Corrosion and Wear Behavior of Fe-19Cr-15Mn-0.66N HNSS in Air and 0.5 mol/L NaCl Solution
摘 要
以Fe-19Cr-15Mn-0.66N高氮钢为研究对象,通过摩擦磨损试验研究了其在空气和0.5 mol/L NaCl溶液中的腐蚀磨损行为。结果发现:在空气和0.5 mol/L NaCl溶液中,随着外加载荷的增加,高氮钢的摩擦因数逐渐降低,但体积损伤随之增加;高氮钢在空气中的磨损机制包括磨粒磨损、氧化磨损和脆性剥落,而在0.5 mol/L NaCl溶液中的磨损机制为磨粒磨损;在0.5 mol/L NaCl溶液中,由于磨损和腐蚀的协同作用,导致磨损率显著增加。
Abstract
The corrosion and wear behavior of Fe-19Cr-15Mn-0.66N high nitrogen stainless steel (HNSS) was studied in air and 0.5 mol/L NaCl solution by friction and wear test. The results show that in air and 0.5 mol/L NaCl solution, with the increase of applied load, the friction coefficient of the HNSS gradually decreased and the volume loss of the HNSS increased. The wear mechanisms of the HNSS in air were abrasive wear, oxidation wear and brittle spalling, while it was abrasive wear in 0.5 mol/L NaCl solution. In 0.5 mol/L NaCl solution, the wear rate increased significantly due to the synergistic effect between wear and corrosion.
中图分类号 TG174 DOI 10.11973/fsyfh-202205002
所属栏目 试验研究
基金项目
收稿日期 2021/12/10
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Lan,ZHANG Wei,GE Lianwei,WANG Xinyi,QIAO Yanxin. Corrosion and Wear Behavior of Fe-19Cr-15Mn-0.66N HNSS in Air and 0.5 mol/L NaCl Solution[J]. Corrosion & Protection, 2022, 43(5): 11
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】LEMAIRE E,CALVAR M L. Evidence of tribocorrosion wear in pressurized water reactors[J]. Wear,2001,249(5/6):338-344.
【2】JIANG J,STACK M M,NEVILLE A. Modelling the tribo-corrosion interaction in aqueous sliding conditions[J]. Tribology International,2002,35(10):669-679.
【3】NINGSHEN S,MUDALI U K,MITTAL V K,et al. Semiconducting and passive film properties of nitrogen-containing type 316LN stainless steels[J]. Corrosion Science,2007,49(2):481-496.
【4】WU X Q,FU Y,KE W,et al. Effects of nitrogen on passivity of nickel-free stainless steels by electrochemical impedance spectroscopy analysis[J]. Journal of Materials Engineering and Performance,2015,24(9):3607-3614.
【5】QIAO Y X,WANG S,LIU B,et al. Synergistic effect of corrosion and cavitation erosion of high nitrogen stainless steel[J]. Acta Metallurgica Sinica,2016,52(2):233-240.
【6】NIEDERHOFER P,HUTH S. Cavitation erosion resistance of high interstitial CrMnCN austenitic stainless steels[J]. Wear,2013,301(1/2):457-466.
【7】YOON Y S,HA H Y,LEE T H,et al. Comparative study of stress corrosion cracking susceptibility of Fe18Cr10Mn and Fe18Cr10Mn1Ni-based high nitrogen stainless steels[J]. Corrosion Science,2014,88:337-348.
【8】毕红运,李诗卓,姜晓霞.不锈钢腐蚀磨损过程中形变强化能力的研究[J].摩擦学学报,1998,18(4):327-331.
【9】BREGLIOZZI G,SCHINO A D,AHMED S I U,et al. Cavitation wear behaviour of austenitic stainless steels with different grain sizes[J]. Wear,2005,258(1/2/3/4):503-510.
【10】CHANG C C,CHEN H W,LEE J W,et al. Influence of Si contents on tribological characteristics of CrAlSiN nanocomposite coatings[J]. Thin Solid Films,2015,584:46-51.
【11】李晓春,韦习成,李健. SUS304奥氏体不锈钢的摩擦变形层研究[J].摩擦学学报,2007,27(4):341-345.
【12】FAN Q X,ZHANG J J,WU Z H,et al. Influence of Al content on the microstructure and properties of the CrAlN coatings deposited by arc ion plating[J]. Acta Metallurgica Sinica (English Letters),2017,30(12):1221-1230.
【13】QIAO Y X,SHENG S L,ZHANG L M,et al. Friction and wear behaviors of a high nitrogen austenitic stainless steel Fe-19Cr-15Mn-0.66N[J]. Journal of Mining and Metallurgy,Section B:Metallurgy,2021,57(2):285-293.
【14】ZHAO H,REN Y,DONG J,et al. The microstructure and tribological behavior of a pre-cold-deformed 0.90% nitrogen containing stainless steel[J]. Materialwissenschaft Und Werkstofftechnik,2018,49(12):1439-1448.
【15】CHEN J,YAN F Y. Tribocorrosion behaviors of Ti-6Al-4V and Monel K500 alloys sliding against 316 stainless steel in artificial seawater[J]. Transactions of Nonferrous Metals Society of China,2012,22(6):1356-1365.
【16】BATENI M R,SZPUNAR J A,WANG X,et al. Wear and corrosion wear of medium carbon steel and 304 stainless steel[J]. Wear,2006,260(1/2):116-122.
【17】DIB J,HEREÑU S,ALÍ D,et al. Influence of load,surface finish and lubrication on friction coefficient of AISI 304 stainless steel[J]. Journal of Materials Engineering and Performance,2020,29(5):2739-2747.
【18】ZANDRAHIMI M,BATENI M R,POLADI A,et al. The formation of martensite during wear of AISI 304 stainless steel[J]. Wear,2007,263(1/2/3/4/5/6):674-678.
【19】YUN J Y,SHIN G S,HUR D H,et al. Effect of strain-induced ε-and α'-martensitic transformations on the sliding wear resistance in austenitic Fe-Cr-C-Mn alloys[J]. Wear,2016,368/369:124-131.
【20】MAO Y S,WANG L,CHEN K M,et al. Tribo-layer and its role in dry sliding wear of Ti-6Al-4V alloy[J]. Wear,2013,297(1/2):1032-1039.
【21】FARGAS G,ROA J J,MATEO A. Influence of pre-existing martensite on the wear resistance of metastable austenitic stainless steels[J]. Wear,2016,364/365:40-47.
【22】CHEN J,WANG J Z,YAN F Y,et al. Effect of applied potential on the tribocorrosion behaviors of Monel K500 alloy in artificial seawater[J]. Tribology International,2015,81:1-8.
【23】BERNS H,KOCH S. Influence of abrasive particles on wear mechanism and wear resistance in sliding abrasion tests at elevated temperatures[J]. Wear,1999,233/234/235:424-430.
【24】王文琴,王昭漫,李玉龙,等.电阻缝焊法制备铁基WC/金属双层涂层及其摩擦行为[J].金属学报,2019,55(4):537-546.
【25】SHENG S L,ZHOU H L,WANG X J,et al. Friction and wear behaviors of Fe-19Cr-15Mn-0.66N steel at high temperature[J]. Coatings,2021,11(11):1285.
【26】TAO S,LI D Y. Investigation of corrosion-wear synergistic attack on nanocrystalline Cu deposits[J]. Wear,2007,263(1/2/3/4/5/6):363-370.
【27】IWABUCHI A,LEE J W,UCHIDATE M. Synergistic effect of fretting wear and sliding wear of Co-alloy and Ti-alloy in Hanks'solution[J]. Wear,2007,263(1/2/3/4/5/6):492-500.
【2】JIANG J,STACK M M,NEVILLE A. Modelling the tribo-corrosion interaction in aqueous sliding conditions[J]. Tribology International,2002,35(10):669-679.
【3】NINGSHEN S,MUDALI U K,MITTAL V K,et al. Semiconducting and passive film properties of nitrogen-containing type 316LN stainless steels[J]. Corrosion Science,2007,49(2):481-496.
【4】WU X Q,FU Y,KE W,et al. Effects of nitrogen on passivity of nickel-free stainless steels by electrochemical impedance spectroscopy analysis[J]. Journal of Materials Engineering and Performance,2015,24(9):3607-3614.
【5】QIAO Y X,WANG S,LIU B,et al. Synergistic effect of corrosion and cavitation erosion of high nitrogen stainless steel[J]. Acta Metallurgica Sinica,2016,52(2):233-240.
【6】NIEDERHOFER P,HUTH S. Cavitation erosion resistance of high interstitial CrMnCN austenitic stainless steels[J]. Wear,2013,301(1/2):457-466.
【7】YOON Y S,HA H Y,LEE T H,et al. Comparative study of stress corrosion cracking susceptibility of Fe18Cr10Mn and Fe18Cr10Mn1Ni-based high nitrogen stainless steels[J]. Corrosion Science,2014,88:337-348.
【8】毕红运,李诗卓,姜晓霞.不锈钢腐蚀磨损过程中形变强化能力的研究[J].摩擦学学报,1998,18(4):327-331.
【9】BREGLIOZZI G,SCHINO A D,AHMED S I U,et al. Cavitation wear behaviour of austenitic stainless steels with different grain sizes[J]. Wear,2005,258(1/2/3/4):503-510.
【10】CHANG C C,CHEN H W,LEE J W,et al. Influence of Si contents on tribological characteristics of CrAlSiN nanocomposite coatings[J]. Thin Solid Films,2015,584:46-51.
【11】李晓春,韦习成,李健. SUS304奥氏体不锈钢的摩擦变形层研究[J].摩擦学学报,2007,27(4):341-345.
【12】FAN Q X,ZHANG J J,WU Z H,et al. Influence of Al content on the microstructure and properties of the CrAlN coatings deposited by arc ion plating[J]. Acta Metallurgica Sinica (English Letters),2017,30(12):1221-1230.
【13】QIAO Y X,SHENG S L,ZHANG L M,et al. Friction and wear behaviors of a high nitrogen austenitic stainless steel Fe-19Cr-15Mn-0.66N[J]. Journal of Mining and Metallurgy,Section B:Metallurgy,2021,57(2):285-293.
【14】ZHAO H,REN Y,DONG J,et al. The microstructure and tribological behavior of a pre-cold-deformed 0.90% nitrogen containing stainless steel[J]. Materialwissenschaft Und Werkstofftechnik,2018,49(12):1439-1448.
【15】CHEN J,YAN F Y. Tribocorrosion behaviors of Ti-6Al-4V and Monel K500 alloys sliding against 316 stainless steel in artificial seawater[J]. Transactions of Nonferrous Metals Society of China,2012,22(6):1356-1365.
【16】BATENI M R,SZPUNAR J A,WANG X,et al. Wear and corrosion wear of medium carbon steel and 304 stainless steel[J]. Wear,2006,260(1/2):116-122.
【17】DIB J,HEREÑU S,ALÍ D,et al. Influence of load,surface finish and lubrication on friction coefficient of AISI 304 stainless steel[J]. Journal of Materials Engineering and Performance,2020,29(5):2739-2747.
【18】ZANDRAHIMI M,BATENI M R,POLADI A,et al. The formation of martensite during wear of AISI 304 stainless steel[J]. Wear,2007,263(1/2/3/4/5/6):674-678.
【19】YUN J Y,SHIN G S,HUR D H,et al. Effect of strain-induced ε-and α'-martensitic transformations on the sliding wear resistance in austenitic Fe-Cr-C-Mn alloys[J]. Wear,2016,368/369:124-131.
【20】MAO Y S,WANG L,CHEN K M,et al. Tribo-layer and its role in dry sliding wear of Ti-6Al-4V alloy[J]. Wear,2013,297(1/2):1032-1039.
【21】FARGAS G,ROA J J,MATEO A. Influence of pre-existing martensite on the wear resistance of metastable austenitic stainless steels[J]. Wear,2016,364/365:40-47.
【22】CHEN J,WANG J Z,YAN F Y,et al. Effect of applied potential on the tribocorrosion behaviors of Monel K500 alloy in artificial seawater[J]. Tribology International,2015,81:1-8.
【23】BERNS H,KOCH S. Influence of abrasive particles on wear mechanism and wear resistance in sliding abrasion tests at elevated temperatures[J]. Wear,1999,233/234/235:424-430.
【24】王文琴,王昭漫,李玉龙,等.电阻缝焊法制备铁基WC/金属双层涂层及其摩擦行为[J].金属学报,2019,55(4):537-546.
【25】SHENG S L,ZHOU H L,WANG X J,et al. Friction and wear behaviors of Fe-19Cr-15Mn-0.66N steel at high temperature[J]. Coatings,2021,11(11):1285.
【26】TAO S,LI D Y. Investigation of corrosion-wear synergistic attack on nanocrystalline Cu deposits[J]. Wear,2007,263(1/2/3/4/5/6):363-370.
【27】IWABUCHI A,LEE J W,UCHIDATE M. Synergistic effect of fretting wear and sliding wear of Co-alloy and Ti-alloy in Hanks'solution[J]. Wear,2007,263(1/2/3/4/5/6):492-500.
相关信息