摘 要
海洋工程用钢服役时一直受到环境腐蚀和疲劳载荷的耦合作用，而传统的腐蚀、疲劳单项评估已不能满足检测需求，因此开发了一套腐蚀疲劳试验系统来测试材料在腐蚀环境下的疲劳寿命，并使用该系统对海洋工程用S690QL高强钢板在腐蚀环境下的疲劳寿命进行了测试。结果表明：该系统可以对试验温度、流速、腐蚀介质pH值等参数精准控制，并可以实现材料在腐蚀与疲劳耦合作用下的性能评估。在相同的循环应力下，材料受到模拟海水腐蚀和疲劳载荷耦合作用的疲劳寿命大大低于在空气中室温下的疲劳寿命。
耦合作用
环境腐蚀
疲劳载荷
疲劳寿命
corrosion fatigue test system
coupling effect
environmental corrosion
fatigue load
fatigue life
Abstract
Marine engineering steel has been subjected to the coupling effect of environmental corrosion and fatigue load, but the traditional single assessment of corrosion and fatigue can not meet the test demand. Therefore, a set of corrosion fatigue test system was developed to test the fatigue life of materials in corrosion environment, and the fatigue life of S690QL high strength steel plate used in marine engineering was tested in corrosion environment with the system. The results show that the system can accurately control the test temperature, flow rate, pH value of corrosive medium and other parameters, and can realize the performance evaluation of materials under the coupling effect of corrosion and fatigue. Under the same cyclic stress, the fatigue life of the material under the coupling effect of simulated seawater corrosion and fatigue load was much lower than that in air at room temperatre.
中图分类号 TG115 DOI 10.11973/lhjy-wl202104010
所属栏目 试验设备及应用
基金项目
收稿日期 2020/6/15
修改稿日期
网络出版日期
作者单位点击查看
备注邢承亮(1987-),男,工程师,主要从事金属材料研发及力学性能研究工作,834119960@qq.com
引用该论文: XING Chengliang,SUN Xiaoran,AN Zhiguo,ZHAO Zhongyu,SONG Yue,SUN Jianghuan,BAI Lijuan. Development and Application of Corrosion Fatigue Test System[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2021, 57(4): 39～42
邢承亮,孙晓冉,安治国,赵中昱,宋月,孙江欢,白丽娟. 腐蚀疲劳试验系统的开发及应用[J]. 理化检验－物理分册, 2021, 57(4): 39～42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】谭晓明,陈跃良,段成美.飞机结构搭接件腐蚀三维裂纹扩展特性分析[J].航空学报,2005,26(1):66-69.
【2】夏耘,王勇刚.铝合金腐蚀疲劳研究进展[J].轻合金加工技术,2018,46(10):15-19.
【3】张丹峰,谭晓明,陈跃良.海洋环境下飞机结构腐蚀疲劳研究现状[J].装备环境工程,2009,6(2):5-8.
【4】贺小帆,刘文璟,向锦武.C-T曲线通用性分析和试验研究[J].航空学报,2005(2):184-189.
【5】郭洪全,杨永安,吴有金.LC4CS高强铝合金腐蚀疲劳行为研究[J].材料工程,1995(4):42-44.
【6】马少华,回丽,周松,等.腐蚀环境对预腐蚀铝合金腐蚀疲劳性能的影响[J].材料工程,2015,43(2):91-95.
【7】丁传富,陈美英,吴有金,等.飞机典型机械紧固连接件腐蚀疲劳性能的试验研究[J].材料工程,1995(8):41-44.
【8】卢松涛,刘立东,杨浩亮,等.盐雾环境下部段对接紧固件耐腐蚀性研究[J].宇航总体技术,2018,2(4):59-64.
【9】陆峰,汤智慧,孙志华,等.航空材料环境试验及表面防护技术[M].北京:国防工业出版社,2012.
【10】陈跃良,卞贵学,衣林,等.腐蚀和疲劳交替作用下飞机铝合金疲劳性能及断裂机理研究[J].机械工程学报,2012,48(20):73-79.
【11】TAN X M, CHEN Y L, JIN P. Corrosion fatigue life prediction of aircraft structure based on fuzzy reliability approach[J]. Chinese Journal of Aeronautics,2005,18(4):346-351.
【12】梁永梅.加载波形对D36钢腐蚀疲劳裂纹扩展的影响[D].大连:大连理工大学,2015.
【13】闫小顺,黄小平,周心桃.船舶含裂纹焊接结构剩余疲劳寿命可靠性预报[J].舰船科学技术,2016,38(3):27-31.
【14】傅惠民,邢军伟,王治华.平均数据ε-N曲线和P-ε-N曲线小子样推断方法[J].机械强度,2010,32(6):125-128.
【15】陈晓峰,党万腾,唐维,等.航空AZ31镁合金腐蚀疲劳性能研究[J].热加工工艺,2017,46(22):92-94.
【16】师小红,徐章遂,康健.基于断裂力学的疲劳裂纹扩展速率公式研究[J].机械设计与制造,2007(10):11-12.
【17】ILMAN M N, ISWANTO P T. Fatigue crack growth rate behaviour of friction-stir aluminium alloy AA2024-T3 welds under transient thermal tensioning[J]. Materials&Design,2013,50(17):235-243.
【18】HONG S, LEE S. Dynamic strain aging under tensile and LCF loading conditions, and their comparison in cold worked 316Lstainless steel[J]. Journal of Nuclear Materials,2004,328(2/3):232-242.
【2】夏耘,王勇刚.铝合金腐蚀疲劳研究进展[J].轻合金加工技术,2018,46(10):15-19.
【3】张丹峰,谭晓明,陈跃良.海洋环境下飞机结构腐蚀疲劳研究现状[J].装备环境工程,2009,6(2):5-8.
【4】贺小帆,刘文璟,向锦武.C-T曲线通用性分析和试验研究[J].航空学报,2005(2):184-189.
【5】郭洪全,杨永安,吴有金.LC4CS高强铝合金腐蚀疲劳行为研究[J].材料工程,1995(4):42-44.
【6】马少华,回丽,周松,等.腐蚀环境对预腐蚀铝合金腐蚀疲劳性能的影响[J].材料工程,2015,43(2):91-95.
【7】丁传富,陈美英,吴有金,等.飞机典型机械紧固连接件腐蚀疲劳性能的试验研究[J].材料工程,1995(8):41-44.
【8】卢松涛,刘立东,杨浩亮,等.盐雾环境下部段对接紧固件耐腐蚀性研究[J].宇航总体技术,2018,2(4):59-64.
【9】陆峰,汤智慧,孙志华,等.航空材料环境试验及表面防护技术[M].北京:国防工业出版社,2012.
【10】陈跃良,卞贵学,衣林,等.腐蚀和疲劳交替作用下飞机铝合金疲劳性能及断裂机理研究[J].机械工程学报,2012,48(20):73-79.
【11】TAN X M, CHEN Y L, JIN P. Corrosion fatigue life prediction of aircraft structure based on fuzzy reliability approach[J]. Chinese Journal of Aeronautics,2005,18(4):346-351.
【12】梁永梅.加载波形对D36钢腐蚀疲劳裂纹扩展的影响[D].大连:大连理工大学,2015.
【13】闫小顺,黄小平,周心桃.船舶含裂纹焊接结构剩余疲劳寿命可靠性预报[J].舰船科学技术,2016,38(3):27-31.
【14】傅惠民,邢军伟,王治华.平均数据ε-N曲线和P-ε-N曲线小子样推断方法[J].机械强度,2010,32(6):125-128.
【15】陈晓峰,党万腾,唐维,等.航空AZ31镁合金腐蚀疲劳性能研究[J].热加工工艺,2017,46(22):92-94.
【16】师小红,徐章遂,康健.基于断裂力学的疲劳裂纹扩展速率公式研究[J].机械设计与制造,2007(10):11-12.
【17】ILMAN M N, ISWANTO P T. Fatigue crack growth rate behaviour of friction-stir aluminium alloy AA2024-T3 welds under transient thermal tensioning[J]. Materials&Design,2013,50(17):235-243.
【18】HONG S, LEE S. Dynamic strain aging under tensile and LCF loading conditions, and their comparison in cold worked 316Lstainless steel[J]. Journal of Nuclear Materials,2004,328(2/3):232-242.
相关信息