Corrosion Behavior of L245 Pipeline Steel at Different Gap Depths under Stripping Coating
摘 要
通过电化学测试和宏观形貌分析,研究了剥离涂层下机坪管道用L245管线钢在不同缝隙深度处的腐蚀行为。结果表明:剥离涂层下不同位置L245钢电极自腐蚀电位的大小与缝隙深度有关;距破损点90 mm处钢电极腐蚀速率有先下降后回升而后再下降的显著变化,并且出现了warburg阻抗扩散弧和明显的弥散效应,是该腐蚀体系下缝隙腐蚀最明显的一个点;距破损点90 mm处钢电极表面腐蚀产物层有明显裂纹,150 mm处钢电极表面点蚀情况突出;涂层剥离会造成L245管线钢缝隙腐蚀,在机坪管道防护中应引起重视。
Abstract
The corrosion behaviors of L245 pipeline steel under stripping coating at different gap depths were studied by electrochemical test and macro morphology analysis. The results showed that the self corrosion potential of L245 steel electrode at different positions under the stripping coating was related to the gap depth. The corrosion rate of steel electrode at 90 mm from the damage point decreased first, then increased and then decreased, and Warburg impedance diffusion arc and obvious dispersion effect appeared, which was the most obvious point of crevice corrosion under this corrosion system; There were obvious cracks in the corrosion product layer on the surface of the steel electrode 90 mm away from the damage point, and the pitting corrosion on the surface of the steel electrode 150 mm was prominent. Coating peeling may cause crevice corrosion of L245 pipeline steel, which should be paid attention to apron pipeline protection.
中图分类号 TG174 DOI 10.11973/fsyfh-202210010
所属栏目 试验研究
基金项目 国家重点研发计划(2018YFC0809500);中国民用航空飞行学院科研基金(J2021-108,J2021-109)
收稿日期 2022/4/26
修改稿日期
网络出版日期
作者单位点击查看
联系人作者岳航(529419058@qq.com)
引用该论文: DENG Zhibin,YUE Hang,HU Xiao,TANG Haiping,LIU Xiang,ZHANG Lei. Corrosion Behavior of L245 Pipeline Steel at Different Gap Depths under Stripping Coating[J]. Corrosion & Protection, 2022, 43(10): 63
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李义田.浅谈金属的腐蚀与防护[J].价值工程, 2013, 32(25):301-302.
【2】任超, 韩鹏举, 张文博.直流电作用下X70钢在砂土中腐蚀的电化学行为[J].腐蚀与防护, 2015, 36(12):1137-1142, 1179.
【3】THACKER B H, LIGHT G M, DANTE J F, et al. Corrosion control in oil and gas pipelines[J]. Pipeline & Gas Journal, 2010, 237(3):62-66.
【4】管道泄漏发生燃爆附近人员无辜躺枪——中石油中缅天然气管道黔西南州晴隆段"6·10"泄漏燃爆较大事故分析[J].吉林劳动保护, 2021(9):47-48.
【5】王晓霖, 闫茂成, 舒韵, 等.破损涂层下管线钢的交流电干扰腐蚀行为[J].中国腐蚀与防护学报, 2017, 37(4):341-346.
【6】徐成.交直流杂散电流与应力耦合作用下X70管线钢腐蚀及涂层剥离行为研究[D].北京:北京工业大学, 2018.
【7】李彬.阴极保护下埋地管道涂层及腐蚀与防护态势评价方法研究[D].成都:西南石油学院, 2004.
【8】WANG Y C, XU L Y, SUN J L, et al.Mechano-electrochemical interaction for pipeline corrosion:a review[J].Journal of Pipeline Science and Engineering, 2021, 1(1):1-16.
【9】李明, 王晓霖, 乔国春, 等.埋地油气管道杂散电流检测与防护[C]//第四届中国管道完整性管理技术大会.[出版地不详]:[出版者不详], 2018.
【10】尚兴彬, 高东, 胡世杰, 等.埋地X70钢管在不同缝隙距离下的腐蚀行为[J].材料保护, 2014, 47(8):78-80, 9.
【11】何莎, 邓勇刚, 李经伟, 等.在有微生物的水中L245钢腐蚀速率模型研究[J].石油化工腐蚀与防护, 2021, 38(6):1-6.
【12】王丹, 肖辉宗, 谢飞, 等.温度、HCO-3和pH值对X70钢在成都土壤模拟溶液中腐蚀行为的影响[J].材料保护, 2017, 50(1):77-81.
【13】姜子涛, 杜艳霞, 董亮, 等.交流电对Q235钢腐蚀电位的影响规律研究[J].金属学报, 2011, 47(8):997-1002.
【14】XU L Y, SU X, YIN Z X, et al.Development of a real-time AC/DC data acquisition technique for studies of AC corrosion of pipelines[J].Corrosion Science, 2012, 61:215-223.
【15】张新, 郭昊, 杜翠薇, 等.库尔勒模拟溶液中HCO-3对X70钢缝隙腐蚀的影响[J].腐蚀与防护, 2008, 29(3):109-112.
【16】丁清苗, 秦永祥, 崔艳雨, 等.交流杂散电流对剥离涂层下X80钢腐蚀行为研究[J].钢铁研究学报, 2021, 33(6):503-514.
【17】方帅, 闫凤霞, 张骁勇.剥离涂层下X90管线钢在近中性pH值模拟溶液中的电化学腐蚀行为[J].焊管, 2019, 42(3):12-15, 22.
【18】王晓霖, 闫茂成, 舒韵, 等.破损涂层下管线钢的交流电干扰腐蚀行为[J].中国腐蚀与防护学报, 2017, 37(4):341-346.
【19】LI Y C, XU C, ZHANG R H, et al. Effects of stray AC interference on corrosion behavior of X70 pipeline steel in a simulated marine soil solution[J].International Journal of Electrochemical Science, 2017:1829-1845.
【20】赵博, 杜翠薇, 刘智勇, 等.剥离涂层下的X80钢在鹰潭土壤模拟溶液中的腐蚀行为[J].金属学报, 2012, 48(12):1530-1536.
【21】孙齐磊, 王志刚, 蔡元兴.材料腐蚀与防护[M].北京:化学工业出版社, 2015.
【2】任超, 韩鹏举, 张文博.直流电作用下X70钢在砂土中腐蚀的电化学行为[J].腐蚀与防护, 2015, 36(12):1137-1142, 1179.
【3】THACKER B H, LIGHT G M, DANTE J F, et al. Corrosion control in oil and gas pipelines[J]. Pipeline & Gas Journal, 2010, 237(3):62-66.
【4】管道泄漏发生燃爆附近人员无辜躺枪——中石油中缅天然气管道黔西南州晴隆段"6·10"泄漏燃爆较大事故分析[J].吉林劳动保护, 2021(9):47-48.
【5】王晓霖, 闫茂成, 舒韵, 等.破损涂层下管线钢的交流电干扰腐蚀行为[J].中国腐蚀与防护学报, 2017, 37(4):341-346.
【6】徐成.交直流杂散电流与应力耦合作用下X70管线钢腐蚀及涂层剥离行为研究[D].北京:北京工业大学, 2018.
【7】李彬.阴极保护下埋地管道涂层及腐蚀与防护态势评价方法研究[D].成都:西南石油学院, 2004.
【8】WANG Y C, XU L Y, SUN J L, et al.Mechano-electrochemical interaction for pipeline corrosion:a review[J].Journal of Pipeline Science and Engineering, 2021, 1(1):1-16.
【9】李明, 王晓霖, 乔国春, 等.埋地油气管道杂散电流检测与防护[C]//第四届中国管道完整性管理技术大会.[出版地不详]:[出版者不详], 2018.
【10】尚兴彬, 高东, 胡世杰, 等.埋地X70钢管在不同缝隙距离下的腐蚀行为[J].材料保护, 2014, 47(8):78-80, 9.
【11】何莎, 邓勇刚, 李经伟, 等.在有微生物的水中L245钢腐蚀速率模型研究[J].石油化工腐蚀与防护, 2021, 38(6):1-6.
【12】王丹, 肖辉宗, 谢飞, 等.温度、HCO-3和pH值对X70钢在成都土壤模拟溶液中腐蚀行为的影响[J].材料保护, 2017, 50(1):77-81.
【13】姜子涛, 杜艳霞, 董亮, 等.交流电对Q235钢腐蚀电位的影响规律研究[J].金属学报, 2011, 47(8):997-1002.
【14】XU L Y, SU X, YIN Z X, et al.Development of a real-time AC/DC data acquisition technique for studies of AC corrosion of pipelines[J].Corrosion Science, 2012, 61:215-223.
【15】张新, 郭昊, 杜翠薇, 等.库尔勒模拟溶液中HCO-3对X70钢缝隙腐蚀的影响[J].腐蚀与防护, 2008, 29(3):109-112.
【16】丁清苗, 秦永祥, 崔艳雨, 等.交流杂散电流对剥离涂层下X80钢腐蚀行为研究[J].钢铁研究学报, 2021, 33(6):503-514.
【17】方帅, 闫凤霞, 张骁勇.剥离涂层下X90管线钢在近中性pH值模拟溶液中的电化学腐蚀行为[J].焊管, 2019, 42(3):12-15, 22.
【18】王晓霖, 闫茂成, 舒韵, 等.破损涂层下管线钢的交流电干扰腐蚀行为[J].中国腐蚀与防护学报, 2017, 37(4):341-346.
【19】LI Y C, XU C, ZHANG R H, et al. Effects of stray AC interference on corrosion behavior of X70 pipeline steel in a simulated marine soil solution[J].International Journal of Electrochemical Science, 2017:1829-1845.
【20】赵博, 杜翠薇, 刘智勇, 等.剥离涂层下的X80钢在鹰潭土壤模拟溶液中的腐蚀行为[J].金属学报, 2012, 48(12):1530-1536.
【21】孙齐磊, 王志刚, 蔡元兴.材料腐蚀与防护[M].北京:化学工业出版社, 2015.
相关信息