预应力钢丝用YL82B热轧盘条断裂原因
Fracture reason of YL82B hot rolled wire rod for prestressed steel wire
摘 要
某批次YL82B预应力钢丝用热轧盘条发生拉拔断裂,对其不同断口进行宏观观察和微观分析。结果表明,盘条断裂的主要原因是产品存在表面缺陷和异常组织。最后提出了改善盘条质量的建议。
钢丝
断裂
显微组织
wire rod
steel wire
fracture
microstructure
Abstract
A batch of hot rolled wire rod for YL82 B prestressed steel wire fractured during drawing. Macroscopic observation and micro analysis were carried out on different fracture surfaces. The results show that the main reason for wire rod fracture was the surface defects and abnormal microstructure of the product. Finally, suggestions for improving the quality of wire rod were put forward.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202206015
所属栏目 质量控制与失效分析
基金项目
收稿日期 2021/12/12
修改稿日期
网络出版日期
作者单位点击查看
备注路丰(1985-),男,工程师,主要从事检验管理和产品研发工作
引用该论文: LU Feng,ZHAO Xiqing,ZU Yizhong. Fracture reason of YL82B hot rolled wire rod for prestressed steel wire[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(6): 58～62
路丰,赵喜庆,祖义忠. 预应力钢丝用YL82B热轧盘条断裂原因[J]. 理化检验－物理分册, 2022, 58(6): 58～62
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张振全,张明博.预应力钢绞线SWRH82B锥形断裂机理及优化研究[J].炼钢,2021,37(3):74-80.
【2】牛亚然.预应力钢丝用热轧盘条实验研究[D].南京:南京理工大学,2004.
【3】刘莹,田庆荣,陈国庆,等.浅析SWRH82B盘条拉拔断口典型形貌及特征[J].天津冶金,2011(4):61-63.
【4】田鹏,王全利,贾元海,等.影响钢绞线拉拔性能因素的探讨[J].河北冶金,2014,224(8):24-28.
【2】牛亚然.预应力钢丝用热轧盘条实验研究[D].南京:南京理工大学,2004.
【3】刘莹,田庆荣,陈国庆,等.浅析SWRH82B盘条拉拔断口典型形貌及特征[J].天津冶金,2011(4):61-63.
【4】田鹏,王全利,贾元海,等.影响钢绞线拉拔性能因素的探讨[J].河北冶金,2014,224(8):24-28.
相关信息