Causes of cracks on a 00Cr17Ni14Mo2 steel flange
摘 要
某00Cr17Ni14Mo2钢法兰在拆除后,准备进行焊接并二次利用时发现裂纹。采用宏观观察、化学成分分析、金相检验、断口分析及力学性能测试等方法,对该法兰产生裂纹的原因进行分析。结果表明:该法兰的开裂性质为应力腐蚀开裂,裂纹主要发生在受拉应力最大的部位;该法兰的碳元素含量过高,使材料的耐腐蚀性能降低,最终导致法兰产生裂纹。
Abstract
Cracks were found on a 00Cr17Ni14Mo2 steel flange when it was ready to be welded and reused after removal. The causes of cracks on the flange were analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, fracture analysis and mechanical property test. The results show that the cracking nature of the flange was stress corrosion cracking, and the cracks mainly occurred at the position with the maximum tensile stress. The carbon content of the flange was too high, which reduced the corrosion resistance of the material, and finally led flange to cracks.
中图分类号 TB31 TG115.2 DOI 10.11973/lhjy-wl202211019
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/2/24
修改稿日期
网络出版日期
作者单位点击查看
备注周宝瑜(1978-),女,工程师,主要从事汽车零部件失效分析工作,29926341@qq.com
引用该论文: ZHOU Baoyu. Causes of cracks on a 00Cr17Ni14Mo2 steel flange[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(11): 69~71
周宝瑜. 00Cr17Ni14Mo2钢法兰裂纹的产生原因[J]. 理化检验-物理分册, 2022, 58(11): 69~71
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡世炎.机械失效分析手册[M].成都:四川科学技术出版社,1989. {
【2】陈渝.天然气钻杆悬挂器断裂分析[J].理化检验(物理分册),2012,48(7):483-490. {
【2】陈渝.天然气钻杆悬挂器断裂分析[J].理化检验(物理分册),2012,48(7):483-490. {
相关信息