Cracking Causes of Steel Plate of Wind Turbine Tower during Production
摘 要
某风力发电机塔筒钢板在压制成筒形过程中发生开裂。通过宏观观察、断口分析、化学成分分析、力学性能试验、金相检验及低倍检验等方法对风力发电机塔筒钢板的开裂原因进行了分析。结果表明:钢板板坯上存在裂纹类的缺陷,在加热炉中发生了氧化和脱碳,经过轧制后形成了折叠裂纹。在随后的钢板压制成筒形过程中,钢板外弧表面受到拉应力作用而发生开裂。
Abstract
The steel plate of a wind turbine tower cracked during pressing process into a cylinder. The cracking causes of wind turbine tower steel plate were analyzed by means of macro observation, fracture analysis, chemical composition analysis, mechanical property test, metallographic inspection and low magnification inspection. The results show that there were defects such as cracks on the steel slab, oxidation and decarburization occurred in the heating furnace, and folding cracks were formed after rolling. In the subsequent pressing process into a cylinder, the outer arc surface of the steel plate was cracked under the action of tensile stress.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202110017
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/11/20
修改稿日期
网络出版日期
作者单位点击查看
备注刘占龙(1989-),男,中级,主要从事工程技术管理工作,673153753@qq.com
引用该论文: LIU Zhanlong,JIA Lufei,WANG Ruihao,ZENG Yazhuo. Cracking Causes of Steel Plate of Wind Turbine Tower during Production[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2021, 57(10): 72~75
刘占龙,贾璐菲,王瑞皓,曾雅卓. 生产过程中风力发电机塔筒钢板开裂原因[J]. 理化检验-物理分册, 2021, 57(10): 72~75
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】温树德.金相技术在失效分析中的作用[J].汽车齿轮, 1996(4):68-71.
【2】郝玉昌.热轧带钢表面质量缺陷的形成及控制措施[J].信息周刊, 2020(3):1-2.
【3】郭景红.风电塔筒制作过程研究[J].科技与企业, 2013(17):285-286.
【4】王峰.低合金中厚板破边缺陷分析及预防[J].热加工工艺.2016, 45(19).256-258.
【5】潘红涛.Q345C钢板表面裂纹金相分析[J].物理测试.2007, 25(1):40-41.
【2】郝玉昌.热轧带钢表面质量缺陷的形成及控制措施[J].信息周刊, 2020(3):1-2.
【3】郭景红.风电塔筒制作过程研究[J].科技与企业, 2013(17):285-286.
【4】王峰.低合金中厚板破边缺陷分析及预防[J].热加工工艺.2016, 45(19).256-258.
【5】潘红涛.Q345C钢板表面裂纹金相分析[J].物理测试.2007, 25(1):40-41.
相关信息