船用柴油机螺柱断裂原因
Causes of stud fracture of marine diesel engine
摘 要
某船用柴油机螺柱发生断裂,利用宏观观察、化学成分分析、金相检验、力学性能测试、断口分析等方法对其断裂原因进行分析。结果表明:由于杆身部位接触了腐蚀介质,产生了点腐蚀,因此在拉应力的作用下,由点腐蚀坑引发了应力腐蚀开裂,最终导致螺柱发生断裂。
点腐蚀
应力腐蚀
断裂
stud
point corrosion
stress corrosion
fracture
Abstract
The fracture of a marine diesel engine stud was analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, mechanical property test and fracture analysis. The results show that due to the contact of the rod body with the corrosive medium, pitting corrosion occured. Therefore, under the action of tensile stress, stress corrosion cracking was caused by pitting corrosion pits, which eventually led to the fracture of the stud.
中图分类号 TG115.2 TB304 DOI 10.11973/lhjy-wl202212013
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/9/6
修改稿日期
网络出版日期
作者单位点击查看
备注陆慧(1976-),女,本科,高级工程师,主要从事物理检测及失效分析工作,luhui0623@163.com
引用该论文: LU Hui. Causes of stud fracture of marine diesel engine[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(12): 55～57
陆慧. 船用柴油机螺柱断裂原因[J]. 理化检验－物理分册, 2022, 58(12): 55～57
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王荣. 机械装备的失效分析(续前)第8讲失效诊断与预防技术(4)[J].理化检验(物理分册),2018,54(6):402-410,462.
相关信息