掺稀泵压盖螺栓断裂原因
Reasons for fracture of bolts in pressure cover of dilute pump
摘 要
采用宏观和微观形貌分析、材料性能试验、金相检验、螺栓载荷校核等方法对某掺稀泵压盖螺栓断裂原因进行分析。结果表明:高周疲劳导致掺稀泵压盖螺栓断裂,螺栓螺纹表面脱碳层的厚度超标、材料性能下降等对螺栓的疲劳断裂具有促进作用。
疲劳断裂
载荷校核
高周疲劳
bolt
fatigue fracture
load checking
high cycle fatigue
Abstract
Macroscopic and microscopic morphology analysis, material performance test, metallographic examination, bolt load checking and other methods were used to analyze the fracture reason of the pressure cover bolt of a dilute pump. The results show that the high cycle fatigue leaded to the fracture of the bolt of the pressure cover of the dilute pump. The thickness of the decarburized layer on the surface of the bolt thread exceeded the standard and decline of material properties promoted fatigue fracture of bolt.
中图分类号 U213.5+2 TG115.5 DOI 10.11973/lhjy-wl202204014
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/8/9
修改稿日期
网络出版日期
作者单位点击查看
备注吕庆钢(1973-),男,高级工程师,主要从事油田物资质量管理和石油专用管质量检验、现场评价、质量事故调查分析等工作
引用该论文: LYU Qinggang,YANG Shasha,WANG Haibo,JI Bingyin,SHI Jiaoqi. Reasons for fracture of bolts in pressure cover of dilute pump[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(4): 52～55
吕庆钢,杨莎莎,王海博,姬丙寅,史交齐. 掺稀泵压盖螺栓断裂原因[J]. 理化检验－物理分册, 2022, 58(4): 52～55
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王国阳,徐卫平,张保奇,等. 船用柴油机活塞连接螺栓断裂失效分析[J]. 机械工程材料,2006,30(4):92-94.
【2】张栋,钟培道. 失效分析[M]. 北京:国防工业出版社,2005.
【3】吴连生.失效分析技术及其应用——第七讲疲劳断裂失效分析[J].理化检验(物理分册),1996,32(1):57-64.
【4】王磊,陈学广,斐海祥.柴油机用高强度螺栓断裂失效分析[J].理化检验(物理分册),2016,52(6):431-434.
【2】张栋,钟培道. 失效分析[M]. 北京:国防工业出版社,2005.
【3】吴连生.失效分析技术及其应用——第七讲疲劳断裂失效分析[J].理化检验(物理分册),1996,32(1):57-64.
【4】王磊,陈学广,斐海祥.柴油机用高强度螺栓断裂失效分析[J].理化检验(物理分册),2016,52(6):431-434.
相关信息