Causes of aluminum alloy foil broken
摘 要
某铝合金箔在生产过程中发生断带,采用宏观观察、化学成分分析、金相检验、扫描电镜和能谱分析等方法对其断带原因进行分析。结果表明:在铝合金箔的厚度较小时,夹杂物影响了轧制过程中的金属流动,形成了孔洞和裂纹,裂纹扩展导致铝合金箔发生断带。
Abstract
The fracture of an aluminum alloy foil occurred during the production process. The fracture reasons were analyzed by means of macroscopic observation, chemical composition analysis, metallographic examination, scanning electron microscopy and energy spectrum analysis. The results show that when the thickness of the aluminum alloy foil was small, the inclusions affected the metal flow during the rolling process, forming holes and cracks. The crack propagation caused the aluminum alloy foil to break.
中图分类号 TB31 TG115.2 DOI 10.11973/lhjy-wl202302008
所属栏目 质量控制与失效分析
基金项目 江苏省成果转化专项资金项目(BA2020040)
收稿日期 2022/11/4
修改稿日期
网络出版日期
作者单位点击查看
备注窦维买(1983-),男,工程师,主要从事理化检验工作,douweimai@163.com
引用该论文: DOU Weimai. Causes of aluminum alloy foil broken[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(2): 28~30
窦维买. 铝合金箔断带原因[J]. 理化检验-物理分册, 2023, 59(2): 28~30
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】路丽英,王祝堂. 中国铝加工业概况[J]. 轻合金加工技术,2019,47(1):1-7.
【2】姜宁,王日侠. 高功效、低油斑轧制油添加剂与润滑油的研制[J]. 有色金属加工,2014,43(1):25-27,57.
【3】黄灏,曾兰英. 铝冷轧制油的研制[J]. 润滑油,2003,18(5):27-31.
【2】姜宁,王日侠. 高功效、低油斑轧制油添加剂与润滑油的研制[J]. 有色金属加工,2014,43(1):25-27,57.
【3】黄灏,曾兰英. 铝冷轧制油的研制[J]. 润滑油,2003,18(5):27-31.
相关信息