基于矫顽力的T91钢老化评价方法
Aging evaluation method of T91 steel based on coercivity
摘 要
某电站锅炉T91耐热钢发生早期爆管失效,对该材料钢管进行矫顽力测量,并研究其组织老化及性能降级规律。结果表明:钢管在老化过程中,材料的硬度逐渐降低,矫顽力递增,材料老化与矫顽力遵循一定的函数变化关系;结合钢管累计运行时间、检验周期与矫顽力变化量,可动态评估钢管在服役工况下发生严重老化的剩余时间。
T91钢
矫顽力
老化
power plant boiler
T91 steel
coercive force
aging
Abstract
The early burst failure of T91 heat resistant steel of a power plant boiler occurred. The coercivity of the material steel pipe was measured, and the microstructure aging and performance degradation were studied. The results show that during the aging process of the steel tube, the hardness of the material gradually decreased, the coercive force increased, and the aging of the material and the coercive force followed a certain functional relationship. Combined with the accumulated running time, inspection period and the change of coercivity of steel pipe, the remaining time of serious aging of steel pipe under service condition could be dynamically evaluated.
中图分类号 TG142.1 DOI 10.11973/lhjy-wl202206007
所属栏目 试验与研究
基金项目 广州市市场监督管理局科技项目(2020kj24)
收稿日期 2022/1/4
修改稿日期
网络出版日期
作者单位点击查看
备注封小亮(1992-),男,硕士,工程师,主要从事金属材料理化检验与失效分析工作,466745534@qq.com
引用该论文: FENG Xiaoliang,MA Kuo,LIU Kexiu. Aging evaluation method of T91 steel based on coercivity[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(6): 26～28
封小亮,马括,刘课秀. 基于矫顽力的T91钢老化评价方法[J]. 理化检验－物理分册, 2022, 58(6): 26～28
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】束国刚,刘江南,石崇哲,等.超临界锅炉用T/P91钢的组织性能与工程应用[M].西安:陕西科学技术出版社,2006.
【2】赵彦芬,张路,赵林凤,等.国产T91钢在高温受热面中的应用评价[J].中国电力,2009,42(10):5-11.
【3】葛翔,许好好.大型电站锅炉高温炉管状态检验与寿命分析[J].中国特种设备安全,2007,23(7):3-8.
【4】钟万里,盘荣旋.超临界锅炉高温过热器T91钢管爆管分析[J].理化检验(物理分册),2009,45(7):440-443.
【5】张李锋,张兵,王小迎,等.超临界锅炉高温过热器T91钢管爆管分析[J].材料导报:纳米与新材料专辑,2014,28(1):440-442.
【6】封小亮,刘课秀,王恋,等.电站锅炉过热器管爆管分析[J].江西科学,2019,37(2):282-286.
【7】李灼贤,王伟,钟万里,等.电站T91炉管服役后的老化状况量化评定[J].广东电力,2014,27(4):13-17.
【8】杨旭.高铬马氏体耐热钢组织老化、性能退化及剩余寿命评估[D].秦皇岛:燕山大学,2019.
【9】戴道生,钱昆明.铁磁学[M].北京:科学出版社,1998.
【10】SABLIK M J,JILES D C.Coupled magnetoelastic theory of magnetic and magnetostrictive hysteresis[J].IEEE Transactions on Magnetics,1993(21):1-8.
【2】赵彦芬,张路,赵林凤,等.国产T91钢在高温受热面中的应用评价[J].中国电力,2009,42(10):5-11.
【3】葛翔,许好好.大型电站锅炉高温炉管状态检验与寿命分析[J].中国特种设备安全,2007,23(7):3-8.
【4】钟万里,盘荣旋.超临界锅炉高温过热器T91钢管爆管分析[J].理化检验(物理分册),2009,45(7):440-443.
【5】张李锋,张兵,王小迎,等.超临界锅炉高温过热器T91钢管爆管分析[J].材料导报:纳米与新材料专辑,2014,28(1):440-442.
【6】封小亮,刘课秀,王恋,等.电站锅炉过热器管爆管分析[J].江西科学,2019,37(2):282-286.
【7】李灼贤,王伟,钟万里,等.电站T91炉管服役后的老化状况量化评定[J].广东电力,2014,27(4):13-17.
【8】杨旭.高铬马氏体耐热钢组织老化、性能退化及剩余寿命评估[D].秦皇岛:燕山大学,2019.
【9】戴道生,钱昆明.铁磁学[M].北京:科学出版社,1998.
【10】SABLIK M J,JILES D C.Coupled magnetoelastic theory of magnetic and magnetostrictive hysteresis[J].IEEE Transactions on Magnetics,1993(21):1-8.
相关信息