Cracking Causes of Sampling Pipe of High Pressure Superheater for Waste Heat Boiler
摘 要
某电厂254 MW燃气机组在运行过程中发现,其材料为07Cr19Ni10不锈钢的高压过热器取样管弯头处发生开裂。通过宏观观察、化学成分分析、金相检验、硬度测试、微观分析及金相检验等方法,对取样管的开裂原因进行了分析。结果表明:由于高压过热器取样管安装不当,取样管弯头处受到斜向上的拉应力。同时,取样管原始质量存在缺陷,其在高温高压工况下长期服役,随着第二相逐渐向晶界偏聚,当晶界强度低于所受拉应力时,晶界被拉裂从而形成裂纹。裂纹沿壁厚方向扩展,最终导致取样管开裂失效。
Abstract
During the operation of 254 MW gas-fired unit in a power plant, it was found that the elbow of sampling pipe of high pressure superheater made of 07cr19Ni10 stainless steel cracked. The cracking causes of the sampling pipe were analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, hardness test, microscopic analysis and metallographic examination. The results show that due to improper installation of the sampling pipe of high pressure superheater, the elbow of the sampling pipe was subject to oblique upward tensile stress. At the same time, the original quality of the sampling pipe had defects. It has been used for a long time under high temperature and high pressure. As the second phase gradually segregated to the grain boundary, when the strength of the grain boundary was lower than the stress, the grain boundary be pulled to crack and formed cracks. The cracks propagated along the wall thickness direction, which eventually led to the cracking failure of the sampling pipe.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202104018
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/6/30
修改稿日期
网络出版日期
作者单位点击查看
备注李根(1989-),男,工程师,主要从事电站金属材料的失效分析工作,gen-li@chder.com
引用该论文: LI Gen,LI Yang,SU Xiaoyang,SHANG Wei,LIU Xinying. Cracking Causes of Sampling Pipe of High Pressure Superheater for Waste Heat Boiler[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2021, 57(4): 73~76
李根,李杨,苏晓阳,尚伟,刘昕颖. 余热锅炉高压过热器取样管开裂原因[J]. 理化检验-物理分册, 2021, 57(4): 73~76
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李鹏刚,王强.某超(超)临界锅炉温度套管失效原因分析[J].铸造技术,2019,40(11):1211-1214.
【2】朱海宝,李戈,王鲁,等.汽轮机EH油系统用奥氏体不锈钢弯管开裂的原因分析[J].热加工工艺,2019,48(12):174-177.
【3】张瑞锋,刘霞.304不锈钢弯头开裂失效分析[J].理化检验(物理分册),2019,55(5):351-355.
【4】马军涛,卢杉.采煤机螺母开裂的失效分析[J].金属热处理,2019,44(10):206-208.
【5】姜锡山,赵晗.钢铁显微断口速查手册[M].北京:机械工业出版社,2010.
【6】赵延灵.余热锅炉不锈钢烟管开裂原因分析[J].理化检验(物理分册),2020,56(1):34-37.
【7】BANSOD A V,PATIL A P,MOON A P,et al. Intergranular corrosion behavior of low-nickel and 304 austenitic stainless steels[J]. Journal of Materials Engineering and performance,2016,25(9):3615-3626.
【8】TATSUYA F,KENJI K,RIKA K,et al. Formation of intergranular M23C6 in sensitized type-347 stainless steel[J]. The Iron and Steel Institute of Japan,2014,54(1):148-152.
【9】曹建春,刘铖霖,高鹏,等.钢中元素偏聚的研究现状及其发展趋势[J].钢铁,2019,54(6):11-19.
【10】薄鑫涛.关于钢中的磷[J].热处理,2015,30(5):40-42.
【11】李益民,范长信,杨百勋,等.大型火电机组用新型耐热钢[M].北京:中国电力出版社,2013.
【2】朱海宝,李戈,王鲁,等.汽轮机EH油系统用奥氏体不锈钢弯管开裂的原因分析[J].热加工工艺,2019,48(12):174-177.
【3】张瑞锋,刘霞.304不锈钢弯头开裂失效分析[J].理化检验(物理分册),2019,55(5):351-355.
【4】马军涛,卢杉.采煤机螺母开裂的失效分析[J].金属热处理,2019,44(10):206-208.
【5】姜锡山,赵晗.钢铁显微断口速查手册[M].北京:机械工业出版社,2010.
【6】赵延灵.余热锅炉不锈钢烟管开裂原因分析[J].理化检验(物理分册),2020,56(1):34-37.
【7】BANSOD A V,PATIL A P,MOON A P,et al. Intergranular corrosion behavior of low-nickel and 304 austenitic stainless steels[J]. Journal of Materials Engineering and performance,2016,25(9):3615-3626.
【8】TATSUYA F,KENJI K,RIKA K,et al. Formation of intergranular M23C6 in sensitized type-347 stainless steel[J]. The Iron and Steel Institute of Japan,2014,54(1):148-152.
【9】曹建春,刘铖霖,高鹏,等.钢中元素偏聚的研究现状及其发展趋势[J].钢铁,2019,54(6):11-19.
【10】薄鑫涛.关于钢中的磷[J].热处理,2015,30(5):40-42.
【11】李益民,范长信,杨百勋,等.大型火电机组用新型耐热钢[M].北京:中国电力出版社,2013.
相关信息