Nondestructive evaluation of thermal aging of 17-4PH stainless steel bymulti-magnetic parameters
摘 要
在350 ℃下对17-4PH不锈钢进行加速热老化后开展力学试验、磁滞回线测试试验与磁多参数测试试验,结果表明,17-4PH不锈钢热老化后冲击功下降,硬度上升。磁滞回线表明热老化对17-4PH不锈钢的宏观磁性无明显影响,且磁参数呈无规律性波动。应用人工神经网络选取合适的节点数与算法,可建立17-4PH不锈钢热老化的多参数高精度评估模型,为17-4PH不锈钢的热老化评估提供新的方法。
Abstract
The mechanical experiment, hysteresis loop test and multi-magnetic parameters test were carried out after accelerated thermal aging of 17-4PH under 350℃. Results show that the impact energy of 17-4PH decrease while the hardness increase after thermal aging. The hysteresis loop shows that thermal aging has no impact on macroscopic magnetism of 17-4PH and the magnetic parameters show no regular change. Through the application of artificial neural network, the proper node and algorithmic was chosen to build the precise module to evaluate the thermal aging of 17-4PH, which provide a new way to evaluate the thermal aging of 17-4PH.
中图分类号 TG115.28 DOI 10.11973/wsjc202105007
所属栏目 试验研究
基金项目
收稿日期 2020/12/3
修改稿日期
网络出版日期
作者单位点击查看
备注褚英杰(1983-),男,高级工程师,研究方向为核电设备的老化、腐蚀及失效分析
引用该论文: CHU Yingjie,SUN Qi,LI Qianwu,SHI Fangjie,HUANG Fei,YANG Guangyu. Nondestructive evaluation of thermal aging of 17-4PH stainless steel bymulti-magnetic parameters[J]. Nondestructive Testing, 2021, 43(5): 29~33
褚英杰,孙琦,李乾武,史芳杰,黄飞,杨广宇. 17-4PH不锈钢热老化的磁多参数无损评估[J]. 无损检测, 2021, 43(5): 29~33
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王瀚霄, 白冰, 张长义, 等. 核电阀杆材料17-4PH不锈钢服役不同时间的组织性能分析[J]. 核科学与工程, 2018, 38(2):318-325.
【2】张磊, 王正品,要玉宏,等.热老化对核电阀杆用17-4PH钢电化学腐蚀性能的影响[J].热加工工艺,2020,49(2):108-113.
【3】BHATTACHARYA D K, JAYAKUMAR T, MOORTHY V, et al. Characterization of microstructures in 17-4-PH stainless steel by magnetic Barkhausen noise analysis[J]. NDT & E International, 1993, 26(3):141-148.
【4】BHATTACHARYA D K, VAIDYANATHAN S, MOORTHY V, et al. Magnetic Barkhausen noise analysis for the assessment of microstructures in heat treated 2. 25Cr-1Mo and 17-4-PH steels[J]. NDT & E International, 1996,29(5):338.
【5】GUPTA B, UCHIMOTO T, DUCHARNE B, et al. Magnetic incremental permeability non-destructive evaluation of 12 Cr-Mo-W-V steel creep test samples with varied ageing levels and thermal treatments[J]. NDT & E International, 2019, 104(6):42-50.
【6】薛飞, 史芳杰,孙琦,等.沉淀硬化马氏体不锈钢热老化脆化的热电势检测研究[J].核动力工程,2019,40(6):135-139.
【7】郑裕芳. 铁在常温至居里温度之穆斯堡尔谱研究[J]. 核技术, 1984(4):34-35.
【2】张磊, 王正品,要玉宏,等.热老化对核电阀杆用17-4PH钢电化学腐蚀性能的影响[J].热加工工艺,2020,49(2):108-113.
【3】BHATTACHARYA D K, JAYAKUMAR T, MOORTHY V, et al. Characterization of microstructures in 17-4-PH stainless steel by magnetic Barkhausen noise analysis[J]. NDT & E International, 1993, 26(3):141-148.
【4】BHATTACHARYA D K, VAIDYANATHAN S, MOORTHY V, et al. Magnetic Barkhausen noise analysis for the assessment of microstructures in heat treated 2. 25Cr-1Mo and 17-4-PH steels[J]. NDT & E International, 1996,29(5):338.
【5】GUPTA B, UCHIMOTO T, DUCHARNE B, et al. Magnetic incremental permeability non-destructive evaluation of 12 Cr-Mo-W-V steel creep test samples with varied ageing levels and thermal treatments[J]. NDT & E International, 2019, 104(6):42-50.
【6】薛飞, 史芳杰,孙琦,等.沉淀硬化马氏体不锈钢热老化脆化的热电势检测研究[J].核动力工程,2019,40(6):135-139.
【7】郑裕芳. 铁在常温至居里温度之穆斯堡尔谱研究[J]. 核技术, 1984(4):34-35.
相关信息