Current Density and Corrosion Morghology of Steel Bar Corrosion in Reinforced Concrete
摘 要
研究了辅助电极布置位置对钢筋锈蚀外形的影响,定量分析了4种辅助电极布置情况下的钢筋锈蚀分布。结果表明:合理布置辅助电极可产生与自然状态下相似的钢筋锈蚀外形。通电锈蚀试验证明了该仿真模型的可靠性。
Abstract
The influence of the location of auxiliary electrode on the corrosion morghology of steel bar was studied, and the distribution of steel bar corrosion under four auxiliary electrode arrangements was quantitatively analyzed. The results show that a reasonable arrangement of the auxiliary electrode could produced the corrosion morghology of the steel bar similar to the natural state; power-on corrosion test proved the reliability of the simulation model.
中图分类号 TU375 DOI 10.11973/fsyfh-202107007
所属栏目 试验研究
基金项目 国家自然科学基金(51778310);西部绿色建筑国家重点实验室2019年度开放基金(LSKF201909);北京建筑未来城市设计先进创新中心开放项目(UDC2017011312)
收稿日期 2019/11/26
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: LIU Jirui,SHANG Huaishuai,WANG Weizhao,LI Shuliang,HU Zhongcun. Current Density and Corrosion Morghology of Steel Bar Corrosion in Reinforced Concrete[J]. Corrosion & Protection, 2021, 42(7): 34
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】CHOI Y S,YI S T,KIM M Y,et al. Effect of corrosion method of the reinforcing bar on bond characteristics in reinforced concrete specimens[J]. Construction and Building Materials,2014,54:180-189.
【2】曾严红,顾祥林,张伟平,等. 混凝土中钢筋加速锈蚀方法探讨[J]. 结构工程师,2009,25(1):101-105.
【3】陆春华,褚天舒,杨金木,等. 通电加速与氯盐干湿条件下钢筋锈蚀的时间相似关系试验[J]. 南京工业大学学报(自然科学版),2019,41(2):194-200.
【4】MAYRBAURL R M,CAMO S. Cracking and fracture of sus-pension bridge wire[J]. Bridge Eng,2001,6(6):645.
【5】叶华文,王义强,孙鹏鹏. 桥梁缆索腐蚀镀锌钢丝的疲劳强度试验研究[J]. 世界桥梁,2013,41(4):44-49.
【6】王义强,叶华文,段熹. 腐蚀桥梁缆索的氢脆和腐蚀疲劳研究[J]. 中外公路,2014,34(6):110-116.
【7】徐文雷,宁世伟,栾佰峰,等. 桥梁缆索用超高强度镀锌钢丝的研制[J]. 金属制品,2010,36(2):27-31.
【8】薛花娟,王吉英. 鸭绿江大桥锌铝合金镀层钢丝技术研究及质量控制[J]. 公路,2015,2:106-110.
【9】ROSALBINO F,ANGELINI E,MACCIO D,et al. Influence of rare earths addition on the corrosion behaviour of Zn-5%Al (Galfan) alloy in neutral aerated sodium sulphate solution[J]. Electrochimica Acta,2007,52(24):7107-7114.
【10】桑春明,周代义,白柄东. 苏通大桥斜拉索用镀锌钢丝生产[J]. 金属制品,2008,34(2):11-15.
【11】MARCHEBOIS H,JOIRET S,SAVALL C,et al. Characterization of zinc-rich powder coatings by EIS and Raman spectroscopy[J]. Surface and Coatings Technology,2002,157(2):151-161.
【12】SERE P R,ZAPPONI M,ELSNER C I,et al. Comparative corrosion behaviour of 55Aluminium-zinc alloy and zinc hot-dip coatings deposited on low carbon steel substrates[J]. Corrosion Science,1998,40(10):1711-1723.
【2】曾严红,顾祥林,张伟平,等. 混凝土中钢筋加速锈蚀方法探讨[J]. 结构工程师,2009,25(1):101-105.
【3】陆春华,褚天舒,杨金木,等. 通电加速与氯盐干湿条件下钢筋锈蚀的时间相似关系试验[J]. 南京工业大学学报(自然科学版),2019,41(2):194-200.
【4】MAYRBAURL R M,CAMO S. Cracking and fracture of sus-pension bridge wire[J]. Bridge Eng,2001,6(6):645.
【5】叶华文,王义强,孙鹏鹏. 桥梁缆索腐蚀镀锌钢丝的疲劳强度试验研究[J]. 世界桥梁,2013,41(4):44-49.
【6】王义强,叶华文,段熹. 腐蚀桥梁缆索的氢脆和腐蚀疲劳研究[J]. 中外公路,2014,34(6):110-116.
【7】徐文雷,宁世伟,栾佰峰,等. 桥梁缆索用超高强度镀锌钢丝的研制[J]. 金属制品,2010,36(2):27-31.
【8】薛花娟,王吉英. 鸭绿江大桥锌铝合金镀层钢丝技术研究及质量控制[J]. 公路,2015,2:106-110.
【9】ROSALBINO F,ANGELINI E,MACCIO D,et al. Influence of rare earths addition on the corrosion behaviour of Zn-5%Al (Galfan) alloy in neutral aerated sodium sulphate solution[J]. Electrochimica Acta,2007,52(24):7107-7114.
【10】桑春明,周代义,白柄东. 苏通大桥斜拉索用镀锌钢丝生产[J]. 金属制品,2008,34(2):11-15.
【11】MARCHEBOIS H,JOIRET S,SAVALL C,et al. Characterization of zinc-rich powder coatings by EIS and Raman spectroscopy[J]. Surface and Coatings Technology,2002,157(2):151-161.
【12】SERE P R,ZAPPONI M,ELSNER C I,et al. Comparative corrosion behaviour of 55Aluminium-zinc alloy and zinc hot-dip coatings deposited on low carbon steel substrates[J]. Corrosion Science,1998,40(10):1711-1723.
相关信息