某重载高速齿轮箱太阳轮开裂原因
Cracking causes of the sun gear of a heavy-duty high speed gearbox
摘 要
某重载高速齿轮箱太阳轮在装配时发生开裂。采用宏观观察、化学成分分析、金相检验、扫描电镜及能谱分析等方法,分析了该太阳轮开裂的原因。结果表明:该太阳轮在加工完成后和装配前,内部夹杂物使裂纹萌生,加工残余应力作用导致太阳轮发生了低应力脆性开裂。
沿晶断裂
准解理断裂
低应力脆性开裂
夹杂
sun gear
intergranular fracture
quasi-cleavage fracture
low stress brittle cracking
inclusion
Abstract
The sun gear of a heavy-duty high speed gearbox cracked during assembly. The reasons for the cracking of the sun gear were analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, scanning electron microscopy and energy spectrum analysis. The results show that the internal inclusions caused the sun gear initiate cracks after maching and before assembly, and the machining residual stress caused the sun gear to low stress brittle cracking.
中图分类号 TB31 TG115.2 DOI 10.11973/lhjy-wl202211021
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/3/1
修改稿日期
网络出版日期
作者单位点击查看
备注刘聪颖(1987-),女,学士,工程师,主要从事热处理技术研究工作
引用该论文: LIU Congying,CHAO Yongqiang,DANG Junling,HUANG Wenpeng,ZHONG Boying,MA Hongli,LONG Qian,WANG Tao. Cracking causes of the sun gear of a heavy-duty high speed gearbox[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(11): 76～78
刘聪颖,晁永强,党军玲,黄文鹏,仲博颖,马宏利,龙倩,王涛. 某重载高速齿轮箱太阳轮开裂原因[J]. 理化检验－物理分册, 2022, 58(11): 76～78
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】袁萍,陈怡,王敬德.某液压系统大型弹簧断裂原因[J].理化检验(物理分册),2021,57(9):64-67.
【2】薛喜才.汽油发动机缸套频繁开裂的原因[J].理化检验(物理分册),2021,57(5):62-65.
【3】包卫平,任学平,马祖南.多晶体材料的晶界强化模型研究[J].塑性工程学报,2008,15(3):97-100.
【2】薛喜才.汽油发动机缸套频繁开裂的原因[J].理化检验(物理分册),2021,57(5):62-65.
【3】包卫平,任学平,马祖南.多晶体材料的晶界强化模型研究[J].塑性工程学报,2008,15(3):97-100.
相关信息