某核电厂核级设备法兰泄漏监测管开裂原因
Cracking Causes of Leak Monitoring Tube of Nuclear-Grade Equipment Flange in a Nuclear Power Plant
摘 要
在国内某核电厂运行1 a后的大修期间,发现核级设备法兰泄漏监测管发生开裂。采用化学成分分析、金相检验、拉伸性能测试、扫描电镜及能谱分析等方法,分析了泄漏监测管开裂的原因。结果表明:该泄漏监测管的开裂形式为应力腐蚀开裂;泄漏监测管在安装阶段冲洗不彻底,导致氯离子残留在管内,在氯离子聚集处首先形成腐蚀坑,在应力及腐蚀性介质的共同作用下,该处产生裂纹,裂纹不断扩展,最终导致泄漏监测管发生开裂。
泄漏监测管
氯离子
腐蚀坑
应力腐蚀开裂
flange
leak monitoring tube
chloride ion
corrosion pit
stress corrosion cracking
Abstract
During the overhaul period of a domestic nuclear power plant after 1 a operation, it was found that the flange leak monitoring tube of nuclear-grade equipment was cracked. The reasons for the cracking of leak monitoring tube were analyzed by chemical composition analysis, metallographic examination, tensile property test, scanning electron microscopy and energy spectrum analysis. The results showed that the cracking form of leak monitoring tube was stress corrosion cracking. During the installation stage, the flushing of leak monitoring tube was not complete, and caused chloride ions remaineing in the tube. Some corrosion pits first formed on the site of chloride ions aggregation. Under the combined action of stress and corrosive medium, cracks occurred there, and the crack continued to expand, eventually leading to leak monitoring tube cracked.
中图分类号 TG174 DOI 10.11973/fsyfh-202206018
所属栏目 失效分析
基金项目
收稿日期 2021/9/29
修改稿日期
网络出版日期
作者单位点击查看
联系人作者马若群(maruoqun@qq.com)
引用该论文: YANG Xingwang,MA Ruoqun,XU Xinzhu. Cracking Causes of Leak Monitoring Tube of Nuclear-Grade Equipment Flange in a Nuclear Power Plant[J]. Corrosion & Protection, 2022, 43(6): 97
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】LU Z,SHOJI T,MENG F,et al. Characterization of microstructure and local deformation in 316NG weld heat-affected zone and stress corrosion cracking in high temperature water[J]. Corrosion Science,2011,53(5):1916-1932.
【2】ANGELIU T M,ADRESEN P L,HALL E,et al. Intergranular stress corrosion cracking of unsensitized stainless steels in BWR environment[C]//Proceedings of 9th International Conference on Environmental Degradation of Materials Nuclear Power Systems-Water Reactors. Newport Beach:TMS,1999.
【3】杨宏亮,薛河,倪陈强.冷加工对316L不锈钢裂尖力学特性的影响[J].西安科技大学学报,2018,38(3):484-489.
【4】ZHOU Z X,JIN S S,LIU C L,et al. Stress Corrosion Cracking and Prevention of Austenitic Stainless Steel Pressure Pipe[J]. Physical Testing and Chemical Analysis (Part A:Physical Testing),2015,51(10):721.
【5】AHMED I I,GRANT B,SHERRY A H,et al. Deformation path effects on the internal stress development in cold worked austenitic steel deformed in tension[J]. Materials Science and Engineering A,2014,614(1/2):326-337.
【6】HOU J,SHOJI T,LU Z P,et al. Residual strain measurement and grain boundary characterization in the heat affected zone of a weld joint between alloy 690TT and alloy 52[J]. Journal of Nuclear Materials,2010,397(1/3):109-115.
【2】ANGELIU T M,ADRESEN P L,HALL E,et al. Intergranular stress corrosion cracking of unsensitized stainless steels in BWR environment[C]//Proceedings of 9th International Conference on Environmental Degradation of Materials Nuclear Power Systems-Water Reactors. Newport Beach:TMS,1999.
【3】杨宏亮,薛河,倪陈强.冷加工对316L不锈钢裂尖力学特性的影响[J].西安科技大学学报,2018,38(3):484-489.
【4】ZHOU Z X,JIN S S,LIU C L,et al. Stress Corrosion Cracking and Prevention of Austenitic Stainless Steel Pressure Pipe[J]. Physical Testing and Chemical Analysis (Part A:Physical Testing),2015,51(10):721.
【5】AHMED I I,GRANT B,SHERRY A H,et al. Deformation path effects on the internal stress development in cold worked austenitic steel deformed in tension[J]. Materials Science and Engineering A,2014,614(1/2):326-337.
【6】HOU J,SHOJI T,LU Z P,et al. Residual strain measurement and grain boundary characterization in the heat affected zone of a weld joint between alloy 690TT and alloy 52[J]. Journal of Nuclear Materials,2010,397(1/3):109-115.
相关信息