增材制造不锈钢的组织和性能
Microstructure and properties of additive manufacturing stainless steel
摘 要
采用金相检验、扫描电镜分析等方法对激光融化技术制备的304及316L不锈钢进行分析。结果表明:材料的轴向结构在增材制造沉积过程中会有不同层间的热传递,其组织的均匀性受到影响;材料的区域成分没有明显偏差,不存在成分偏析及次相的析出;熔体的重力作用会使材料在纵向存在各向异性。
不锈钢
显微组织
性能
additive manufacturing
stainless steel
microstructure
property
Abstract
The 304 and 316 L stainless steels prepared by laser melting technology were analyzed by metallographic examination and scanning electron microscopy. The results show that the axial structure of the material had heat transfer between different layers during the deposition process of additive manufacturing, and the microstructure uniformity was affected. There was no obvious deviation in the regional composition of the material, and there was no component segregation and secondary phase precipitation. The gravity of the melt would make the material anisotropy in the longitudinal direction.
中图分类号 TG115.21 DOI 10.11973/lhjy-wl202206012
所属栏目 试验技术与方法
基金项目 甘肃省教育厅创新基金项目(2020A-218);甘肃省大学生创新创业训练计划项目(S202013933022)
收稿日期 2022/1/27
修改稿日期
网络出版日期
作者单位点击查看
备注张龙(1984-),男,硕士,高级工程师,主要从事材料改性和失效分析方面的研究工作
引用该论文: ZHANG Long,LIU Ying,LU Chuan. Microstructure and properties of additive manufacturing stainless steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(6): 46～49
张龙,刘莹,路遄. 增材制造不锈钢的组织和性能[J]. 理化检验－物理分册, 2022, 58(6): 46～49
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】田杰,黄正华,戚文军,等.金属选区激光熔化的研究现状[J].材料导报,2017,31(5):90-91.
【2】李勇,巴发海,许鹤君.3D打印技术的发展和挑战[J].理化检验(物理分册),2018,54(11):799-804.
【3】尹燕,刘鹏宇,路超,等.选区激光熔化成型316L不锈钢微观组织及拉伸性能分析[J].焊接学报,2018,39(8):77-81.
【4】余晨帆,赵聪聪,张哲峰,等.选区激光熔化316L不锈钢的拉伸性能[J].金属学报,2020,56(5):683-692.
【5】彭小敏,徐若,李敖,等.工艺参数对316L不锈钢选区激光熔化成型组织性能的影响[J].湖南工程学院学报(自然科学版),2019(4):26-32.
【6】CASATI R,LEMKE J,VEDANI M.Microstructure and fracture behavior of 316L austenitic stainless steel produced by selective laser melting[J].Journal of Materials Science & Technology,2016,32(8):738-744.
【2】李勇,巴发海,许鹤君.3D打印技术的发展和挑战[J].理化检验(物理分册),2018,54(11):799-804.
【3】尹燕,刘鹏宇,路超,等.选区激光熔化成型316L不锈钢微观组织及拉伸性能分析[J].焊接学报,2018,39(8):77-81.
【4】余晨帆,赵聪聪,张哲峰,等.选区激光熔化316L不锈钢的拉伸性能[J].金属学报,2020,56(5):683-692.
【5】彭小敏,徐若,李敖,等.工艺参数对316L不锈钢选区激光熔化成型组织性能的影响[J].湖南工程学院学报(自然科学版),2019(4):26-32.
【6】CASATI R,LEMKE J,VEDANI M.Microstructure and fracture behavior of 316L austenitic stainless steel produced by selective laser melting[J].Journal of Materials Science & Technology,2016,32(8):738-744.
相关信息