某水电厂锅炉水冷壁管泄漏的原因
Cause of Leakage of Water Wall Tube of Boiler of a Hydropower Plant
摘 要
某水电厂锅炉水冷壁管发生泄漏，通过宏观观察、化学成分分析、扫描电镜分析、能谱分析以及显微组织观察等方法，分析了水冷壁管泄漏的原因。结果表明：水冷壁管发生泄漏的原因是高温烟气中的腐蚀性介质渗入墙体内部，导致水冷壁管发生腐蚀，管壁减薄，最终发生泄漏。
腐蚀
泄漏
water wall tube
corrosion
leakage
Abstract
A water wall tube leaked of boiler of a hydropower plant. Through macro observation, chemical composition analysis, scanning electron microscopy analysis, energy spectrum analysis and microstructure observation, the reason for leakage of water wall tube was analyzed. The results showed that the reason for leakage of water wall tube was that corrosive medium in high-temperature flue gas penetrated into the wall, causing water wall tube to corrode, tube wall was thinned, and finally leaked.
中图分类号 TG115 DOI 10. 11973/lhjy-wl202111016
所属栏目 质量控制与失效分析
基金项目
收稿日期 2020/9/28
修改稿日期
网络出版日期
作者单位点击查看
备注付洋洋(1989-),男,工程师,主要从事金相检验及失效分析工作,nlfd_lg@163.com
引用该论文: FU Yangyang. Cause of Leakage of Water Wall Tube of Boiler of a Hydropower Plant[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2021, 57(11): 63～65
付洋洋. 某水电厂锅炉水冷壁管泄漏的原因[J]. 理化检验－物理分册, 2021, 57(11): 63～65
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】范从振. 锅炉原理[M]. 北京:水利电力出版社, 1986.
【2】郭巍.电厂煤粉锅炉水冷壁管爆管分析与防护措施研究[D].上海:华东理工大学, 2015.
【3】次仁德吉.电化学反应及其腐蚀[J]. 广州化学, 2009, 34(3):73-77.
【2】郭巍.电厂煤粉锅炉水冷壁管爆管分析与防护措施研究[D].上海:华东理工大学, 2015.
【3】次仁德吉.电化学反应及其腐蚀[J]. 广州化学, 2009, 34(3):73-77.
相关信息