Determination of Gold in Crude Lead by ICP-AES after Separation with Low Temperature Ethanol
摘 要
建立了低温乙醇分离-电感耦合等离子体原子发射光谱法(ICP-AES)测定粗铅中金含量的方法。取2.0~10.0 g粗铅样品,先用33%(体积分数)硝酸溶液溶解,再用盐酸溶解完全。加入液溴(氯金酸保护剂) 1~3 mL,微沸赶酸至体积约为20 mL后,再加入液溴2 mL和水50 mL,进行重复赶酸,以降低体系酸度。在上述体系中加入60 mL乙醇,0 ℃放置2 h后过滤。弃去沉淀,在滤液中加入1~3 mL液溴,加热除去乙醇至体积约为10 mL,用5%(体积分数)盐酸溶液定容至10~50 mL,供ICP-AES分析。结果显示:金的质量浓度在0.5~8.0 mg·L-1内与其对应的光谱强度呈线性关系,检出限(3.143s)为0.026 g·t-1;对纯铅样品进行加标回收试验,回收率大于96.0%;方法用于实际样品分析,并与YS/T 248.6-2007进行比对,所得测定值基本一致,标准偏差(0.085 g·t-1)低于依据YS/T 248.6-2007中内插法计算所得的重复性限(0.5 g·t-1)。
Abstract
A method for determination of gold in crude lead by ICP-AES after separation with low temperature ethanol was established. Crude lead sample (2.0-10.0 g) was taken and dissolved with 33% (volume fraction) nitric acid solution, and then completely dissolved with hydrochloric acid. 1-3 mL of liquid bromine (chloroauric acid protector) was added, and the acid in the solution was driven out by boiling slightly, and the volume of the solution was concentrated to about 20 mL. Liquid bromine (2 mL) and water (50 mL) were added to drive out the acid repeatedly, thus to reduce the acidity of the system. Ethanol (60 mL) was added to the above system, and the solution was placed at 0℃ for 2 h and filtered. The precipitation was discarded, liquid bromine (1-3 mL) was added into the filtrate, and the solution was heated to remove ethanol until the volume reached about 10 mL and then diluted to 10-50 mL with 5% (volume fraction) hydrochloric acid solution for ICP-AES analysis. The results showed that linear relationship between mass concentration of gold and its respective spectral intensity was kept in the range of 0.5-8.0 mg·L-1, with detection limit (3.143s) of 0.026 g·t-1. The spiked recovery test was made on pure lead, giving values of recovery more than 96.0%. The prescribed method was applied to the analysis of actual sample and compared with YS/T 248.6-2007, the determined value was basically consistent, and the standard deviation (0.085 g·g-1) was lower than the repeatability limit (0.5 g·t-1) calculated by the interpolation method in YS/T 248.6-2007.
中图分类号 O657.31 DOI 10.11973/lhjy-hx202111003
所属栏目 工作简报
基金项目
收稿日期 2020/11/19
修改稿日期
网络出版日期
作者单位点击查看
备注齐白羽,高级工程师,硕士,主要从事理化检验与环境检测方面研究工作,86569014@qq.com。
引用该论文: QI Baiyu,WANG Ding,WANG Zhuo,LU Changxiang,LIU Jingjing. Determination of Gold in Crude Lead by ICP-AES after Separation with Low Temperature Ethanol[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2021, 57(11): 977~980
齐白羽,王丁,王卓,卢昌祥,刘静静. 低温乙醇分离-电感耦合等离子体原子发射光谱法测定粗铅中金[J]. 理化检验-化学分册, 2021, 57(11): 977~980
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘亮, 柯玲.铅试金法测定铅精矿及粗铅中的金、银[J].分析试验室, 2007, 26(增刊1):111-115.
【2】王景凤.火试金富集测定粗铅中金、银含量的改进试验研究[J].有色金属科学与工程, 2018, 9(3):100-104.
【3】赵德年.直接灰吹粗铅中金银的测定[J].冶金分析, 1988, 8(6):57-57.
【4】杜勤文, 陈金亮.活性炭吸附-原子吸收光谱法测定粗铅中金[J].分析试验室, 1984, 3(5):44-46.
【5】王丽, 马会春, 庞雪敏, 等.活性炭动态吸附ICP-AES法测定粗铅中的金[J].中国测试, 2019, 45(4):58-62.
【6】范延臻, 王宝贞, 王琳, 等.改性活性炭的表面特性及其对金属离子的吸附性能[J].环境化学, 2001, 20(5):437-443.
【7】伍喜庆, 黄志华.改性活性炭吸附金的性能[J].中国有色金属学报, 2005, 15(1):129-132.
【8】李子龙, 马双枫, 王栋, 等.活性炭吸附水中金属离子和有机物吸附模式和机理的研究[J].环境科学与管理, 2009, 34(10):88-92.
【9】张婕, 申宗华.粗铅中金的测定[J].湖南冶金, 1996, 24(2):49-51.
【10】《岩石矿物分析》编写组.岩石矿物分析(第一分册)[M].4版.北京:地质出版社, 2011:841-856.
【2】王景凤.火试金富集测定粗铅中金、银含量的改进试验研究[J].有色金属科学与工程, 2018, 9(3):100-104.
【3】赵德年.直接灰吹粗铅中金银的测定[J].冶金分析, 1988, 8(6):57-57.
【4】杜勤文, 陈金亮.活性炭吸附-原子吸收光谱法测定粗铅中金[J].分析试验室, 1984, 3(5):44-46.
【5】王丽, 马会春, 庞雪敏, 等.活性炭动态吸附ICP-AES法测定粗铅中的金[J].中国测试, 2019, 45(4):58-62.
【6】范延臻, 王宝贞, 王琳, 等.改性活性炭的表面特性及其对金属离子的吸附性能[J].环境化学, 2001, 20(5):437-443.
【7】伍喜庆, 黄志华.改性活性炭吸附金的性能[J].中国有色金属学报, 2005, 15(1):129-132.
【8】李子龙, 马双枫, 王栋, 等.活性炭吸附水中金属离子和有机物吸附模式和机理的研究[J].环境科学与管理, 2009, 34(10):88-92.
【9】张婕, 申宗华.粗铅中金的测定[J].湖南冶金, 1996, 24(2):49-51.
【10】《岩石矿物分析》编写组.岩石矿物分析(第一分册)[M].4版.北京:地质出版社, 2011:841-856.
相关信息