Cause of leakage analysis of vacuum brazed stainless steel plate heat exchanger
摘 要
某换热器在长期使用后出现渗水和腐蚀现象,对其渗漏部位进行宏观检查、扫描电镜及能谱分析。结果表明:部分区域的铜焊料与不锈钢基体在焊接时未完全熔合;在换热器使用期间,多次热循环与水流周期性冲击使焊接未熔合区域的铜焊料与不锈钢基体分离,最终导致局部渗水。
Abstract
Water seepage and corrosion occurred in a heat exchanger after long-term use. Macroscopic examination, scanning electron microscope and energy spectrum analysis were performed on the leakage site. The results show that the copper solder in some areas was not fully fused with the stainless steel substrate during welding. During the use of heat exchanger, multiple thermal cycles and periodic impact of water flow separated the copper solder from the stainless steel substrate in the unmelted area of welding, and eventually led to local water seepage.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202202016
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/3/22
修改稿日期
网络出版日期
作者单位点击查看
备注应桂元(1995-),男,硕士研究生,主要从事换热器失效分析工作
引用该论文: YING Guiyuan,LIU Jiejie,XIANG Xiongzhi. Cause of leakage analysis of vacuum brazed stainless steel plate heat exchanger[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(2): 66~69
应桂元,刘洁洁,向雄志. 真空钎焊不锈钢板式换热器渗漏原因[J]. 理化检验-物理分册, 2022, 58(2): 66~69
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】曹影, 张成文. 换热器应用与发展前景[J]. 中国机械, 2014(3):116-117.
【2】赵桐. 斜方格板式换热器的流体流动与传热模拟及新板片结构开发[D]. 北京:北京化工大学, 2018.
【3】陈永东, 张明然, 艾志斌. 钎焊板式换热器的失效分析[J]. 压力容器, 2005, 22(12):39-42, 35.
【4】BOBIČ M H, GJEREK B, GOLOBIČ I, et al. Dynamic behaviour of a plate heat exchanger:Influence of temperature disturbances and flow configurations[J]. International Journal of Heat and Mass Transfer, 2020, 163:120439.
【5】魏松, 张亚霄, 周晓蕾, 等. 紫铜与不锈钢真空钎焊组织与力学性能[J]. 焊接, 2020(3):54-57, 68.
【6】张青科, 钟素娟, 张雷, 等. 奥氏体不锈钢-铜钎料钎焊界面反应行为分析[J]. 焊接学报, 2017, 38(3):75-78, 132.
【7】刘建波. 浅谈低碳钢管道焊接缺陷产生的原因及措施[J]. 冶金与材料, 2018, 38(6):143-144.
【8】NILPUENG K, ASIRVATHAM L G, DALKL A S, et al. Heat transfer and fluid flow characteristics in a plate heat exchanger filled with copper foam[J]. Heat and Mass Transfer, 2020, 56(12):3261-3271.
【9】张杰, 窦泉山, 吴业俊, 等. 热丝TIG焊层间未熔合缺陷成因与预防措施[J]. 金属加工(热加工), 2020(11):66-68.
【10】王思鸿. 薄壁不锈钢细管的钎焊材料、工艺及机理研究[D]. 杭州:浙江科技学院, 2019.
【2】赵桐. 斜方格板式换热器的流体流动与传热模拟及新板片结构开发[D]. 北京:北京化工大学, 2018.
【3】陈永东, 张明然, 艾志斌. 钎焊板式换热器的失效分析[J]. 压力容器, 2005, 22(12):39-42, 35.
【4】BOBIČ M H, GJEREK B, GOLOBIČ I, et al. Dynamic behaviour of a plate heat exchanger:Influence of temperature disturbances and flow configurations[J]. International Journal of Heat and Mass Transfer, 2020, 163:120439.
【5】魏松, 张亚霄, 周晓蕾, 等. 紫铜与不锈钢真空钎焊组织与力学性能[J]. 焊接, 2020(3):54-57, 68.
【6】张青科, 钟素娟, 张雷, 等. 奥氏体不锈钢-铜钎料钎焊界面反应行为分析[J]. 焊接学报, 2017, 38(3):75-78, 132.
【7】刘建波. 浅谈低碳钢管道焊接缺陷产生的原因及措施[J]. 冶金与材料, 2018, 38(6):143-144.
【8】NILPUENG K, ASIRVATHAM L G, DALKL A S, et al. Heat transfer and fluid flow characteristics in a plate heat exchanger filled with copper foam[J]. Heat and Mass Transfer, 2020, 56(12):3261-3271.
【9】张杰, 窦泉山, 吴业俊, 等. 热丝TIG焊层间未熔合缺陷成因与预防措施[J]. 金属加工(热加工), 2020(11):66-68.
【10】王思鸿. 薄壁不锈钢细管的钎焊材料、工艺及机理研究[D]. 杭州:浙江科技学院, 2019.
相关信息