高温过热器TP347H钢管焊接接头开裂原因
Reasons for cracking of welded joint of TP347H steel pipe in high temperature superheater
摘 要
某高温过热器TP347H钢管焊接接头多次发生开裂,采用宏观观察、化学成分分析、金相检验、扫描电子显微镜及能谱分析、力学性能测试和双环电化学动电位再活化法试验对其开裂原因进行分析。结果表明:TP347H钢管焊接接头开裂性质为晶间型应力腐蚀开裂,焊接时循环热导致的管材热影响区敏化以及焊接接头的残余应力是其开裂的主要原因。
焊接接头
奥氏体不锈钢
晶间型应力腐蚀开裂
敏化
残余应力
TP347H steel
welding joint
austenitic stainless steel
intergranular stress corrosion cracking
sensitization
residual stress
Abstract
The welding joint of TP347H steel pipe of a high temperature superheater cracked several times. The cracking reasons were analyzed by macroscopic observation, chemical composition analysis, metallographic examination, scanning electron microscope and energy spectrum analysis, mechanical properties test and double-loop electrochemical potentiokinetic reactivation method test. The results show that the cracking property of TP347H steel pipe welded joint was intergranular stress corrosion cracking. The main causes of cracking were the sensitization of pipe heat affected zone caused by circulating heat during welding and the residual stress of welded joint.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl202212017
所属栏目 质量控制与失效分析
基金项目 2020年内蒙古电力科学研究院科技项目(2020-ZC-04)
收稿日期 2022/2/22
修改稿日期
网络出版日期
作者单位点击查看
备注谭晓蒙(1993-),男,硕士,工程师,主要从事电力设备无损检测与失效分析工作,tanxmfocus@foxmail.com
引用该论文: TAN Xiaomeng,CHEN Hao,QIAO Xin,GUO Xin. Reasons for cracking of welded joint of TP347H steel pipe in high temperature superheater[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2022, 58(12): 73～76
谭晓蒙,陈浩,乔欣,郭心爱. 高温过热器TP347H钢管焊接接头开裂原因[J]. 理化检验－物理分册, 2022, 58(12): 73～76
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李新梅, 张忠文,杜宝帅,等.600℃时效后HR3C钢的显微组织和冲击韧性[J].机械工程材料,2014,38(7):95-98.
【2】肖纪美.不锈钢的金属学问题[M].北京:冶金工业出版社,2006.
【3】马红,史志刚,贺锡鹏,等.18-8型奥氏体不锈钢锅炉管服役特性研究(二)[J].热力发电,2012,41(2):42-46.
【4】谭晓蒙,邢敬舒,田峰,等.电站锅炉奥氏体不锈钢管晶间腐蚀开裂分析[J].山东电力技术,2020,47(5):77-80.
【5】李新梅,张忠文,杜宝帅,等.时效对HR3C钢晶间腐蚀敏感性的影响[J].腐蚀科学与防护技术,2014,26(6):541-544.
【6】张述林,李敏娇,王晓波,等.18-8奥氏体不锈钢的晶间腐蚀[J].中国腐蚀与防护学报,2007,27(2):124-128.
【7】朱江.激光共聚焦扫描显微镜原位观察奥氏体不锈钢的敏化过程[J].理化检验(物理分册),2016,52(2):83-87,91.
【8】谢春玉,黄子东,陈丽玲,等.使用电化学动电位再活化法研究热处理工艺对304不锈钢晶间腐蚀敏感性的影响[J].理化检验(物理分册),2017,53(5):303-308,332.
【2】肖纪美.不锈钢的金属学问题[M].北京:冶金工业出版社,2006.
【3】马红,史志刚,贺锡鹏,等.18-8型奥氏体不锈钢锅炉管服役特性研究(二)[J].热力发电,2012,41(2):42-46.
【4】谭晓蒙,邢敬舒,田峰,等.电站锅炉奥氏体不锈钢管晶间腐蚀开裂分析[J].山东电力技术,2020,47(5):77-80.
【5】李新梅,张忠文,杜宝帅,等.时效对HR3C钢晶间腐蚀敏感性的影响[J].腐蚀科学与防护技术,2014,26(6):541-544.
【6】张述林,李敏娇,王晓波,等.18-8奥氏体不锈钢的晶间腐蚀[J].中国腐蚀与防护学报,2007,27(2):124-128.
【7】朱江.激光共聚焦扫描显微镜原位观察奥氏体不锈钢的敏化过程[J].理化检验(物理分册),2016,52(2):83-87,91.
【8】谢春玉,黄子东,陈丽玲,等.使用电化学动电位再活化法研究热处理工艺对304不锈钢晶间腐蚀敏感性的影响[J].理化检验(物理分册),2017,53(5):303-308,332.
相关信息