热轧钢板高频直缝电阻焊接制管开裂原因
Reasons for cracking of high frequency longitudional resistance welding pipe of hot-rolled steel plate
摘 要
某公司使用热轧钢板生产高频直缝电阻焊管,焊管端部在切削后发生开裂。采用宏观观察、化学成分分析、金相检验及断口分析等方法,分析了焊管开裂的原因。结果表明:在焊接过程中,焊接电流过大引起输入功率过高,造成焊缝温度过高,在焊缝处形成粗大的魏氏组织和大量孔洞,从而导致焊管发生开裂。
焊管
开裂
魏氏组织
孔洞
hot-rolled steel plate
welded pipe
cracking
Widmanstä
tten structure
hole
Abstract
A company used hot-rolled steel plate to produce pipes by high frequency longitudinal resis tance welding,the welded pipe end cracked after cutting.By means of macroscopic observation,chemical composition analysis,metallographic inspection and fracture analysis,the reasons for cracking of welded pipe were analyzed.The results showed that in the welding process,the input power was too high due to the excessive welding current,which caused the welding seam temperature to be too high.Thick Widmanstätten microstructure and a large number of holes were formed at the weld,which led to cracking of welded pipe.
中图分类号 TG115 DOI 10.11973/lhjy-wl202203014
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/2/25
修改稿日期
网络出版日期
作者单位点击查看
备注海超(1975-),男,高级工程师,主要从事金属材料质量分析工作,bxhch@126.com
引用该论文: HAI Chao,GUO Xiaojing. Reasons for cracking of high frequency longitudional resistance welding pipe of hot-rolled steel plate[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(3): 49～52
海超,郭晓静. 热轧钢板高频直缝电阻焊接制管开裂原因[J]. 理化检验－物理分册, 2022, 58(3): 49～52
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张君彩,刘毅.焊接温度对焊管焊缝质量的影响[J].焊接,2007(1):60.
【2】邓有林,邵丽慧.20钢管焊缝开裂分析[J].理化检验(物理分册),2004,40(11):578-580.
【3】于恩林,韩毅,范玉林,等.HFW管高频感应加热过程电磁热耦合数值模拟[J].焊接学报,2010,31(4):5-8,113.
【4】孟根巴根,艾兵权,王秋雨,等.S380高频焊管焊缝开裂分析[J].焊接,2019(8):57-60,68.
【5】上海交通大学《金属断口分析》编写组.金属断口分析[M].北京:国防工业出版社,1979.
【6】姜锡山,赵晗.钢铁显微断口速查手册[M].北京:机械工业出版社,2010.
【7】张波.烟囱焊接开裂分析[J].理化检验(物理分册),2006,42(11):586-587.
【2】邓有林,邵丽慧.20钢管焊缝开裂分析[J].理化检验(物理分册),2004,40(11):578-580.
【3】于恩林,韩毅,范玉林,等.HFW管高频感应加热过程电磁热耦合数值模拟[J].焊接学报,2010,31(4):5-8,113.
【4】孟根巴根,艾兵权,王秋雨,等.S380高频焊管焊缝开裂分析[J].焊接,2019(8):57-60,68.
【5】上海交通大学《金属断口分析》编写组.金属断口分析[M].北京:国防工业出版社,1979.
【6】姜锡山,赵晗.钢铁显微断口速查手册[M].北京:机械工业出版社,2010.
【7】张波.烟囱焊接开裂分析[J].理化检验(物理分册),2006,42(11):586-587.
相关信息