Remaining life estimation of main steam pipeline in power plant after long-term high temperature service
摘 要
采用金相检验、力学性能测试及高温蠕变持久试验等方法,对某电站主蒸汽管道12Cr1MoV钢管的显微组织和力学性能进行了研究。结果表明:长期高温服役后,12Cr1MoV钢管道组织中出现5级珠光体球化,晶内碳化物析出明显,蒸汽管道内壁、中间、外壁组织的球化程度、晶粒度等级均一致,管道的力学性能下降明显;估算管道的剩余寿命约为4.45a。
Abstract
The microstructure and mechanical properties of 12Cr1MoV steel pipe for the main steam pipeline of a power plant were studied by means of metallographic examination, mechanical property test and high temperature creep rupture test. The results show that after long-term high temperature service, the microstructure of 12Cr1MoV steel pipeline appearred 5 grade pearlite spheroidization, the precipitation of carbide in the crystal was obvious, the spheroidization degree and grain size grade of the inner wall, middle wall and outer wall of the steam pipeline were consistent, and the mechanical properties of the pipeline declined significantly. The remaining life of the pipeline was estimated to be about 4. 45 years.
中图分类号 TB31 DOI 10.11973/lhjy-wl202301004
所属栏目 试验与研究
基金项目 2020年浙江省市场监督管理局科研计划项目(20200308)
收稿日期 2022/3/28
修改稿日期
网络出版日期
作者单位点击查看
备注陈兴阳(1990-),男,博士,高级工程师,主要从事特种设备检验检测与安全评估工作,chencxy@zjtj.org
引用该论文: CHEN Xingyang,ZHOU Yang,SONG Junjun,WANG Fenghuai,XIE Haoping,MA Linlin. Remaining life estimation of main steam pipeline in power plant after long-term high temperature service[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(1): 13~15
陈兴阳,周阳,宋俊俊,王锋淮,谢浩平,马琳琳. 长期高温服役电站主蒸汽管道的剩余寿命评估[J]. 理化检验-物理分册, 2023, 59(1): 13~15
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王宪军,李书瑞,胡因洪.锅炉及压力容器用12Cr1MoVR钢板的焊接接头性能研究[J].压力容器,2016,33(10):9-15.
【2】黎小秋,赵康文,唐囡,等.300 MW电站锅炉后屏过热器爆管原因分析和对策[J].压力容器,2012,29(4):68-71.
【3】姜勇,巩建鸣,叶有俊,等.12Cr1MoV过热器管劣化行为研究[J].压力容器,2011,28(2):11-15.
【4】姜勇,巩建鸣,叶有俊,等.基于碳化物相分析法的12Cr1MoV过热器管寿命无损评价[J].材料热处理学报,2011,32(8):15-18.
【5】谷树超,王松,李俊,等.12Cr1MoV钢过热器爆管的显微组织和力学性能[J].理化检验(物理分册),2018,54(3):169-174.
【6】王友华,魏安安,纪熙,等.制氢转化炉炉管剩余寿命评估[J].腐蚀与防护,2012,33(4):335-337.
【7】耿鲁阳,刘建杰,巩建鸣,等.基于修正θ投影法的炉管用Cr25Ni35Nb钢蠕变寿命预测[J].机械工程材料,2011,35(12):93-96.
【8】刘建杰,巩建鸣,姜勇,等.采用修正θ投影法预测Cr25Ni35Nb炉管钢的蠕变性能[J].机械工程材料,2011,35(1):89-92.
【9】宋文强,李尚林.热处理工艺对12Cr1MoV钢显微组织和力学性能的影响[J]. 理化检验(物理分册),2017,53(2):97-100.
【10】陈品同,张博智.焊后热处理对12Cr1MoV钢管焊接接头组织与性能的影响[J].理化检验(物理分册),2014,50(3):180-183.
【11】杨宜科,董富,朱云秀,等.在蠕变-疲劳复合作用下12Cr1MoV钢强度特性的研究[J].理化检验(物理分册),1989,25(3):13-16.
【12】严伟,张国福,丘思晓,等.珠光体球化对20G拉伸力学性能的影响[J].压力容器,2003,20(8):10-13.
【2】黎小秋,赵康文,唐囡,等.300 MW电站锅炉后屏过热器爆管原因分析和对策[J].压力容器,2012,29(4):68-71.
【3】姜勇,巩建鸣,叶有俊,等.12Cr1MoV过热器管劣化行为研究[J].压力容器,2011,28(2):11-15.
【4】姜勇,巩建鸣,叶有俊,等.基于碳化物相分析法的12Cr1MoV过热器管寿命无损评价[J].材料热处理学报,2011,32(8):15-18.
【5】谷树超,王松,李俊,等.12Cr1MoV钢过热器爆管的显微组织和力学性能[J].理化检验(物理分册),2018,54(3):169-174.
【6】王友华,魏安安,纪熙,等.制氢转化炉炉管剩余寿命评估[J].腐蚀与防护,2012,33(4):335-337.
【7】耿鲁阳,刘建杰,巩建鸣,等.基于修正θ投影法的炉管用Cr25Ni35Nb钢蠕变寿命预测[J].机械工程材料,2011,35(12):93-96.
【8】刘建杰,巩建鸣,姜勇,等.采用修正θ投影法预测Cr25Ni35Nb炉管钢的蠕变性能[J].机械工程材料,2011,35(1):89-92.
【9】宋文强,李尚林.热处理工艺对12Cr1MoV钢显微组织和力学性能的影响[J]. 理化检验(物理分册),2017,53(2):97-100.
【10】陈品同,张博智.焊后热处理对12Cr1MoV钢管焊接接头组织与性能的影响[J].理化检验(物理分册),2014,50(3):180-183.
【11】杨宜科,董富,朱云秀,等.在蠕变-疲劳复合作用下12Cr1MoV钢强度特性的研究[J].理化检验(物理分册),1989,25(3):13-16.
【12】严伟,张国福,丘思晓,等.珠光体球化对20G拉伸力学性能的影响[J].压力容器,2003,20(8):10-13.
相关信息