某吊链双环卸扣断裂原因
Reasons for breaking of double ring shackle of a crane chain
摘 要
某吊链双环卸扣在工作时发生断裂。采用断口形貌分析、化学成分分析、金相检验和硬度测试等方法对卸扣断裂的原因进行了分析，并采用有限元分析方法对不同直径的卸扣进行应力校核。结果表明：过度磨损导致卸扣直径变小是其断裂的根本原因。规范的定期检查，及时更换过度磨损的零件可以避免卸扣断裂。
疲劳
磨损
有限元分析
shackle
fatigue
wear
finite element analysis
Abstract
A double ring shackle of a crane chain broken during operation. Fracture morphology analysis, chemical composition analysis, metallographic examination and hardness test were used to analyze the fracture causes of the shackle, and the finite element analysis method was used to check the stress of the shackles with different diameters. The results show that the root cause of fracture was that the diameter of the shackle decreased due to excessive wear. Standard periodic inspection, timely replacement of excessive wear parts could avoid shackle fracture.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202209016
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/1/6
修改稿日期
网络出版日期
作者单位点击查看
备注李陈昊(1983-),男,工程师,主要从事金属零部件的失效分析工作,li.chenhao@hotmail.com
引用该论文: LI Chenhao. Reasons for breaking of double ring shackle of a crane chain[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(9): 59～61
李陈昊. 某吊链双环卸扣断裂原因[J]. 理化检验－物理分册, 2022, 58(9): 59～61
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】初铭祥. 国外吊索具及相关零件[J].起重运输机械,1992(7):23-26.
【2】钟群鹏,田永江.失效分析基础知识[M].北京:机械工业出版社,1990.
【3】王仁智,吴培远.疲劳失效分析[M].北京:机械工业出版社,1987.
【4】钟群鹏,赵子华.断口学[M].北京:高等教育出版社,2006.
【5】范立坤.有限元技术在失效分析中的应用研究[D].上海:上海交通大学,2012.
【6】怀玉兰,孟宪举,李军,等.圆截面卸扣的有限元设计与结构[J].河北联合大学学报(自然科学版),2012,34(2):40-43.
【2】钟群鹏,田永江.失效分析基础知识[M].北京:机械工业出版社,1990.
【3】王仁智,吴培远.疲劳失效分析[M].北京:机械工业出版社,1987.
【4】钟群鹏,赵子华.断口学[M].北京:高等教育出版社,2006.
【5】范立坤.有限元技术在失效分析中的应用研究[D].上海:上海交通大学,2012.
【6】怀玉兰,孟宪举,李军,等.圆截面卸扣的有限元设计与结构[J].河北联合大学学报(自然科学版),2012,34(2):40-43.
相关信息