29(6):933-937.
【16】张斌,钱成文,王玉梅,等. 国内外高钢级管线钢的发展及应用[J]. 石油工程建设,2008(1):13-16,7,76.
【17】王国丽, 管伟, 韩景宽,等. X100、X90管线钢管在高压输气管道中应用的方案研究[J]. 石油规划设计,2015(2):5-10,54.9
相关信息